Nanotechnology ; 33(23)2022 Mar 15.
Artículo en Inglés | MEDLINE | ID: mdl-35289768

RESUMEN

In this paper, we are reporting on the fabrication of a porous silicon/Au and silicon filament/Au using the two-step Au-assisted chemical etching of p-type Si with a specific resistivity of 0.01, 1, and 12 Ω·cm when varying the Au deposition times. The structure analysis results show that with an increasing Au deposition time of up to 7 min, the thickness of the porous Si layer increases for the same etching duration (60 min), and the morphology of the layer changes from porous to filamentary. This paper shows that the uniform macro-porous layers with a thickness of 125.5-171.2µm and a specific surface area of the mesopore sidewalls of 142.5-182 m2·g-1are formed on the Si with a specific resistivity of 0.01 Ω·cm. The gradient macro-porous layers with a thickness of 220-260µm and 210-290µm, the specific surface area of the mesopore sidewalls of 3.7-21.7 m2·g-1and 17-29 m2·g-1are formed on the silicon with a specific resistivity of 1 and 12 Ω·cm, respectively. The por-Si/Au has excellent low-temperature electro oxidation performance with ethanol, the activity of ethanol oxidation is mainly due to the synergistic effect of the Au nanoparticles and porous Si. The formation mechanism of the uniform and gradient macro-porous layers and ethanol electro-oxidation on the porous/filament silicon, decorated with Au nanoparticles, was established. The por-Si/Au structures with perpendicularly oriented pores, a high por-Si layer thickness, and a low mono-Si layer thickness (with a specific resistivity of 1 Ω·cm) are optimal for an effective ethanol electro-oxidation, which has been confirmed with chronoamperometry measurements.

2.
Micromachines (Basel) ; 10(12)2019 Dec 12.
Artículo en Inglés | MEDLINE | ID: mdl-31842302

RESUMEN

The formation of porous silicon by Pd nanoparticles-assisted chemical etching of single-crystal Si with resistivity ρ = 0.01 Ω·cm at 25 °C, 50 °C and 75 °C in HF/H2O2/H2O solution was studied. Porous layers of silicon were studied by optical and scanning electron microscopy, and gravimetric analysis. It is shown that por-Si, formed by Pd nanoparticles-assisted chemical etching, has the property of ethanol electrooxidation. The chromatographic analysis of ethanol electrooxidation products on por-Si/Pd shows that the main products are CO2, CH4, H2, CO, O2, acetaldehyde (CHO)+, methanol and water vapor. The mass activity of the por-Si/Pd system was investigated by measuring the short-circuit current in ethanol solutions. The influence of the thickness of porous silicon and wafer on the mass activity and the charge measured during ethanol electrooxidation was established. Additionally, the mechanism of charge transport during ethanol electrooxidation was established.