RESUMEN
Fresh and frozen cartilage samples of the fetlock, carpus, and stifle were collected from 12 deceased horses. Half were measured immediately following extraction, and half were frozen for seven days and then measured. Seven indentations (various normalized displacements) were implemented with an indention rate of 0.1 mm/s. Solid phase aggregate modulus (Es), hyperelastic material constant (α), and fluid load fraction (F') of equine articular cartilage were assessed using the Ogden hyperelastic model. The properties were statistically compared in various joints (fetlock, carpus, and stifle), and between fresh and frozen samples using various statistical models. There was no statistical difference between the fetlock and carpus in the aggregate modulus (p = 0.5084), while both were significantly different from the stifle (fetlock: p = 0.0017 and carpus: p = 0.0406). For the hyperelastic material constant, no statistical differences between joints were observed (p = 0.3310). For the fluid load fraction, the fetlock and stifle comparison showed a difference (p = 0.0333), while the carpus was not different from the fetlock (p = 0.1563) or stifle (p = 0.3862). Comparison between the fresh and frozen articular cartilage demonstrated no significant difference among the joints in the three material properties: p = 0.9418, p = 0.7031, and p = 0.9313 for the aggregate modulus, the hyperelastic material constant, and the fluid load fraction, respectively.
Asunto(s)
Cartílago Articular , Articulaciones , Animales , Fenómenos Biomecánicos , CaballosRESUMEN
PURPOSE: Thicknesses of fresh equine articular cartilage surfaces from the fetlock, carpal and stifle joints were measured employing a needle probe test. MATERIALS AND METHODS: Eighty-seven samples used in measurement were cultivated from fetlock, carpal and stifle joints of 12 deceased within 4 h of death. After approximately three minutes of exposure to air during dissection, all cartilage samples were preserved in a saline solution to keep the articular cartilage hydrated for testing. The thickness was measured on five different spots on the same sample. The thicknesses of the fetlock, carpus and stifle were compared. RESULTS: The articular cartilage of the stifle was thicker than the fetlock and carpus, while the fetlock and the carpus had similar thickness values. The average thickness of the fetlock, carpal and stifle joint are 0.86, 0.87 and 2.1 mm, respectively. They were statistically compared using the Student t-test. The differences on the articular cartilage thicknesses between the fetlock and stifle, and carpus and stifle were "very highly significant" (p < 0.001). This indicates that the articular cartilage thickness of the stifle is significantly different from that of the fetlock and carpus. Four different surfaces in the fetlock and four in the carpal joint were also compared. Significant differences between each set of the four surfaces were not observed. In the carpus, the difference in thickness between the distal radius and proximal third carpal bone articular cartilage surfaces as well as the proximal radial carpal bone and distal radial carpal bone articular cartilage surfaces were statistically significant.