RESUMEN
The role of the surface plasmon resonance (SPR) of gold nanorods (Au NRs) on the performance of Y123 dye-sensitized solar cells (DSSC) was investigated. DSSCs were fabricated by incorporating different concentrations (0.6 to 3.0 wt%) of Au NRs into TiO2 photoanodes. With an increase in the concentration of the Au NRs, the light absorption by the Y123 dye loaded photoanodes enhanced linearly, but the charge extraction was susceptible to the concentration of the Au NRs. With optimized concentrations (â¼1.8 wt%) of the Au NRs, the photocurrent of the DSSC enhanced from 12.45 to 15.74 mA cm-2, and the power conversion efficiency (PCE) improved from 5.31 to 8.86%. The DSSC performance was also verified using Au nanoparticles (the PCE was enhanced from 5.31 to 7.72%) for comparison with the Au NR DSSC performance, which demonstrated the advantage of the Au NRs' shape effect with longitudinal SPR due to the modified light interaction. To explain the experimental observations of the plasmonic DSSC, the Au NRs' extinction efficiency and spatial distribution of the near-fields in complete and porous TiO2 media were also estimated using the finite-element method.
RESUMEN
Self-assembled silver-aluminum (Ag-Al) alloy nanoparticles (NPs) embedded in SiO2, Si3N4, and SiON dielectric thin film matrices explored as a hybrid plasmonic structure for silicon solar cells to maximize light confinement. The Ag2Al NPs prepared by ex-vacuo solid-state dewetting, and alloy formation confirmed by X-ray diffraction and photoelectron spectroscopy analysis. Nanoindentation by atomic force microscopy revealed better surface adhesion of alloy NPs on silicon surface than Ag NPs due to the Al presence. The SiON spacer layer/Ag2Al NPs reduced silicon average reflectance from 22.7% to 9.2% due to surface plasmonic and antireflection effects. The SiON capping layer on NPs reduced silicon reflectance from 9.2% to 3.6% in wavelength region 300-1150 nm with preferential forward light scattering due to uniform Coulombic restoring force on NPs' surface. Minimum reflectance and parasitic absorptance from 35 nm SiON/Ag2Al NPs/25 nm SiON structure reflected in plasmonic cell's photocurrent enhancement from 26.27 mA/cm2 (of bare cell) to 34.61 mA/cm2 due to the better photon management. Quantum efficiency analysis also showed photocurrent enhancement of cell in surface plasmon resonance and off-resonance regions of NPs. We also quantified dielectric thin film antireflection and alloy NPs plasmonic effects separately in cell photocurrent enhancement apart from hybrid plasmonic structure role.