At present, due to advanced fatigue calculation models, it is becoming more crucial to find a reliable source for design S-N curves, especially in the case of new 3D-printed materials. Such obtained steel components are becoming very popular and are often used for important parts of dynamically loaded structures. One of the commonly used printing steels is EN 1.2709 tool steel, which has good strength properties and high abrasion resistance, and can be hardened. The research shows, however, that its fatigue strength may differ depending on the printing method, and may be characterized by a wide scatter of the fatigue life. This paper presents selected S-N curves for EN 1.2709 steel after printing with the selective laser melting method. The characteristics are compared, and conclusions are presented regarding the resistance of this material to fatigue loading, especially in the tension-compression state. A combined general mean reference and design fatigue curve is presented, which incorporates our own experimental results as well as those from the literature for the tension-compression loading state. The design curve may be implemented in the finite element method by engineers and scientists in order to calculate the fatigue life.
RESUMEN
This study aimed to analyze the effect of the impact velocity of a Zr 700 flyer plate explosively welded to a Ti Gr. 1/P265GH bimetallic composite on the residual stress formation, structural properties, and tensile strength. The residual stresses were determined by the orbital hole-drilling strain-gauge method in a surface layer of Zr 700 in as-received and as-welded conditions. The analysis of the tensile test results based on a force parallel to interfaces was used to propose a model for predicting the yield force of composite plates. Compressive residual stresses found in the initial state of the Zr 700 plate were transformed to tensile stresses on the surface layer of the welded Zr 700 plate. A higher impact velocity resulted in higher tensile stresses in the Zr 700 surface layer. To increase the resistance of the composite plate to stress-based corrosion cracking, a lower value of impact velocity is recommended in the welding process.