RESUMEN
The interest in the development of novel biodegradable composites has increased over last years, and multilayer composites allow the design of materials with functionality and improved properties. In this work, bilayer structures based on a coated zein layer containing quercetin and cellulose nanocrystals (CNC) over an extruded poly(lactic acid) (PLA) layer were developed and characterized. Bilayer composites were successfully obtained and presented a total thickness of approx. 90 µm. The coated zein layer and quercetin gave a yellowish tone to the composites. The incorporation of the zein layer containing CNC decreased the volatile release rate during thermal degradation. Regarding to mechanical properties, bilayer composites presented lower brittleness and greater ductility evidenced by a lower Young's modulus and higher elongation values. Water permeability values of bilayer composites greatly increased with humidity and the zein coated layer containing quercetin increased this effect. Experimental data of quercetin release kinetics from bilayer structures indicated a higher release for an alcoholic food system, and the incorporation of cellulose nanocrystals did not influence the quercetin diffusion process.
RESUMEN
The açaí fruit (Euterpe oleracea Mart.) is well known for its high content of antioxidant compounds, especially anthocyanins, which provide beneficial health properties. The incorporation of this fruit is limited to food products whose processing does not involve the use of high temperatures due to the low thermal stability of these functional components. The objective of this work was the encapsulation of açaí fruit antioxidants into electrosprayed zein, a heat-resistant protein, to improve their bioavailability and thermal resistance. First, the hydroalcoholic açaí extract was selected due to its high polyphenolic content and antioxidant capacities, and, subsequently, it was successfully encapsulated in electrosprayed zein particles. Scanning electron microscopy studies revealed that the resulting particles presented cavities with an average size of 924 nm. Structural characterization by Fourier transform infrared spectroscopy revealed certain chemical interaction between the active compounds and zein. Encapsulation efficiency was approximately 70%. Results demonstrated the effectiveness of the encapsulated extract on protecting polyphenolic content after high-temperature treatments, such as sterilization (121 °C) and baking (180 °C). Bioaccesibility studies also indicated an increase of polyphenols presence after in vitro digestion stages of encapsulated açaí fruit extract in contrast with the unprotected extract.