RESUMEN

A facile one-pot solvothermal method was applied to synthesize a magnetic biochar composite (MB) using phoenix tree leaves-derived biochar as the carbon matrix. The structure of MB was optimized by varying the load ratio and particle size of Fe3O4 nanoparticles on biochar. Time-dependent structure and composition evolution of solid and liquid phases during heterogeneous solvothermal process were investigated to understand the formation mechanism of MB. Firstly, Fe2+/Fe3+ ions were coordinated by oxygen-containing groups on biochar and part of them were hydrolyzed to form iron hydroxides. Then, those iron-containing precursors were thermally decomposed and reduced to iron oxides; and finally Fe3O4 nanoparticles were generated. The MB had an adsorption capacity for Cr(VI) of 55.0 mg/g in an aqueous solution, which exceeds those of biochar (39.8 mg/g) and Fe3O4 nanoparticles (26.5 mg/g). The adsorption mechanism study reveals that biochar as a carbon skeleton mainly provided binding sites for Cr(VI) and electron-donor groups for reduction of Cr(VI), while Fe3O4 nanoparticles mainly involved in the immobilization of newly formed Cr(III) through formation of Fe(III)-Cr(III) hydroxide. MB exhibited a stable structure with a lower Fe leakage at pH 2.0 than that of a comparable magnetic biochar sample prepared by conventional co-precipitation method. Recycling experiments suggested that MB could keep 84% of its initial removal capability for Cr(VI) even after seven cycles. The results indicate that solvothermal method is a promising alternative to prepare magnetic biochar for adsorption of heavy metal-containing wastewater.

Asunto(s)

Cromo/química , Eliminación de Residuos Líquidos/métodos , Contaminantes Químicos del Agua/química , Adsorción , Carbón Orgánico/química , Cromo/análisis , Compuestos Férricos , Magnetismo , Contaminantes Químicos del Agua/análisis

RESUMEN

Fe3O4@SiO2-NH2 magnetic particles with core-shell structure were attached on carboxylated biochar derived from phoenix tree leaves to synthesize a novel magnetic biochar for removing Cr(VI) ions from acidic solutions. FSEM, FTEM, XRD characterizations of the synthesized magnetic biochar revealed that the Fe3O4@SiO2-NH2 magnetic particles distributed uniformly on the surface or macrospores of carboxylated biochar by strong chemical bonding. The Cr(VI) ions adsorption capacity of magnetic biochar was 27.2mg·g-1, surpassing original carboxylated biochar (18.2mg·g-1). VSM and XPS characterizations demonstrated that the attached Fe3O4@SiO2-NH2 magnetic particles not only endowed biochar with perfect magnetic property (23emu·g-1) but also provided complexing sites for binding Cr(III) cations reduced from Cr(VI) anions. The Cr(VI) ions removal by magnetic biochar contained three steps: (1) adsorption of Cr(VI) anions by protonated functional groups; (2) reduction of Cr(VI) anions to Cr(III) cations by electron-donor groups; and (3) chelation of Cr(III) cations by amine groups. The adsorption recycling test showed that magnetic biochar kept 85% of its initial Cr(VI) adsorption capacity at the sixth cycle, and the Fe leakage under pH1.0 was smaller than 0.25mg·L-1. The results indicated that this novel magnetic biochar was applicable for the practical treatment of Cr(VI)-containing wastewater.