RESUMEN
PURPOSE: This in vitro study investigated the null hypothesis that metal-free crowns induce fracture loads and mechanical behavior similar to metal ceramic systems and to study the fracture pattern of ceramic crowns under compressive loads using finite element and fractography analyses. MATERIALS AND METHODS: Six groups (n = 8) with crowns from different systems were compared: conventional metal ceramic (Noritake) (CMC); modified metal ceramic (Noritake) (MMC); lithium disilicate-reinforced ceramic (IPS Empress II) (EMP); leucite-reinforced ceramic (Cergogold) (CERG); leucite fluoride-apatite reinforced ceramic (IPS d.Sign) (SIGN); and polymer crowns (Targis) (TARG). Standardized crown preparations were performed on bovine roots containing NiCr metal dowels and resin cores. Crowns were fabricated using the ceramics listed, cemented with dual-cure resin cement, and submitted to compressive loads in a mechanical testing machine at a 0.5-mm/min crosshead speed. Data were submitted to one-way ANOVA and Tukey tests, and fractured specimens were visually inspected under a stereomicroscope (20×) to determine the type of fracture. Maximum principal stress (MPS) distributions were calculated using finite element analysis, and fracture origin and the correlation with the fracture type were determined using fractography. RESULTS: Mean values of fracture resistance (N) for all groups were: CMC: 1383 ± 298 (a); MMC: 1691 ± 236 (a); EMP: 657 ± 153 (b); CERG: 546 ± 149 (bc); SIGN: 443 ± 126 (c); TARG: 749 ± 113 (b). Statistical results showed significant differences among groups (p < 0.05) represented by different lowercase letters. Metal ceramic crowns presented fracture loads significantly higher than the others. Ceramic specimens presented high incidence of fractures involving either the core or the tooth, and all fractures of polymer crown specimens involved the tooth in a catastrophic way. Based on stress and fractographic analyses it was determined that fracture occurred from the occlusal to the cervical direction. CONCLUSIONS: Within the limitations of this study, the results indicated that the use of ceramic and polymer crowns without a core reinforcement should be carefully evaluated before clinical use due to the high incidence of failure with tooth involvement. This mainly occurred for the polymer crown group, although the fracture load was higher than normal occlusal forces. High tensile stress concentrations were found around and between the occlusal loading points. Fractographic analysis indicated fracture originating from the load point and propagating from the occlusal surface toward the cervical area, which is the opposite direction of that observed in clinical situations.
Asunto(s)
Coronas , Porcelana Dental/química , Análisis de Elementos Finitos , Óxido de Aluminio/química , Silicatos de Aluminio/química , Animales , Apatitas/química , Bisfenol A Glicidil Metacrilato/química , Bovinos , Aleaciones de Cromo/química , Resinas Compuestas/química , Análisis del Estrés Dental , Recubrimientos Dentinarios/química , Cementos de Ionómero Vítreo/química , Compuestos de Litio/química , Ensayo de Materiales , Aleaciones de Cerámica y Metal/química , Polietilenglicoles/química , Ácidos Polimetacrílicos/química , Técnica de Perno Muñón/instrumentación , Compuestos de Potasio/química , Cementos de Resina/química , Cemento de Silicato/química , Estrés Mecánico , Fracturas de los Dientes/fisiopatología , Cemento de Fosfato de Zinc/químicaRESUMEN
The aim of this study was to assess the effect of bleaching agents (10% and 16% carbamide peroxide) on the roughness of two dental ceramics in vitro, and to analyze the surface by scanning electronic microscopy (SEM). Two bleaching agents (10% and 16% / Whiteness, FGM Gel) and two microparticle feldspathic ceramics (Vita VM7 and Vita VM13) were used. Forty disks of Vita VM7 and Vita VM13 ceramic were manufactured, measuring 4mm in diameter and 4mm high, in accordance with the manufacturers’ recommendations, and were divided into 4 groups (n=10): (1) VM7 + Whiteness 10%; (2) VM7 + Whiteness 16%; (3) VM13 + Whiteness 10%; (4) VM13 + Whiteness 16%. The bleaching agent was applied for 8 hours a day for 15 days and during the intervals the test specimens were stored in distilled water at 37°C. The roughness (Ra) of the test specimens was evaluated before and after exposure to the bleaching agents using a laser roughness meter and the topographic description was analyzed by SEM. The statistical analysis of roughness data showed significant differences in the VM7 groups, using paired t-test, p=0.05 (VM7 + Whiteness 10%: p=0.002; VM7 + Whiteness 16%: p=0.001) and two-sample t-test (VM7 p=0,047), and no significant difference was found among VM13 groups. The qualitative SEM analysis showed different degrees of surface changes. The results suggest that the roughness of the tested ceramic surfaces increased after exposure to the bleaching agents.
O objetivo do estudo foi avaliar o efeito de agente clareador (10% e 16% de peroxido de carbamida) na rugosidade de duas ceramicas dentais in vitro e analisar a superficie atraves da microscopia eletronica de varredura (SEM). Foram utilizados dois agentes clareadores (10% e 16% / Whiteness, FGM Gel) e duas ceramicas feldspaticas microparticuladas (Vita VM7 e Vita VM13). Foram confeccionados quarenta discos de ceramica Vita VM7 e Vita VM13, com 4mm de diametro e 4mm de altura, de acordo com as recomendacoes do fabricante, sendo divididos em 4 grupos (n=10): G1- VM7 + Whiteness 10%, G2- VM7 + Whiteness 16%, G3- VM13 + Whiteness 10% e G4- VM13 + Whiteness 16%. O agente clareador foi aplicado por 8 horas durante 15 dias e durante os intervalos os corpos de prova (cp) ficavam armazenados em agua destilada a 37°C. A rugosidade (Ra) dos cp foi avaliada antes e apos a exposicao aos agentes clareadores utilizando o rugosimetro a laser Perthomether S8P, e a descricao topografica foi analisada no MEV. A analise estatistica na rugosidade mostrou diferenca significante entre os grupos da VM7, usando o teste pareado, p=0.05 (VM7 + Whiteness 10%: p=0.002; VM7 + Whiteness 16%: p=0.001) e nao foi encontrado diferenca estatistica para os grupos da VM13. A descricao qualitativa no SEM evidenciou alteracao nas superficies em diferentes graus. Os resultados sugeriram que as superficies das ceramicas testadas aumentaram a rugosidade apos a exposicao ao agente clareador.
Asunto(s)
Humanos , Peróxidos/química , Urea/análogos & derivados , Porcelana Dental/química , Blanqueadores Dentales/química , Peróxidos/administración & dosificación , Propiedades de Superficie , Temperatura , Factores de Tiempo , Urea/administración & dosificación , Urea/química , Ensayo de Materiales , Agua/química , Microscopía Electrónica de Rastreo , Cerámica/química , Compuestos de Potasio/química , Silicatos de Aluminio/química , Blanqueadores Dentales/administración & dosificación , Peróxido de Carbamida , Geles , Rayos LáserRESUMEN
This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): GI-VM7 + 10% Whiteness, G2-VM7 + 16% Whiteness, G3-VM13 + 10% and G4-VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37 degrees C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann-Whitney tests (p < 0.05). The microhardness values before exposure were: g1-433 (57); g2-486 (22); g3-509 (28); g4-518 (24), and after exposure: G1-349 (32); G2-496 (95); G3-519 (38); G4-502 (81). G2 exhibited a higher and significant difference than GI in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.
Asunto(s)
Cerámica , Materiales Dentales , Dureza/efectos de los fármacos , Peróxidos/farmacología , Blanqueadores Dentales/farmacología , Urea/análogos & derivados , Peróxido de Carbamida , Pruebas de Dureza , Urea/farmacologíaRESUMEN
This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% and G4- VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37°C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann- Whitney tests (p<0.05). The microhardness values before exposure were: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), and after exposure: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exhibited a higher and significant difference than G1 in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.
Este estudo examinou o efeito do agente clareador peroxido de carbamida a 10% e a 16% na microdureza superficial de ceramicas feldspaticas micro-particuladas (VM7 e VM13, Vita Zahnfabrik). Quarenta corpos-de-prova (8 mm de diametro, 2 mm de espessura) foram divididos em quatro grupos (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% e G4- VM13 + 16% Whiteness. Os agentes clareadores foram aplicados por 8 horas durante 15 dias e os cp foram armazenados em agua destilada a 37°C. A dureza Vickers (HV) de cada cp foi determinada. Os dados foram analisados pelos testes de Wilcoxon e Mann-Whitney (p<0.05). Os valores da dureza antes da exposicao ao agente clareador foram: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), e depois da exposicao: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exibiu diferenca significante e microdureza maior comparado ao G1 nos grupos da VM7 e o efeito da concentracao do clareador foi significante, apresentados atraves dos testes Mann-Whitney. Para VM13, ambos testes, Wilcoxon e Mann-Whitney, nao apresentaram diferenca significante. Quando o peroxido de carbamida a 10% foi avaliado, a microdureza da ceramica VM7 foi afetada, e nao houve diferenca na microdureza entre as ceramicas VM7 e VM13 quando o peroxido de carbamida a 16% foi utilizado.
Asunto(s)
Peróxidos/farmacología , Urea/análogos & derivados , Cerámica , Materiales Dentales , Blanqueadores Dentales/farmacología , Dureza/efectos de los fármacos , Urea/farmacología , Peróxido de Carbamida , Pruebas de DurezaRESUMEN
OBJECTIVES: Evaluate the flexural strength (sigma) and subcritical crack growth (SCG) under cyclic loading of glass-infiltrated alumina-based (IA, In-Ceram Alumina) and zirconia-reinforced (IZ, In-Ceram Zirconia) ceramics, testing the hypothesis that wet environment influences the SCG of both ceramics when submitted to cyclic loading. METHODS: Bar-shaped specimens of IA (n=45) and IZ (n=45) were fabricated and loaded in three-point bending (3P) in 37 degrees C artificial saliva (IA(3P) and IZ(3P)) and cyclic fatigued (F) in dry (D) and wet (W) conditions (IA(FD), IA(FW), IZ(FD), IZ(FW)). The initial sigma and the number of cycles to fracture were obtained from 3P and F tests, respectively. Data was examined using Weibull statistics. The SCG behavior was described in terms of crack velocity as a function of maximum stress intensity factor (K(Imax)). RESULTS: The Weibull moduli (m=8) were similar for both ceramics. The characteristic strength (sigma(0)) of IA and IZ was and 466MPa 550MPa, respectively. The wet environment significantly increased the SCG of IZ, whereas a less evident effect was observed for IA. In general, both ceramics were prone to SCG, with crack propagation occurring at K(I) as low as 43-48% of their critical K(I). The highest sigma of IZ should lead to longer lifetimes for similar loading conditions. SIGNIFICANCE: Water combined with cyclic loading causes pronounced SCG in IZ and IA materials. The lifetime of dental restorations based on these ceramics is expected to increase by reducing their direct exposure to wet conditions and/or by using high content zirconia ceramics with higher strength.
Asunto(s)
Porcelana Dental/química , Análisis del Estrés Dental , Vidrio , Ensayo de Materiales , Docilidad , Análisis de Supervivencia , AguaRESUMEN
The aim of this study was to assess the effect of bleaching agents (10% and 16% carbamide peroxide) on the roughness of two dental ceramics in vitro, and to analyze the surface by scanning electronic microscopy (SEM). Two bleaching agents (10% and 16%/Whiteness, FGM Gel) and two microparticle feldspathic ceramics (Vita VM7 and Vita VM13) were used. Forty disks of Vita VM7 and Vita VM13 ceramic were manufactured, measuring 4 mm in diameter and 4 mm high, in accordance with the manufacturers' recommendations, and were divided into 4 groups (n = 10): (1) VM7 + Whiteness 10%; (2) VM7 + Whiteness 16%; (3) VM13 + Whiteness 10%; (4) VM13 + Whiteness 16%. The bleaching agent was applied for 8 hours a day for 15 days and during the intervals the test specimens were stored in distilled water at 37 degrees C. The roughness (Ra) of the test specimens was evaluated before and after exposure to the bleaching agents using a laser roughness meter and the topographic description was analyzed by SEM. The statistical analysis of roughness data showed significant differences in the VM7 groups, using paired t-test, p = 0.05 (VM7 + Whiteness 10%: p = 0.002; VM7 + Whiteness 16%: p = 0.001) and two-sample t-test (VM7 p = 0.047), and no significant difference was found among VM13 groups. The qualitative SEM analysis showed different degrees of surface changes. The results suggest that the roughness of the tested ceramic surfaces increased after exposure to the bleaching agents.
Asunto(s)
Porcelana Dental/química , Peróxidos/química , Blanqueadores Dentales/química , Urea/análogos & derivados , Silicatos de Aluminio/química , Peróxido de Carbamida , Cerámica/química , Geles , Humanos , Rayos Láser , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Peróxidos/administración & dosificación , Compuestos de Potasio/química , Propiedades de Superficie , Temperatura , Factores de Tiempo , Blanqueadores Dentales/administración & dosificación , Urea/administración & dosificación , Urea/química , Agua/químicaRESUMEN
PURPOSE: To compare the flexural strength of two glass-infiltrated high-strength ceramics and two veneering glass-ceramics. MATERIALS AND METHODS: Four ceramic materials were tested: two glass-infiltrated high-strength ceramics used as framework in metal-free restorations [In-Ceram Zirconia IZ (Gr1) and In-Ceram Alumina IA (Gr2)], and two glass-ceramics used as veneering material in metal-free restorations [Vita VM7 (Gr3) and Vitadur-alpha (Gr4)]. Bar specimens (25 x 5 x 2 mm3) made from core ceramics, alumina, and zirconia/alumina composites were prepared and applied to a silicone mold, which rested on a base from a gypsum die material. The IZ and IA specimens were partially sintered in an In-Ceram furnace according to the firing cycle of each material, and then were infiltrated with a low-viscosity glass to yield bar specimens of high density and strength. The Vita VM7 and Vitadur-alpha specimens were made from veneering materials, by vibration of slurry porcelain powder and condensation into a two-part brass Teflon matrix (25 x 5 x 2 mm3). Excess water was removed with absorbent paper. The veneering ceramic specimens were then removed from the matrix and were fired as recommended by the manufacturer. Another ceramic application and sintering were performed to compensate the contraction of the feldspar ceramic. The bar specimens were then tested in a three-point bending test. RESULTS: The core materials (Gr1: 436.1 +/- 54.8; Gr2: 419.4 +/- 83.8) presented significantly higher flexural strength (MPa) than the veneer ceramics (Gr3: 63.5 +/- 9.9; Gr4: 57.8 +/- 12.7). CONCLUSION: In-Ceram Alumina and Zirconia were similar statistically and more resistant than VM7 and Vitadur-alpha.