RESUMEN
MoO2-Fe2O3 nanoparticle systems were successfully synthesized by mechanochemical activation of MoO2 and α-Fe2O3 equimolar mixtures throughout 0-12 h of ball-milling. The role of the long-range ferromagnetism of MoO2 on a fraction of more defect hematite nanoparticles supporting a defect antiferromagnetic phase down to the lowest temperatures was investigated in this work. The structure and the size evolution of the nanoparticles were investigated by X-ray diffraction, whereas the magnetic properties were investigated by SQUID magnetometry. The local electronic structure and the specific phase evolution in the analyzed system versus the milling time were investigated by temperature-dependent Mössbauer spectroscopy. The substantially shifted magnetic hysteresis loops were interpreted in terms of the unidirectional anisotropy induced by pinning the long-range ferromagnetic order of the local net magnetic moments in the defect antiferromagnetic phase, as mediated by the diluted magnetic oxide phase of MoO2, to those less defect hematite nanoparticles supporting Morin transition. The specific evolutions of the exchange bias and of the coercive field versus temperature in the samples were interpreted in the frame of the specific phase evolution pointed out by Mössbauer spectroscopy. Depending on the milling time, a different fraction of defect hematite nanoparticles is formed. Less nanoparticles supporting the Morin transition are formed for samples exposed to a longer milling time, with a direct influence on the induced unidirectional anisotropy and related effects.
RESUMEN
Li2FeGeS4 (LIGS) and Li2FeSnS4 (LITS), which are among the first magnetic semiconductors with the wurtz-kesterite structure, exhibit antiferromagnetism with TN ≈ 6 and 4 K, respectively. Both compounds undergo a conventional metamagnetic transition that is accompanied by a hysteresis; a reversible spin-flop transition is dominant. On the basis of constant-wavelength neutron powder diffraction data, we propose that LIGS and LITS exhibit collinear magnetic structures that are commensurate and incommensurate with propagation vectors km = [1/2, 1/2, 1/2] and [0, 0, 0.546(1)], respectively. The two compounds exhibit similar magnetic phase diagrams, as the critical fields are temperature-dependent. The nuclear structures of the bulk powder samples were verified using time-of-flight neutron powder diffraction along with synchrotron X-ray powder diffraction. (57)Fe and (119)Sn Mössbauer spectroscopy confirmed the presence of Fe(2+) and Sn(4+) as well as the number of crystallographically unique positions. LIGS and LITS are semiconductors with indirect and direct bandgaps of 1.42 and 1.86 eV, respectively, according to optical diffuse-reflectance UV-vis-NIR spectroscopy.