RESUMEN
The radioisotope thorium-229 (229Th) is renowned for its extraordinarily low-energy, long-lived nuclear first-excited state. This isomeric state can be excited by vacuum ultraviolet (VUV) lasers and 229Th has been proposed as a reference transition for ultra-precise nuclear clocks. To assess the feasibility and performance of the nuclear clock concept, time-controlled excitation and depopulation of the 229Th isomer are imperative. Here we report the population of the 229Th isomeric state through resonant X-ray pumping and detection of the radiative decay in a VUV transparent 229Th-doped CaF2 crystal. The decay half-life is measured to 447(25) s, with a transition wavelength of 148.18(42) nm and a radiative decay fraction consistent with unity. Furthermore, we report a new "X-ray quenching" effect which allows to de-populate the isomer on demand and effectively reduce the half-life. Such controlled quenching can be used to significantly speed up the interrogation cycle in future nuclear clock schemes.
RESUMEN
We have grown [Formula: see text]Th:CaF[Formula: see text] and [Formula: see text]Th:CaF[Formula: see text] single crystals for investigations on the VUV laser-accessible first nuclear excited state of [Formula: see text]Th, with the aim of building a solid-state nuclear clock. To reach high doping concentrations despite the extreme scarcity (and radioactivity) of [Formula: see text]Th, we have scaled down the crystal volume by a factor 100 compared to established commercial or scientific growth processes. We use the vertical gradient freeze method on 3.2 mm diameter seed single crystals with a 2 mm drilled pocket, filled with a co-precipitated CaF[Formula: see text]:ThF[Formula: see text]:PbF[Formula: see text] powder in order to grow single crystals. Concentrations of [Formula: see text] cm[Formula: see text] have been realized with [Formula: see text]Th with good (> 10%) VUV transmission. However, the intrinsic radioactivity of [Formula: see text]Th drives radio-induced dissociation during growth and radiation damage after solidification. Both lead to a degradation of VUV transmission, currently limiting the [Formula: see text]Th concentration to [Formula: see text] cm[Formula: see text].