RESUMEN
Experimental evidence of tremendous magnetic moment dynamical inversion, from metastable trapping state to the state with essentially the same moment oriented in the opposite direction, appearing during giant flux jump connected to thermomagnetic avalanche process in superconducting YBa2Cu3O7-δ single crystal, is presented. Magnetization inversion takes place in the system, without thermal contact between sample and sample holder, with a tremendous stored energy once the avalanche process is completed in quasi-adiabatic conditions. A model of magnetic moment inversion, caused by the jump between two metastable states of superconductor with the same energy storage, is presented and discussed in terms of the critical state with peculiar evolution of the critical-current spatial distribution. Importantly, knowledge of conditions of the appearance of such a phenomenon is crucial for applications of bulk superconductors as "permanent" magnets, for example, in superconducting levitation devices, etc.
RESUMEN
The effect of Fe ion concentration on the morphological, structural, and optical properties of TiO2 films supported on silica (SiO2) opals has been studied. TiO2:Fe2O3 films were prepared by the sol-gel method in combination with a vertical dip coating procedure; precursor solutions of Ti and Fe were deposited on a monolayer of SiO2 opals previously deposited on a glass substrate by the same procedure. After the dip coating process has been carried out, the samples were thermally treated to obtain the TiO2:Fe2O3/SiO2 composites at the Fe ion concentrations of 1, 3, and 5 wt%. Scanning electron microscopy (SEM) micrographs show the formation of colloidal silica microspheres of about 50 nm diameter autoensembled in a hexagonal close-packed fashion. Although the X-ray diffractograms show no significant effect of Fe ion concentration on the crystal structure of TiO2, the µ-Raman and reflectance spectra do show that the intensity of a phonon vibration mode and the energy bandgap of TiO2 decrease as the Fe(+3) ion concentration increases.
RESUMEN
On the basis of the formalism of the Boltzmann kinetic equation for the distribution function of the conduction electrons, the photonic band structure of binary dielectric-metal superlattice is theoretically studied. Using the constitutive nonlocal relation between the electrical current density and the electric field inside the metallic layer, the dispersion equation for photonic eigenmodes in the periodic stack is analytically expressed in terms of the surface impedances at the interfaces of the metal and dielectric layers. In the case of very thin metallic layers, the optic spectrum for the superlattice exhibits narrow pass bands as a result of the strong contrast between the impedances of the dielectric and the metal. The narrow pass bands are attributed to Fabry-Perot resonances in the relatively-thick dielectric layer. The metal nonlocality is well pronounced in the infrared and, therefore, the nonlocal effect upon the photonic band structure of the superlattice can be strong when the Fabry-Perot resonance bands are in that frequency range. Our results for the photonic spectrum have been compared with those obtained within the local Drude-Lorentz model. Noticeably differences not only in the the magnitude, but also in the sign of the real part of the Bloch wave number in the Fabry-Perot resonance bands, have been found.
RESUMEN
Uniform, spherical-shaped TiO2:Eu nanoparticles with different doping concentrations have been synthesized through controlled hydrolysis of titanium tetrabutoxide under appropriate pH and temperature in the presence of EuCl3·6H2O. Through air annealing at 500°C for 2 h, the amorphous, as-grown nanoparticles could be converted to a pure anatase phase. The morphology, structural, and optical properties of the annealed nanostructures were studied using X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy [EDS], and UV-Visible diffuse reflectance spectroscopy techniques. Optoelectronic behaviors of the nanostructures were studied using micro-Raman and photoluminescence [PL] spectroscopies at room temperature. EDS results confirmed a systematic increase of Eu content in the as-prepared samples with the increase of nominal europium content in the reaction solution. With the increasing dopant concentration, crystallinity and crystallite size of the titania particles decreased gradually. Incorporation of europium in the titania particles induced a structural deformation and a blueshift of their absorption edge. While the room-temperature PL emission of the as-grown samples is dominated by the 5D0 - 7Fj transition of Eu+3 ions, the emission intensity reduced drastically after thermal annealing due to outwards segregation of dopant ions.