RESUMEN
INTRODUCTION: The purpose of this study was to evaluate whether the mixing method of AH Plus Jet sealer affects its physicochemical and mechanical properties. METHODS: The properties of AH Plus Jet sealer were analyzed when mixed using either the Auto Mix Tip or manual mixing. The evaluated properties included radiopacity (n = 5), initial and final setting times (n = 5), flow (n = 5), and solubility (n = 3), following specifications outlined in ISO 6876/2012 and ADA Nº 57/2000. pH levels were measured at intervals of 3, 24, 72, and 168 hours (n = 10). The push-out bond strength test was conducted using a universal testing machine and using bovine teeth (n = 30). Failure modes were analyzed with stereomicroscopy. Porosity was evaluated under micro-CT (n = 5), and scanning electron microscopy was also performed (n = 5). One-way analysis of variance and Tukey, unpaired t-tests, or Mann-Whitney tests were used with a significance level of 5%. RESULTS: The Auto Mix exhibited a radiopacity value of 12.11 mmAl, whereas manual mixing resulted in 12.55 mmAl (P > .05). For initial and final setting times, Auto Mix showed 901 minutes and 1779 minutes, respectively, while manual mixing recorded values of 631 minutes and 1504 minutes (P < .05). In terms of flow, Auto Mix demonstrated higher values (25.26 mm) than manual mixing (21.71 mm) (P < .05). No statistical differences were observed between the two methods for solubility and pH (P > .05). Manual mixing presented a higher bond strength value (14.52 MPa) than Auto Mix (9.81 MPa) (P < .05). The mixed failure mode was the most frequent outcome for both methods. The highest porosity was observed for Auto Mix (P < .05). Scanning electron microscopy analysis revealed that manual mixing resulted in a smoother surface with fewer pores and smaller, more evenly distributed agglomerates compared to automatic mixing. CONCLUSION: The mixing method employed for AH Plus Jet sealer influences some physicochemical and mechanical properties of the material.
Asunto(s)
Resinas Epoxi , Ensayo de Materiales , Materiales de Obturación del Conducto Radicular , Materiales de Obturación del Conducto Radicular/química , Bovinos , Animales , Resinas Epoxi/química , Microscopía Electrónica de Rastreo , Solubilidad , Concentración de Iones de HidrógenoRESUMEN
OBJECTIVES: To perform a systematic review of animal studies that compared the histopathological characteristics between teeth with apical periodontitis after endodontic treatment in one or two visits. MATERIALS AND METHODS: This systematic review was registered on the International Prospective Register of Systematic Reviews (PROSPERO) - CRD42022340849. Studies were collected from PubMed/MEDLINE, LILACS, EMBASE, Livivo, SciELO, Web of Science, Scopus, and Cochrane Library and manual and gray literature searches. Animal studies that evaluated histological characteristics after endodontic treatment of teeth with apical periodontitis in one or two visits were included. Risk of bias analysis of the included studies was performed using the Systematic Review Centre for Laboratory Animal Experimentation (SYRCLE) tool. Data synthesis of the included studies with quantitative data was performed, and meta-analysis was conducted with the Comprehensive Meta-Analysis software, using the random effects model and odds ratio (OR). RESULTS: Eighteen studies met the inclusion criteria (Kappa = 0.891). Meta-analyses indicated values in inflammatory infiltrate intensity with effect size of 5.5% (95% CI: 0.020-0.148; p < 0.001), periodontal ligament thickness: 25.6% (95% CI: 0.134-0.487; p < 0.001), dentin resorption: 13% (95% CI: 0.015-1.141; p = 0.066), cementum resorption: 7.1% (95% CI: 0.015-0.325; p = 0.001), bone resorption: 1.4% (95% CI: 0.002-0.130; p < 0.001), mineralized tissue resorption: 42.8% (95% CI: 0.110-1.671; p = 0.222), biological apical sealing: 13.1% (95% CI: 0.055-0.314; p < 0.001), and presence of microorganisms: 10.3% (95% CI: 0.014-0.747; p = 0.025). CONCLUSIONS: When considering animal studies, the two-visit endodontic treatment, using calcium hydroxide-based intracanal medication, resulted in better biological repair characteristics. CLINICAL RELEVANCE: A two-visit endodontic treatment with calcium hydroxide-based intracanal medication yields superior histopathological outcomes.