RESUMEN
A silver-containing gel based on polyvinyl alcohol and aryloxycyclotriphosphazene containing ß-carboxyethenylphenoxy and p-formylphenoxy groups has been developed. Phosphazene was synthesized via the Doebner reaction from hexakis[(4-formyl)phenoxy]cyclotriphosphazene and malonic acid and characterized by 1H, 13C, and 31P NMR spectroscopy and MALDI-TOF mass spectrometry. The study of the gel using scanning electron microscopy showed that the gel contains open pores and can absorb wound exudate. The maximum water absorption capacity of the gel was 272%, which was reached after 80 min of testing. The antimicrobial activity of the obtained silver-containing gel was evaluated using the diffusion method. The gel was found to inhibit the growth of the main microorganisms in contact with the skin: the bacteria S. aureus, P. aeruginosa, E. coli, B. subtilis, S. epidermidis, and C. stationis and the fungus C. albicans. The study of the wound-healing effect of the gel in vivo showed a decrease in the wound area of the rabbit hind limb by 91.43% (p < 0.05) on the 10th day of observation and a decrease in the content of C-reactive protein in the rabbit blood serum by 1.3 times (p < 0.05).
RESUMEN
A modifier consisting of the mixture of cyclotriphosphazenes containing 4-allyl-2-methoxyphenoxy and ß-carboxyethenylphenoxy moieties was developed for administration with acrylate dental restorative compositions. The synthesized compounds were characterized by 1H and 13C NMR spectroscopy and MALDI-TOF mass spectrometry. The optimal conditions to combine the modifier with the starting dental mixture consisting of bis-GMA and TGM-3 were revealed by differential scanning calorimetry (DSC) method. Properties of the cured modified compositions were evaluated for the compliance with requirements of ISO 4049:2019. It was found that these compositions possess the increased adhesion to dental tissues and cure depth and the decreased water sorption and water solubility. The values of elastic modules, destructive compressive stress and microhardness were also increasing along with the increased content of the modifier in the composition.