RESUMEN
OBJECTIVE: To evaluate experimental dimethacrylate-based materials containing calcium orthophosphates or calcium silicate particles in terms of their optical, mechanical and Ca2+ release behaviour. METHODS: Dicalcium phosphate dihydrate (DCPD), hydroxyapatite (HAp), beta-tricalcium phosphate (ß-TCP) or calcium silicate (CaSi) particles were added to a photocurable BisGMA/TEGDMA resin (1:1 in mols) at a 30 vol% fraction. Materials containing silanized or non-silanized barium glass particles were used as controls. Degree of conversion (DC) at the top and base of 2-mm thick specimens was determined by ATR-FTIR spectroscopy (n = 5). Translucency parameter (TP) and transmittance (%T) were determined using a spectrophotometer (n = 3). Biaxial flexural strength (BFS) and flexural modulus (FM) were determined by biaxial flexural testing after 24 h storage in water (n = 10). Ca2+ release in water was determined during 28 days by inductively coupled plasma optical emission spectrometry (n = 3). Statistical analysis was performed using ANOVA/Tukey test (DC: two-way; TP, %T; BFS and FM: one-way; Ca2+ release: repeated measures two-way, α = 5 %). RESULTS: CaSi and ß-TCP particles drastically reduced DC at 2 mm, TP and %T (p < 0.001). Compared to both controls, all Ca2+-releasing materials presented lower BFS (p < 0.001) and only the material with DCPD showed significantly lower FM (p < 0.05). The material containing CaSi presented the highest Ca2+ release, while among materials formulated with calcium orthophosphates the use of DCPD resulted in the highest release (p < 0.001). SIGNIFICANCE: CaSi particles allowed the highest Ca2+ release. Notwithstanding, the use of DCPD resulted in a material with the best compromise between optical behaviour, DC, strength and Ca2+ release.
Asunto(s)
Compuestos de Calcio , Fosfatos de Calcio , Ensayo de Materiales , Silicatos , Silicatos/química , Compuestos de Calcio/química , Fosfatos de Calcio/química , Espectroscopía Infrarroja por Transformada de Fourier , Durapatita/química , Resistencia Flexional , Ácidos Polimetacrílicos/química , Polietilenglicoles/química , Bisfenol A Glicidil Metacrilato/química , Resinas Compuestas/química , Vidrio/química , Calcio/química , Espectrofotometría , Fenómenos Químicos , Dióxido de Silicio , Compuestos de BarioRESUMEN
OBJECTIVE: The study aims to evaluate the effect of a glass ionomer cement (GIC; Fuji 9 Gold Label, GC) with added calcium orthophosphate particles and a calcium silicate cement (CSC; Biodentine, Septodont) regarding ion release, degradation in water, mineral content, and mechanical properties of demineralized dentin samples. METHODS: GIC, GIC + 5% DCPD (dicalcium phosphate dihydrate), GIC + 15% DCPD, GIC + 5% ß-TCP (tricalcium phosphate), GIC + 15% ß-TCP (by mass), and CSC were evaluated for Ca2+/Sr2+/F- release in water for 56 days. Cement mass loss was evaluated after 7-day immersion in water. Partially demineralized dentin disks were kept in contact with materials while immersed in simulated body fluid (SBF) at 37 °C for 56 days. The "mineral-to-matrix ratio" (MMR) was determined by ATR-FTIR spectroscopy. Dentin hardness and elastic modulus were obtained by nanoindentation. Samples were observed under scanning and transmission electron microscopy. Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ release from CSC and GIC (µg/cm2) were 4737.0 ± 735.9 and 13.6 ± 1.6, respectively. In relation to the unmodified GIC, the addition of DCPD or ß-TCP increased ion release (p < 0.001). Only the dentin disks in contact with CSC presented higher MMR (p < 0.05) and mechanical properties than those restored with a resin composite used as control (p < 0.05). Mass loss was similar for GIC and CSC; however, the addition of DCPD or ß-TCP increased GIC degradation (p < 0.05). CONCLUSION: Despite the increase in ion release, the additional Ca2+ sources did not impart remineralizing capability to GIC. Both unmodified GIC and CSC showed similar degradation in water. CLINICAL RELEVANCE: CSC was able to promote dentin remineralization.
Asunto(s)
Compuestos de Calcio , Fosfatos de Calcio , Calcio , Cementos de Ionómero Vítreo , Silicatos , Cementos de Ionómero Vítreo/farmacología , Cementos de Ionómero Vítreo/química , Calcio/análisis , Fosfatos/análisis , Cemento de Silicato/análisis , Cemento de Silicato/farmacología , Dentina , Agua/química , Ensayo de MaterialesRESUMEN
OBJECTIVE: to evaluate the effect a glass ionomer cement (GIC) containing hydroxyapatite (HAp) or calcium silicate (CaSi) particles on mineral content and mechanical properties of demineralized dentin. Ion release and compressive strength (CS) of the cements were also evaluated. METHODS: GIC (Fuji 9 Gold Label, GC), GIC+ 5%HAp and GIC+ 5%CaSi (by mass) were evaluated. Ion release was determined by induced coupled plasma optical emission spectroscopy (Ca2+/Sr2+) or ion-specific electrode (F-) (n = 3). A composite (Filtek Z250, 3 M ESPE) was used as control in remineralization tests. Demineralized dentin discs were kept in contact with materials in simulated body fluid (SBF) at 37 °C for eight weeks. Mineral:matrix ratio (MMR) was determined by ATR-FTIR spectroscopy (n = 5). Dentin hardness (H) and elastic modulus (E) were determined by nanoindentation (n = 10). CS was tested after 24 h and 7d in deionized water (n = 12). Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ and Sr2+ release was higher for the modified materials (p < 0.05). Only GIC+ 5%HAp showed higher F- release than the control (p < 0.05). All groups showed statistically significant increases in MMR, with no differences among them after 8 weeks (p > 0.05). No differences in dentin H or E were observed among groups (p > 0.05). HAp-modified GIC showed increased initial CS, while adding CaSi had the opposite effect (p < 0.05). After 7 days, GIC+ 5%CaSi presented lower CS in relation to control and GIC+ 5%HAp (p < 0.05). SIGNIFICANCE: GIC modification with HAp or CaSi affected CS and increased ion release; however, none of the groups showed evidence of dentin remineralization in comparison to the negative control.
Asunto(s)
Calcio , Cementos de Ionómero Vítreo , Calcio/análisis , Ensayo de Materiales , Cementos de Ionómero Vítreo/farmacología , Cementos de Ionómero Vítreo/química , Durapatita/farmacología , Durapatita/química , Dentina/químicaRESUMEN
Amphiphilic hydrogels are widely reported as systems with great potential for controlled drug release. Nevertheless, the majority of studies make use of functionalization or attachment of drugs to the polymer chains. In this study, we propose a strategy of combining amphiphilic polyurethanes with pH-responsive drugs to develop smart drug carriers. While the amphiphilic character of the polymer imparts an efficient load of hydrophobic and hydrophilic drugs, the drug's characteristics determine the selectivity of the medium delivery. Drug loading and release behavior as well as hydrolytic degradation of chemically crosslinked polyurethane hydrogels based on PEG and PCL-triol (PU (polyurethane) hydrogels) synthesized by an easy one-pot route were studied. PU hydrogels have been shown to successfully load the hydrophobic acidic drug sodium diclofenac, reaching a partition coefficient of 8 between the most hydrophobic PU and diclofenac/ethanol solutions. Moreover, an oral administration simulation was conducted by changing the environment from an acidic to a neutral medium. PU hydrogels release less than 5% of the drug in an acidic medium; however, in a PBS pH 7.4 solution, diclofenac is delivered in a sustained fashion for up to 40â¯h, achieving 80% of cumulative release.
Asunto(s)
Portadores de Fármacos/química , Hidrogeles/química , Poliuretanos/química , Antiinflamatorios no Esteroideos/química , Diclofenaco/química , Liberación de Fármacos , Concentración de Iones de Hidrógeno , Interacciones Hidrofóbicas e HidrofílicasRESUMEN
Adhesion, proliferation and differentiation of dental pulp stem cells (DPSCs) into chondrocytes were investigated in this work with the purpose of broadening the array of cell alternatives to the therapy of cartilage lesions related to tissue engineering approaches. A porous chitosan-xanthan (C-X) matrix was used as scaffold and kartogenin was used as a selective chondrogenic differentiation promoter. The scaffold was characterized regarding aspect and surface morphology, absorption and stability in culture medium, thickness, porosity, thermogravimetric behavior, X-ray diffraction, mechanical properties and indirect cytocompatibility. The behavior of DPSCs cultured on the scaffold was evaluated by scanning electron microscopy and cell differentiation, by histological analysis. A sufficiently stable amorphous scaffold with mean thickness of 0.89±0.01mm and high culture medium absorption capacity (13.20±1.88g/g) was obtained, and kartogenin concentrations as low as 100nmol/L were sufficient to efficiently induce DPSCs differentiation into chondrocytes, showing that the strategy proposed may be a straightforward and effective approach for tissue engineering aiming at the therapy of cartilage lesions.