In this study we show that pure and well crystallized nanoparticles of Ba(x)Sr(1-x)TiO(3) (BST) can be synthesized over the entire range of composition through the hydrolysis and further crystallization of alkoxide precursors under supercritical conditions. To our knowledge, this is the first time that the whole ferroelectric solid solution has been produced in a continuous way, using the same experimental conditions. The composition of the powder can be easily controlled by adjusting the feed solution composition. The powders consist of soft-aggregated monocrystalline nanoparticles with an average particle size ranging from approximately 20 to 40 nm. Ferroelectric ceramics with accurately adjustable Curie temperature (100-390 K) can thus be obtained by sintering.
RESUMEN
Pure and well-crystallized Barium Strontium Titanate (BST) nanoparticles with controlled Ba/Sr ratio have been successfully synthesized under supercritical conditions using a continuous-flow reactor in the temperature range of 150-380 degrees C at 26 MPa. To synthesize the Ba0.6Sr0.4TiO3 composition, alkoxides, ethanol and water were used. The resulting nanopowder consists of fine particles with an average particle size of 23 nm. The results show that the Ba/Sr ratio of this powder can be accurately controlled from the composition of precursor. The characterization of the as-synthesized Ba0.6Sr0.4TiO3 solid-solution and the dielectric properties of the sintered ceramics are here reported.