RESUMEN
Poly(lactic acid) (PLA) was plasticized with maleinized linseed oil (MLO) and further reinforced with sheep wool fibers recovered from the dairy industry. The wool fibers were firstly functionalized with 1 and 2.5 phr of tris(2-methoxyethoxy)(vinyl) (TVS) silane coupling agent and were further used in 1, 5, and 10 phr to reinforce the PLA/MLO matrix. Then, the composite materials were processed by extrusion, followed by injection-molding processes. The mechanical, thermal, microstructural, and surface properties were assessed. While the addition of untreated wool fibers to the plasticized PLA/MLO matrix caused a general decrease in the mechanical properties, the TVS treatment was able to slightly compensate for such mechanical losses. Additionally, a shift in cold crystallization and a decrease in the degree of crystallization were observed due to the fiber silane modification. The microstructural analysis confirmed enhanced interaction between silane-modified fibers and the polymeric matrix. The inclusion of the fiber into the PLA/MLO matrix made the obtained material more hydrophobic, while the yellowish color of the material increased with the fiber content.
RESUMEN
A method to modify polymers is that of introducing fibers in a matrix to produce a fiber-reinforced polymer (FRP). Consequently, the aim of this work was to study the compatibility effect of four coupling agents on wool FRP properties, using poly(lactic acid) plasticized with maleinized linseed oil as polymer matrix. The content of wool assessed was 1 phr. The compatibilizers were (3-(2-aminoethylamino)propyl)-trimethoxysilane, trimethoxy (2-(7-oxabicyclo (4.1.0)hept-3-yl) ethyl) silane, tris(2-methoxyethoxy)(vinyl) silane and titanium (IV) (triethanolaminate)isopropoxide. Initially, wool was modified with coupling agents in an acetone/water (50/50) solution. Mechanical properties were evaluated by tensile and flexural properties, hardness by Shore D measurement and impact resistance by Charpy's energy. Differential scanning calorimetry, dynamic thermo-mechanical analysis, and thermogravimetric analysis were conducted to evaluate the interaction among components and the effect of the coupling agents on the thermal properties of the original material. Color, wettability and scanning electron microscopy were used to describe physical and microstructural properties. Modification of fibers allows achieving improved mechanical properties and changes the thermal properties of the FRPs slightly. Coupling agent treatment helps to formulate PLA-MLO and sheep wool materials and to improve their performance, thereby creating a broader spectrum of applications for PLA maintaining the bio-based character of the material.