RESUMEN
Platinum group metal (PGM)-free electrocatalysts have emerged as promising alternatives to replace Pt for the oxygen reduction reaction (ORR) in anion exchange membrane fuel cells (AEMFCs). However, traditional synthesis methods limit the single-atom site density due to metal agglomeration at higher temperatures. This work explores the preparation of hierarchically porous atomically dispersed electrocatalysts for the ORR. The materials were prepared via ionothermal synthesis, where magnesium nitrate was used to prepare hierarchically porous carbon materials. The in-situ formed Mg-Nx sites were trans-metalated to yield ORR-active Fe-Nx sites. The resulting carbon-based catalysts displayed excellent electrocatalytic activity, attributed to the atomically dispersed Fe-Nx active sites and high meso- and macroporosity that enhances the mass transport and exposes more accessible active sites.
RESUMEN
Transition-metal- and nitrogen-codoped carbide-derived carbon/carbon nanotube composites (M-N-CDC/CNT) have been prepared, characterized, and used as cathode catalysts in anion-exchange membrane fuel cells (AEMFCs). As transition metals, cobalt, iron, and a combination of both have been investigated. Metal and nitrogen are doped through a simple high-temperature pyrolysis technique with 1,10-phenanthroline as the N precursor. The physicochemical characterization shows the success of metal and nitrogen doping as well as very similar morphologies and textural properties of all three composite materials. The initial assessment of the oxygen reduction reaction (ORR) activity, employing the rotating ring-disk electrode method, indicates that the M-N-CDC/CNT catalysts exhibit a very good electrocatalytic performance in alkaline media. We find that the formation of HO2 - species in the ORR catalysts depends on the specific metal composition (Co, Fe, or CoFe). All three materials show excellent stability with a negligible decline in their performance after 10000 consecutive potential cycles. The very good performance of the M-N-CDC/CNT catalyst materials is attributed to the presence of M-N x and pyridinic-N moieties as well as both micro- and mesoporous structures. Finally, the catalysts exhibit excellent performance in in situ tests in H2/O2 AEMFCs, with the CoFe-N-CDC/CNT reaching a current density close to 500 mA cm-2 at 0.75 V and a peak power density (P max) exceeding 1 W cm-2. Additional tests show that P max reaches 0.8 W cm-2 in an H2/CO2-free air system and that the CoFe-N-CDC/CNT material exhibits good stability under both AEMFC operating conditions.
RESUMEN
Highly active electrocatalysts for electrochemical oxygen reduction reaction (ORR) were prepared by high-temperature pyrolysis from 5-methylresorcinol, Co and/or Fe salts and dicyandiamide, which acts simultaneously as a precursor for reactive carbonitride template and a nitrogen source. The electrocatalytic activity of the catalysts for ORR in alkaline solution was studied using the rotating disc electrode (RDE) method. The bimetallic catalyst containing iron and cobalt (FeCoNC-at) showed excellent stability and remarkable ORR performance, comparable to that of commercial Pt/C (20 wt%). The superior activity was attributed to high surface metal and nitrogen contents. The FeCoNC-at catalyst was further tested in anion exchange membrane fuel cell (AEMFC) with poly-(hexamethyl-p-terphenylbenzimidazolium) (HMT-PMBI) membrane, where a high value of peak power density (Pmax = 415 mW cm-2) was achieved.