The chemical originals of natural superhydrophobic surfaces are based on botanic or animal wax or fat, which have poor chemical and thermal resistance. Herein, we report a simple chemical modification of stearic acid (STA) with γ-aminopropyl triethoxysilane (APTES), to obtain an organic-inorganic molecular hybrid STA-APTES compound. A flower-like hierarchically structured surface with superhydrophobicity can be obtained simply by casting the STA-APTES solution under ambient circumstance. The crystallization of the hydrocarbon chain from STA leads to the formation of the binary microstructure and reduces the surface tension, contributing to the superhydrophobicity of the as-formed surface. In addition, the condensation of Si(OCH2CH3)3 from APTES can lead to the cross-linking of the resultant surface, which endows the as-formed superhydrophobic surface with high performances, such as excellent thermal and solvent resistance, etc. This superhydrophobic surface prepared is superior to its many analogs in nature, promising a wide application especially in harsh circumstance.

Asunto(s)

Compuestos Inorgánicos/química , Compuestos Orgánicos/química , Interacciones Hidrofóbicas e Hidrofílicas , Microscopía Electrónica de Rastreo , Tensión Superficial

RESUMEN

The polymerization-induced phase-separation process of polyethersulfone (PES)-modified epoxy systems was monitored in situ continuously on a single sample throughout the entire curing process by using optical microscopes, time-resolved light scattering (TRLS), scanning electronic microscopes (SEM), and a rheometry instrument. At specific PES content a viscoelastic transformation process of phase inversion morphology to bicontinuous was found with an optical microscope. The rheological behavior during phase separation corresponds well with the morphology development. Light-scattering results monitoring the phase-separation process of systems with final phase inversion morphology show a typical exponential decay procedure of scattering vector qm. The characteristic relaxation time of phase separation can be described well by the WLF equation.