RESUMEN

INTRODUCTION: Orthodontic relapse occurs after orthodontic treatment and shifting of teeth to unfavorable positions. Bisphosphonates' effects on bone resorption and relapse prevention have been extensively investigated. However, topical administration, which results in local effect, is still a problem. OBJECTIVE: This study aimed to investigate the effect of risedronate with gelatin hydrogel as a carrier to prevent relapse movement by inhibiting osteoclast activity. METHODS: Lower incisors of 75 guinea pigs were moved distally using an orthodontic appliance until ±3 mm length. Gelatin hydrogel was fabricated to obtain a semisolid controlled release of 250 (Bis-CR250) and 500 mmol/L risedronate (Bis-CR500) and then applied intrasulcularly into the mesial subperiosteal area of 50 guinea pigs (25 in each group) every 3 days; the rest were the control (Bis-CR000). After 14 days of stabilization, the apparatus was removed. The distance decrease between incisors and the osteoclast number with TRAP staining at 0, 3, 7, 14, and 21 days were measured. ANOVA was used to determine the differences among the different time and experimental groups. RESULTS: Both treatments showed significantly less relapse movement compared to the control (p < 0.05) at 14 and 21 days. Bis-CR500 more effectively inhibited the relapse movement than Bis-CR250 on day 21, indicating a dose dependency in the inhibition. Both treatments showed less osteoclast numbers than control (p < 0.05). CONCLUSION: Controlled release of bisphosphonate risedronate with a topically administered gelatin hydrogel has shown to be effective in decreasing the tooth relapse movement and osteoclast activity.

RESUMEN

INTRODUCTION: The number of patients who seek orthodontic treatment that may have a history of tooth bleaching is increasing over the time. Bleaching may influence the decrease of the bond strength of orthodontic brackets. OBJECTIVE: To determine and prove the effect of mangosteen peel (MP) extract to reverse the reduced shear bond strength (SBS) of orthodontic brackets after bleaching. METHODS: A total of 150 maxillary first premolar teeth were randomly divided into 6 experimental groups as follow (n=25): negative-control (N: no bleaching), positive-control (P: bleaching + no treatment), and the treatment groups (bleaching + 10% sodium ascorbate (SA), 10% (MP-10), 20% (MP-20) and 40% (MP-40) MP extract gel). After treatment, the brackets were bonded with the resin-modified glass ionomer cement, SBS testing was performed using universal testing machine, and the adhesive remnant index (ARI) was examined using stereoscopic microscope after debonding. The SBS data were analyzed by analysis of variance (Anova) and the Tukey test. For the ARI, the Kruskal-Wallis test was performed. RESULT: There was significant SBS difference (p< 0.001) between various groups. The group without bleaching showed significantly higher SBS (8.19 ± 2.26 MPa) compared to others, while SBS in the group treated with 40% MP gel was significantly higher (7.93 ± 1.92 MPa) than other groups treated with antioxidants. The failure of orthodontic brackets bonded after bleaching and treatment using MP extract occurred at the enamel-adhesive interface. CONCLUSION: The application of MP extract as an antioxidant after bleaching was effective in reversing the reduced shear bond strength of orthodontic brackets after bleaching.

Asunto(s)

RESUMEN

Abstract Introduction: The number of patients who seek orthodontic treatment that may have a history of tooth bleaching is increasing over the time. Bleaching may influence the decrease of the bond strength of orthodontic brackets. Objective: To determine and prove the effect of mangosteen peel (MP) extract to reverse the reduced shear bond strength (SBS) of orthodontic brackets after bleaching. Methods: A total of 150 maxillary first premolar teeth were randomly divided into 6 experimental groups as follow (n=25): negative-control (N: no bleaching), positive-control (P: bleaching + no treatment), and the treatment groups (bleaching + 10% sodium ascorbate (SA), 10% (MP-10), 20% (MP-20) and 40% (MP-40) MP extract gel). After treatment, the brackets were bonded with the resin-modified glass ionomer cement, SBS testing was performed using universal testing machine, and the adhesive remnant index (ARI) was examined using stereoscopic microscope after debonding. The SBS data were analyzed by analysis of variance (Anova) and the Tukey test. For the ARI, the Kruskal-Wallis test was performed. Result: There was significant SBS difference (p< 0.001) between various groups. The group without bleaching showed significantly higher SBS (8.19 ± 2.26 MPa) compared to others, while SBS in the group treated with 40% MP gel was significantly higher (7.93 ± 1.92 MPa) than other groups treated with antioxidants. The failure of orthodontic brackets bonded after bleaching and treatment using MP extract occurred at the enamel-adhesive interface. Conclusion: The application of MP extract as an antioxidant after bleaching was effective in reversing the reduced shear bond strength of orthodontic brackets after bleaching.

Resumo Introdução: o número de pacientes que procuram o tratamento ortodôntico e têm histórico de clareamento dentário tem aumentado. O clareamento pode levar à diminuição da resistência adesiva dos braquetes ortodônticos. Objetivos: comprovar a efetividade do extrato de casca de mangostão (CM) em reverter a diminuição da resistência ao cisalhamento de braquetes ortodônticos colados após o clareamento. Métodos: 150 primeiros pré-molares superiores foram aleatoriamente divididos em seis grupos experimentais (n= 25): controle negativo (grupo N, sem clareamento), controle positivo (grupo P, clareamento + sem tratamento) e os grupos com tratamento (clareamento + ascorbato de sódio a 10% [grupo AS], gel de extrato de CM a 10% [grupo CM-10], a 20% [grupo CM-20] e a 40% [grupo CM-40]). Após o tratamento, os braquetes foram colados com cimento de ionômero de vidro modificado por resina e, depois, fez-se o teste de resistência ao cisalhamento (SBS) em uma máquina universal de ensaios. Após a descolagem dos braquetes, verificou-se o índice de adesivo remanescente (ARI), com o uso de um microscópio estereoscópico. Os dados da SBS foram submetidos a uma análise de variância (ANOVA) e ao teste de Tukey. Para o ARI, foi utilizado o teste de Kruskal-Wallis. Resultados: houve diferença significativa na SBS (p< 0,001) entre os diferentes grupos. O grupo sem clareamento mostrou resistência ao cisalhamento significativamente maior (8,19 ± 2,26 MPa) do que os outros grupos, enquanto a resistência ao cisalhamento do grupo tratado com o gel de extrato de CM a 40% foi significativamente maior (7,93 ± 1,92 MPa) do que nos outros grupos tratados com antioxidantes. A falha na colagem dos braquetes ortodônticos após o clareamento e tratamento com o extrato de CM ocorreu na interface adesivo/esmalte. Conclusão: a aplicação do extrato de CM como agente antioxidante foi efetiva em reverter a diminuição, que ocorre após o clareamento dentário, na resistência ao cisalhamento da colagem de braquetes ortodônticos.

Asunto(s)