RESUMEN
The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.
O objetivo deste estudo in vitro foi avaliar a resistência à tração de pinos de fibra de vidro submetidos a diferentes tratamentos de superfície. Quarenta e oito caninos superiores tiveram suas coroas seccionadas e as raízes tratadas endodonticamente. As raízes foram incluídas em resina acrílica e distribuídas em 3 grupos de acordo com o tratamento de superfície aplicado aos pinos: Grupo I: os pinos receberam agente silano por 30 s e adesivo; Grupo II: os pinos foram limpos com álcool e então receberam o agente silano e adesivo; Grupo III: os pinos foram submetidos ao condicionamento com ácido fosfórico a 37% por 30 s, seguido de agente silano e adesivo. Cada grupo foi dividido em 2 subgrupos de acordo com fotoativação do adesivo antes da inserção do pino no interior do canal: A – adesivo não foi fotoativado, B: o adesivo foi fotoativado. Todos os pinos foram cimentados com Panavia F e as amostras foram submetidas a teste de tração utilizando máquina universal de ensaios, com velocidade de 1 mm/min. Os dados obtidos foram submetidos à ANOVA a um critério e ao teste de Tukey com nível de significância de 5%. Houve diferença estatisticamente significante (p<0,01) entre o grupo GIII-B e os grupos GI-A e GI-B. Os demais grupos não apresentaram diferenças significantes entre si (p>0,05). Pode-se concluir que as substâncias utilizadas para a limpeza dos pinos interferiram em sua retenção, independente da fotopolimerização do adesivo.
Asunto(s)
Humanos , Análisis del Estrés Dental/métodos , Técnica de Perno Muñón/instrumentación , Tratamiento del Conducto Radicular , Diente Premolar , Resinas Compuestas/química , Cementos Dentales/química , Vidrio , Técnicas In Vitro , Polimerizacion , Cementos de Resina/química , Materiales de Obturación del Conducto Radicular/química , Propiedades de Superficie , Silanos/química , Resistencia a la TracciónRESUMEN
This study used micro-computed tomography (micro-CT) to evaluate the fit of the master gutta-percha cone at time of cone fit, gutta-percha volume in the filling material, and the filling material volume in relation to the canal at the apical limit of the working length. Root canals of 20 maxillary central incisors were prepared with rotary instruments and distributed into two groups (n=10). The gutta-percha cone tip was either plasticized (apical thermal impression technique - ATI) or not (conventional technique - CT), and its apical fit was checked. The apical 1 mm of working length was examined with a micro-CT, canals were filled with gutta-percha and sealer, and new micro-CT scans were obtained. In CT, gutta-percha filled 35.83 ± 15.05% of the canal at cone selection and 38.72 ± 11.64% after filling. In ATI, these values were 23.14 ± 7.74% and 26.98 ± 20.40%, respectively. Gutta-percha volume in the filling material, and filling material volume in relation to the canal were, respectively, 61.28 ± 11.64% and 87.76 ± 9.98% for CT, and 73.00 ± 20.41% and 89.96 ± 9.08% for ATI. No significant difference was found between cone selection and after canal filling, for either CT (p=0.593) or ATI (p=0.4975). The techniques did not differ significantly with respect to gutta-percha volume in the filling material (p=0.132) and filling material volume in relation to the canal (p=0.612). An ideal fit of the master gutta-percha cone at working length was not achieved regardless of the cone selection technique, and the material-filled area was similar for both techniques.
Asunto(s)
Gutapercha , Microtomografía por Rayos X/métodos , HumanosRESUMEN
This study used micro-computed tomography (micro-CT) to evaluate the fit of the master gutta-percha cone at time of cone fit, gutta-percha volume in the filling material, and the filling material volume in relation to the canal at the apical limit of the working length. Root canals of 20 maxillary central incisors were prepared with rotary instruments and distributed into two groups (n=10). The gutta-percha cone tip was either plasticized (apical thermal impression technique - ATI) or not (conventional technique - CT), and its apical fit was checked. The apical 1 mm of working length was examined with a micro-CT, canals were filled with gutta-percha and sealer, and new micro-CT scans were obtained. In CT, gutta-percha filled 35.83 ± 15.05% of the canal at cone selection and 38.72 ± 11.64% after filling. In ATI, these values were 23.14 ± 7.74% and 26.98 ± 20.40%, respectively. Gutta-percha volume in the filling material, and filling material volume in relation to the canal were, respectively, 61.28 ± 11.64% and 87.76 ± 9.98% for CT, and 73.00 ± 20.41% and 89.96 ± 9.08% for ATI. No significant difference was found between cone selection and after canal filling, for either CT (p=0.593) or ATI (p=0.4975). The techniques did not differ significantly with respect to gutta-percha volume in the filling material (p=0.132) and filling material volume in relation to the canal (p=0.612). An ideal fit of the master gutta-percha cone at working length was not achieved regardless of the cone selection technique, and the material-filled area was similar for both techniques.
Este estudo utilizou microtomografia computadorizada (micro-CT) para avaliar a adaptação do cone de guta-percha no momento da sua seleção, o volume de guta-percha no material obturador, e o volume do material obturador em relação ao canal no limite apical do comprimento de trabalho. Canais radiculares de 20 incisivos centrais superiores foram preparados com instrumentos rotatórios e distribuídos em dois grupos (n=10). A ponta do cone de guta-percha foi plastificada (técnica de impressão térmica apical - TIT) ou não (técnica convencional - TC), e seu ajuste apical foi verificado. O milimetro apical do comprimento de trabalho foi examinado em micro-CT, os canais foram preenchidos com guta-percha e cimento, e novas imagens em micro-CT foram obtidas. Na TC, a guta-percha preencheu 35,83 ± 15,05% do canal no momento da seleção do cone e 38,72 ± 11,64% após a obturação. Na TIT, estes valores foram de 23,14 ± 7,74% e 26,98 ± 20,40%, respectivamente. O volume de guta-percha no material obturador, e o volume do material obturador em relação ao canal, foram, respectivamente, 61,28 ± 11,64% e 87,76 ± 9,98% para a TC, e 73,00 ± 20,41% e 89,96 ± 9,08% para TIT. Não foi encontrada diferença significativa entre a seleção do cone e depois o preenchimento do canal para ambas as técnicas, TC (p =0,593) ou TIT (p=0,4975). As técnicas não diferiram significativamente com respeito ao volume de guta-percha no material obturador (p=0,132), e volume de preenchimento de material em relação ao canal (p=0,612). Um ajuste ideal do cone principal de guta-percha cone no seu comprimento de trabalho não foi alcançado, independentemente da técnica de seleção empregada, e a area preenchida pelo material obturador foi semelhante para ambas as técnicas.
Asunto(s)
Humanos , Gutapercha , Microtomografía por Rayos X/métodosRESUMEN
The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.
Asunto(s)
Análisis del Estrés Dental/métodos , Técnica de Perno Muñón/instrumentación , Tratamiento del Conducto Radicular , Diente Premolar , Resinas Compuestas/química , Cementos Dentales/química , Vidrio , Humanos , Técnicas In Vitro , Polimerizacion , Cementos de Resina/química , Materiales de Obturación del Conducto Radicular/química , Silanos/química , Propiedades de Superficie , Resistencia a la TracciónRESUMEN
PURPOSE: Dental fusion is defined as the union of two dental germs at some stage of their development. The aim of this article is to report the endodontic treatment of two clinical cases of dental fusion. CASE DESCRIPTION: In the first case, the patient was referred by an orthodontist for endodontic treatment of tooth 12, which was fused to 13. Surgical separation and later replacement of the involved elements in the dental arch was indicated. In the second case, the patient sought dental attendance due to spontaneous pain. In the radiographic exam, gemination in tooth 11 and fusion of 21 with a supernumerary tooth was observed. The fused teeth were endodontically treated, and patients were referred to other dental specialties to reestablish esthetics and function. CONCLUSION: The dentist must be able to diagnose, differentiate and treat these dental anomalies adequately, with the goal of maintaining patients' oral health.
OBJETO: Fusão dental é definida como sendo a união de dois germes dentais em algum momento do estágio de desenvolvimento. O objetivo desse artigo foi descrever o tratamento endodôntico de dois casos de fusão dental. DESCRIÇÃO DO CASO: No primeiro caso clínico, o paciente foi orientado pelo ortodontista a realizar tratamento endodôntico do dente 12, o qual estava fusionado ao dente 13. Foi realizada a separação cirúrgica dos elementos dentais e posterior reposicionamento no arco dental. No segundo caso clínico, o paciente procurou atendimento relatando dor espontânea na região anterior superior. Por meio do exame radiográfico, foi observado geminação do dente 11 e fusão do dente 21 com dente extranumerário. Em ambos os casos os dentes fusionados foram tratados endodônticamente e os pacientes encaminhados para restabelecimento da estética e função. CONCLUSÃO: O cirurgião dentista deve ter habilidade de diagnosticar, diferenciar e tratar adequadamente as anomalias dentárias, objetivando a manutenção da saúde oral dos pacientes.
Asunto(s)
Humanos , Masculino , Femenino , Niño , Adolescente , Diente Supernumerario/complicaciones , Dientes Fusionados/cirugía , Dientes Fusionados/diagnóstico , Tratamiento del Conducto RadicularRESUMEN
A articulação temporomandibular (ATM) é constituída pela fossa mandibular do osso temporal e côndilo d amandíbula. Ela é responsável pela movimentação da mandíbula durante a mastigação, deglutição e conversação. Entretanto, o excesso de uso e a perda de harmonia de seus constituintes articulares e musculares predispôem ao aparecimento da Disfunção Temporomandibular (DTM). Essa disfunção apresenta uma etiologia multifatorial com complexidade de sinais e sintomas que dificultam seu diagnóstico. Este estudo teve por objetivo traçar o perfil epidemiológico dos sujetos com DTM, tratados pela Faculdade de Ondontologia de Caruaru - Pernambuco. Foram coletados dados de 53 prontuários de sujeitos com DTM e as variáveis seguintes analisados: sexo, idade, abertura bucal, ausculta, presença de dores no ouvido, região cervical e cefaléia, dor muscular e hábitos gerais. Os resultados mostraram que a DTM acometeu em maior percentual o sexo feminino, na faixa etária entre 28 e 39 anos. Cerca de 41,5 por cento dos sujeitos referiram estalidos durante os movimentos da ATM. O bruxismo estava presente em 28,3 por cento dos sujeitos. E os dados em relação à dor mostraram que 75,5 por cento dos sujeitos referiram dor cervical, 71,1 por cento cefaléia associada e 28,3 por cento referiram dor no músculo masseter. Esta pesquisa mostrou que os principais fatores encolvidos nas DTMs seguem o padrão da literatura que trata do assunto
Asunto(s)
Femenino , Adulto , Epidemiología , Articulación Temporomandibular , Trastornos de la Articulación TemporomandibularRESUMEN
O presente estudo testou in vitro, a capacidade vedante de três materiais em forma de película seladora, aplicada sobreo terço cervical das obturações e assoalho da câmara pulpar, imediatamente pós-obturação de canais radiculares, visandoprevenir a microinfiltração coronária, através da interface parede dentinária / material obturador do canal radicular.Utilizou-se de quarenta molares humanos com raízes completamente formadas, os canais radiculares instrumentadospela técnica de Oregon, irrigados com solução de hipoclorito de sódio a 0,5% e obturados pela técnica clássica decondensação lateral. Após a limpeza da câmara pulpar e das superfícies dentais, impermeabilizaram-se coroas e raízescom a utilização do esmalte para unhas incolor. Os dentes foram divididos aleatoriamente em quatro grupos de dezdentes, sendo um grupo controle e três grupos experimentais. Diferentes materiais foram aplicados sobre o assoalhoda câmara pulpar e terço cervical das obturações de cada grupo experimental: G1- Super Bonder; G2- Esmalte paraunhas; G3- Primer & Bonder 2.1; e G4- nenhum material foi aplicado. Logo após aplicação, os elementos dentáriosforam termociclados e imersos na tinta Nankin por um período de cinco dias. Em seguida foram então lavados, secose o esmalte para unhas aplicado superficialmente, removido. Os espécimes foram então descalcificados, desidratadose diafanizados sendo, posteriormente, examinados por três examinadores previamente calibrados. Os resultados, apóstestes estatísticos, segundo técnica descritiva e inferencial (Kruskal-Wallis e Comparação Pareada), determinaram quenão houve diferença estatisticamente significante entre os três materiais. Os produtos, esmalte para unhas e Super Bondermostraram-se estatisticamente superiores ao grupo controle.