RESUMEN
A set of five vitrimers with glass transition temperatures in the range of 80-90 °C were designed to assess the effect of the network structure and disulfide concentration on their dynamic and mechanical properties, and to find the best performing system overall compared to the commercial Araldite LY1564/Aradur 3486 commercial thermoset system. Vitrimer networks were prepared by incorporating mono- and bifunctional epoxy reactive diluents and an amine chain extender into the Araldite LY1564/4-aminophenyldisulfide system.
RESUMEN
Traditional crosslinked aero grade epoxy resins have excellent thermal-mechanical properties and solvent resistance, but they cannot be remolded, recycled, or repaired. Vitrimers can be topologically rearranged via an associative exchange mechanism, endowing them with thermoplasticity. Introducing dynamic bonds into crosslinked networks to obtain more sustainable thermosets is currently an interesting research topic. While recent research into vitrimers has indicated many advantages over traditional thermosets, an important shortcoming has been identified: susceptibility to creep at service temperature due to the dynamic bonds present in the network. In addition, designing aero grade epoxy vitrimers (similar to RTM6 resin) still remains a challenge. Herein, low creep aero grade epoxy vitrimer with thermal and mechanical properties similar to those of aero grade epoxy resins and with the ability to be recyclable, repairable, and reprocessable, has been prepared. In this manuscript, we demonstrate that aero grade epoxy vitrimer with reduced creep can be easily designed by the introduction of a certain fraction of permanent crosslinks, without having a negative effect on the stress relaxation of the material. Subsequently, the mechanical and relaxation properties were investigated and compared with those of classical aero grade epoxy resin. A high Tg (175 °C) epoxy vitrimer was obtained which fulfilled all mechanical and thermal specifications of the aero sector. This work provides a simple network design to obtain aero grade epoxy resins with excellent creep resistance at elevated temperatures while being sustainable.
RESUMEN
Epoxy resins are widely used in the composite industry due to their dimensional stability, chemical resistance, and thermo-mechanical properties. However, these thermoset resins have important drawbacks. (i) The vast majority of epoxy matrices are based on non-renewable fossil-derived materials, and (ii) the highly cross-linked molecular architecture hinders their reprocessing, repairing, and recycling. In this paper, those two aspects are addressed by combining novel biobased epoxy monomers derived from renewable resources and dynamic crosslinks. Vanillin (lignin) and phloroglucinol (sugar bioconversion) precursors have been used to develop bi- and tri-functional epoxy monomers, diglycidyl ether of vanillyl alcohol (DGEVA) and phloroglucinol triepoxy (PHTE) respectively. Additionally, reversible covalent bonds have been incorporated in the network by using an aromatic disulfide-based diamine hardener. Four epoxy matrices with different ratios of epoxy monomers (DGEVA/PHTE wt%: 100/0, 60/40, 40/60, and 0/100) were developed and fully characterized in terms of thermal and mechanical properties. We demonstrate that their performances are comparable to those of commonly used fossil fuel-based epoxy thermosets with additional advanced reprocessing functionalities.
RESUMEN
In the present work, sustainable rigid polyurethane foams (RPUF) reinforced with chicken feathers (CF) were prepared and characterized. The bio-based polyol used to formulate the foams was obtained from castor oil. This investigation reports the influence of the chicken feathers fibers as reinforcement of RPUF, on water absorption, thermal, mechanical and morphological properties (field-emission scanning electron microscope-FESEM) and thermal conductivity on water-blown biofoams. It was found that the biofoams improved thermal insulating properties when CF was added. The addition of CF to foams provided lower heat flux density to the biofoams obtaining bio-based materials with better insulation properties. The results obtained in this study proved that the incorporation of CF to RPUF modified the cell structure of the foams affecting their physical and mechanical properties, as well as functional properties such as the heat transmission factor. These biofoams containing up to 45% of bio-based materials have shown the potential to replace fully petroleum-based foams in thermal insulation applications.
RESUMEN
Feathers are made of keratin, a fibrous protein with high content of disulfide-crosslinks and hydrogen-bonds. Feathers have been mainly used as reinforcing fiber in the preparation of biocomposites with a wide variety of polymers, also poly(urea-urethane)s. Surface compatibility between the keratin fiber and the matrix is crucial for having homogenous, high quality composites with superior mechanical properties. Poly(urea-urethane) type polymers are convenient for this purpose due to the presence of polar functionalities capable of forming hydrogen-bonds with keratin. Here, we demonstrate that the interfacial compatibility can be further enhanced by incorporating sulfur moieties in the polymer backbone that lead to new fiber-matrix interactions. We comparatively studied two analogous thermoplastic poly(urea-urethane) elastomers prepared starting from the same isocyanate-functionalized polyurethane prepolymer and two aromatic diamine chain extenders, bis(4-aminophenyl) disulfide (TPUU-SS) and the sulfur-free counterpart bis(4-aminophenyl) methane (TPUU). Then, biocomposites with high feather loadings (40, 50, 60 and 75 wt %) were prepared in a torque rheometer and hot-compressed into flexible sheets. Mechanical characterization showed that TPUU-SS based materials underwent higher improvement in mechanical properties than biocomposites made of the reference TPUU (up to 7.5-fold higher tensile strength compared to neat polymer versus 2.3-fold). Field Emission Scanning Electron Microscope (FESEM) images also provided evidence that fibers were completely embedded in the TPUU-SS matrix. Additionally, density, thermal stability, and water absorption of the biocomposites were thoroughly characterized.
RESUMEN
The aim of this work was to develop new biodegradable polymeric materials with high loadings of chicken feather (CF). In this study, the effect of CF concentration and the type of biodegradable matrix on the physical, mechanical and thermal properties of the biocomposites was investigated. The selected biopolymers were polylactic acid (PLA), polybutyrate adipate terephthalate (PBAT) and a PLA/thermoplastic copolyester blend. The studied biocomposites were manufactured with a torque rheometer having a CF content of 50 and 60 wt %. Due to the low tensile strength of CFs, the resulting materials were penalized in terms of mechanical properties. However, high-loading CF biocomposites resulted in lightweight and thermal-insulating materials when compared with neat bioplastics. Additionally, the adhesion between CFs and the PLA matrix was also investigated and a significant improvement of the wettability of the feathers was obtained with the alkali treatment of the CFs and the addition of a plasticizer like polyethylene glycol (PEG). Considering all the properties, these 100% fully biodegradable biocomposites could be adequate for panel components, flooring or building materials as an alternative to woodâ»plastic composites, contributing to the valorisation of chicken feather waste as a renewable material.
RESUMEN
Thiol-functionalised silicone-oils were crosslinked with silver nanoparticles to give mechanically consistent elastomers with high self-healing power. The materials were broken into small pieces and put together in intimate contact for 24 hours at room temperature, observing a complete macroscopic healing and a quantitative recovery of compression-stress and strain.