RESUMEN
This study investigates the use of waste glass as an active aggregate in glass polymers based on water glass, aiming to enhance the sustainability of construction materials by utilizing recyclable waste. Methodologically, the research employs a combination of water glass as a binder with waste glass, analyzing their chemical interaction and the resulting mechanical properties. The primary findings reveal that the inclusion of finely ground waste glass not only promotes the polycondensation and hardening processes of water glass but also significantly influences the adhesive and cohesive strengths of the developed glass polymers. After 7 days of hardening, the tensile strength of these materials exceeds that of standard concrete with values reaching up to 4.11 MPa, indicating strong adhesion capabilities that could pull out fragments of the concrete substrate. Conclusively, the study underscores the potential of waste glass in improving the structural and economic efficiencies of building materials, contributing to a reduction in landfill waste and offering a promising avenue for the innovative use of recyclable materials in construction.
RESUMEN
A feature of silicate materials is that they can exist in two antagonistic states-amorphous and crystalline. In both cases, alkalis, which are always present in chemical compositions, play an important role. A feature of alkalis in the composition of silicate materials is that at certain stages of the synthesis of products, they play a positive role, reducing the temperature of synthesis, but worsening the properties of these products at the stage of their operation. Synthesis products should be understood as important building materials such as building glass and cement. It is known that the performance properties of glass and cement can be improved by the extraction of alkalis. In the first part of the article, the issues of extraction of alkalis in amorphous silicate materials-inorganic glasses were considered. This article presents the results of studies on the extraction process of alkalis in crystalline silicate materials-cement.
RESUMEN
The main building materials widely used worldwide are those based on cement, glass, and ceramics. Taking into account the fact that the raw material base for the production of these materials is narrowing, and the quality of raw materials is declining, methods are being used to modify the structure of silicate materials in order to improve their properties when using cheaper raw materials and industrial waste, which should help reduce the energy intensity of their production. One of the ways to reduce energy consumption is the use of alkaline components in the chemical composition of silicate materials, which makes it possible to reduce the temperature of their synthesis. However, the presence of alkalis in the material at the stage of the operation is undesirable since it contributes, for example, to a decrease in the chemical resistance of silicate glasses or leads to the phenomenon of alkaline corrosion in cement products. In this regard, in order to reduce the negative impact of alkalis, it is necessary to extract them from the surface layers of the silicate material. There are various methods for extracting alkalis from silicate materials, some of which are presented in this article.
RESUMEN
This article presents a study of the effect of water glass and its introduction on the hydration of Portland cement and its properties in plastic and solid states. The introduction of sodium water glass into the mixing water extends the setting time of Portland cement by 35%, while introduction into the cement paste reduces it by 24.4%; for potassium water glass, the respective values are 10.8% and 10.8%. The introduction of sodium water glass into the mixing water decreases its consistency by 17.6%; its introduction into the cement paste reduces its consistency by 97%. Based on microcalorimetric studies and using the modelling method, mechanisms of the processes occurring in the cement paste, for various methods of introducing water glass admixtures, and their influence on the properties of cement are proposed. The important implications of the obtained results are that, using various methods for introducing admixtures of water glass, it is possible to regulate the setting of cement slurries within significant limits that are important during their transportation.
RESUMEN
The concept of the alkaline activity of powdered materials introduced into cement compositions has been proposed, along with methods for its determination. The possibility of using waste glass as an active additive to Portland cement was evaluated from the standpoint of alkaline activity. Replacing the Portland cement component with glass waste in the form of glass powder at amounts from 1 to 35% made it possible to maintain the cement composition's alkaline activity at a level that met the standard requirements. The previously unknown effects of mixed alkali in Portland cement in the presence of glass waste are described. Portland cement has a high potassium alkaline activity; however, container glass has a high sodium alkaline activity and a fairly low potassium alkaline activity. When glass waste is introduced into the structure of cement compositions, potassium alkaline activity is reduced.