RESUMEN
In regenerative medicine of vascularized tissues, there is a great interest in the use of biomaterials that are able to stimulate angiogenesis, a process necessary for rapid revascularization to allow the transport and exchange of oxygen, nutrients, growth factors and cells that take part in tissue repair and/or regeneration. An increasing number of publications have shown that bioactive glasses stimulate angiogenesis. Because it has been established that boron (B) may play a role in angiogenesis, the aim of this study was to assess the in vivo angiogenic effects of the ionic dissolution products that from a bioactive glass (BG) in the 45S5 system doped with 2 wt% B2O3 (45S5.2B). The pro-angiogenic capacity of 45S5.2B BG was assessed on the vasculature of the embryonic quail chorioallantoic membrane (CAM). Ionic dissolution products from 45S5.2B BG increased angiogenesis. This is quantitatively evidenced by the greater expression of integrin αvß3 and higher vascular density in the embryonic quail CAM. The response observed at 2 and 5 days post-treatment was equivalent to that achieved by applying 10 µg mL-1 of basic fibroblast growth factor. These results show that the ionic dissolution products released from the bioactive glass 45S5.2B stimulate angiogenesis in vivo. The effects observed are attributed to the presence the ionic dissolution products, which contained 160 ± 10 µM borate.
RESUMEN
As it has been established that boron (B) may perform functions in angiogenesis and osteogenesis, the controlled and localized release of B ions from bioactive glasses (BGs) is expected to provide a promising therapeutic alternative for regenerative medicine of vascularized tissues, such as bone. The aim of this study was to assess the in vitro angiogenic effects of the ionic dissolution products (IDPs) from BGs in the SiO2-CaO-Na2O-P2O5 (45S5) system and of those from 45S5 BG doped with 2 wt% B2O3 (45S5.2B). The results show, for the first time, the IDPs from 45S5.2B BG stimulated human umbilical vein endothelial cell (HUVEC) proliferation and migration that were associated with phosphorylation of extracellular signal-related kinase (ERK) 1/2, focal adhesion kinase (FAK) and p38 protein. It was also shown that IDPs from 45S5.2B BG could enhance in vitro HUVEC tubule formation and secretion of interleukin 6 (IL6) and the basic fibroblast growth factor (bFGF). The effects observed are attributed to the presence of B in the IDPs. These findings are relevant to bone tissue engineering and regeneration because the IDPs from 45S5.2B BG may act as inexpensive inorganic angiogenic agents providing a convenient alternative to the application of conventional angiogenic growth factors.
RESUMEN
There is accumulating evidence that strontium (Sr)-containing bioceramics have positive effects on bone tissue repair. The aims of the present study were to evaluate the osteoconductivity of Sr-doped bioactive glass (BG) particles implanted in rat tibia bone marrow, and characterize the neoformed bone tissue by SEM-energy-dispersive X-ray microanalysis. Melt-derived BGs were prepared from a base 45S5 BG. Sr-doped glass (45S5.6Sr) was prepared using 6 wt % SrO as a substitute for the CaO. Histological analysis using undecalcified sections showed that new lamellar bone had formed along the surface of both 45S5 and 45S5.6Sr BG particles within 4 weeks. To evaluate osteoconductivity, affinity indices were calculated. At 30 days after implantation, 45S5 and 45S5.6Sr BGs had almost identical affinity indices (88% +/- 7% and 87% +/- 9%; p > 0.05). Strontium was not detected in the neoformed bone tissue surrounding 45S5.6Sr BG particles. These results indicate that 45S5.6Sr BG particles are osteoconductive when implanted inside the intramedullary canal of rat tibiae, and no alterations in bone mineralization, in terms of Ca/P ratio, were observed in the neoformed bone tissue around 45S5.6Sr BG particles.