RESUMEN
Applying surfactants to reduce the interfacial tension (IFT) on water/oil interfaces is a proven technique. The search for new surfactants and delivery strategies is an ongoing research area with applications in many fields such as drug delivery through nanoemulsions and enhanced oil recovery. Experimentally, the combination of hyperbranched polyglycerol (HPG) with cetyltrimethylammonium bromide (CTAB) substantially reduced the observed IFT of oil/water interface, 0.9 mN/m, while HPG alone was 5.80 mN/m and CTAB alone IFT was 8.08 mN/m. Previous simulations in an aqueous solution showed that HPG is a surfactant carrier. Complementarily, in this work, we performed classical molecular dynamics simulations on combinations of CTAB and HPG with one aliphatic chain to investigate further the interaction of this pair in oil interfaces and propose the mechanism of IFT decrease. Basically, from our results, one can observe that the IFT reduction comes from a combination of effects that have not been observed for other dual systems: (i) Due to the CTAB-HPG strong interaction, a weakening of their specific and isolated interactions with the water and oil phases occurs. (ii) Aggregates enlarge the interfacial area, turning it into a less ordered interface. (iii) The spread of individual molecules charge profiles leads to the much lower interfacial tension observed with the CTAB+HPG systems.
RESUMEN
The influence of processing intumescent bio-based poly(lactic acid) (PLA) composites by injection and fused filament fabrication (FFF) was evaluated. A raw (ANa) and two acidic-activated (AH2 and AH5) montmorillonites were added to the intumescent formulation, composed by lignin and ammonium polyphosphate, in order to evaluate the influence of the strength and the nature (Brønsted or Lewis) of their acidic sites on the fire behavior of the composites. The thermal stability and the volatile thermal degradation products of the composites were assessed. The injected and 3D-printed composites were submitted to cone calorimeter (CC), limit oxygen index (LOI), and UL-94 flammability tests. A similar tendency was observed for the injected and 3D-printed samples. The high density of strong Lewis sites in AH2 showed to be detrimental to the fire-retarding properties. For the CC test, the addition of the intumescent composite reduced the peak of heat released (pHRR) in approximately 49% when compared to neat PLA, while the composites containing ANa and AH5 presented a reduction of at least 54%. However, the addition of AH2 caused a pHRR reduction of around 47%, close to the one of the composite without clay (49%). In the LOI tests, the composites containing ANa and AH5 achieved the best results: 39% and 35%, respectively, for the injected samples, and 35 and 38% for the 3D-printed samples. For the composite containing AH2 the LOI values were 34% and 32% for injected and 3D-printed samples, respectively. Overall, the best performance in the flammability tests was achieved by the composites containing clays with only weak and moderate strength acidic sites (ANa and AH5).
RESUMEN
A raw montmorillonite (Mt) was submitted to different acidic activation times in order to investigate the influence of the strength and the nature (Brønsted and Lewis) of acidic sites on the synergistic action with an intumescent formulation (IF) composed of ammonium polyphosphate (APP) and pentaerythritol (PER) when incorporated into a polypropylene (PP) matrix. The acidity of the Mt samples was quantified by ammonia temperature-programmed desorption (TPD-NH3) and Fourier transform infrared spectroscopy (FTIR) with pyridine adsorption. The mineral clays were also characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD), nitrogen adsorption analysis and particle size distribution. Thermogravimetric analysis (TGA), limit oxygen index (LOI) and UL-94 were performed to evaluate the flame-retardant properties and the thermal stability. The TGA results show that the final residue increased 2 to 3 fold in comparison to the values predicted theoretically. The flammability properties achieved a maximum for the system containing an excess of moderate-strength Brønsted sites relative to the Lewis ones, reaching 38% in the LOI test. This result suggests that the presence of these Brønsted acidic sites is important, as they take part in the esterification reaction between APP and PER which gives rise to the char formation. The FTIR-Pyr adsorption and flammability results indicate that both the nature and strength of the acidic sites influence the flame-retardant properties.
RESUMEN
Vem sendo discutido na classe odontológica o fato de cobrar ou não a primeira consulta ao paciente. Com o objetivo de verificar se a consulta é cobrada, o valor da mesma e se era tomado por base alguma tabela, foram aplicados 50 questinários a professores de odontologia da UFRN, UFS e FOP/UPE, que atendem em consultório particular. Os dados coletados foram analisados estatisticamente, sendo constatado que a grande maioria dos entrevistados cobram a primeira consulta odontológica e que o valor médio da mesma é de R$ 54,00, sendo que a maior parte dos professores utiliza uma tabela própria para a fixação dos honorários profissionais