RESUMEN
Transfer method of chemically vapor deposition graphene is an appealing issue to realize its application as flexible and transparent electrodes. A universal stamping method to transfer as grown graphene from copper onto different flexible and transparent polymers (FTPs) reported here ensures simple, robust, rapid, clean and low-cost. This method relies on coating ethylene vinyl acetate (EVA) onto the as grown graphene, binding EVA coated graphene/Cu with FTPs and delamination by hydrogen bubbling process, which is analogous to the method used by stamping process where ink carries the imprint of the object onto any materials. The fate of the stamping method depends on how strongly the adhesion of EVA coated graphene/Cu with target FTPs. Interestingly, we have found that the thin film of EVA/graphene/Cu can only bind strongly with the FTPs of less than 25 µm in thickness and lower glass transition temperature value to the EVA while wide range of other FTPs are considered upon surface engineering to enhance the binding strength between FTPs and EVA. What's more, the electrical performance was investigated with a demonstration of triboelectric nanogenerators which confirmed the reliability of graphene transfer onto the FTPs and prospect for the development of flexible and transparent electronics.
RESUMEN
HYPOTHESIS: Transfer of chemical-vapor-deposition (CVD) grown monolayer graphene from one substrate to another requires a transfer agent. The transfer agent usually needs to be removed by washing with organic solvent such as acetone or high temperature annealing, which is harmful to the structure integrity and intrinsic property of a graphene film. Here, we propose the use of camphor as a transfer agent to transfer monolayer graphene onto a target dielectric substrate, which bypasses these demanding steps and only needs the common alcohol solvent rinsing. EXPERIMENTS: To facilitate a crack-free graphene transfer, the proposed approach allows the camphor supported polycrystalline graphene to be rationally fastened with a thickened and solidified edge bead (i.e. camphor oil-filled boundary). A layer of camphor was first deposited onto a graphene/copper surface. The backside copper substrate was then etched away, whilst the camphor/graphene bilayer was placed onto a SiO2/Si substrate. Finally, the camphor remaining on the camphor/graphene/SiO2/Si sublimed into a vapor. The graphene/SiO2 stack was then examined by microscopic, spectral and electrical characterization. FINDINGS: The results of our examination suggest that the proposed method can guarantee a clean and damage-free graphene transfer. This method is particularly attractive in the application area for nano/micro-electronics, where it provides CVD-grown graphene the ability to be used on wide varieties of substrates that are sensitive to organic solvents and high temperature.
RESUMEN
A novel roll-to-roll, etching-free, clean transfer of CVD-grown graphene from copper to plastic using surface-energy-assisted delamination in hot deionized water is reported. The delamination process is realized by water penetration between the hydrophobic graphene and a hydrophilic native oxide layer on a copper foil.The transferred graphene on plastic is used as a high-output flexible and transparent triboelectric nanogenerator.