RESUMEN

The aim of this study was to evaluate the micro-shear bond strength (µSBS) of one and two steps self-etch adhesive systems after enamel bleaching with photo-activated bleaching systems of different hydrogen peroxide (HP) concentration. Occlusal enamel of forty intact human molars were flattened and assigned into four groups. GI Unbleached, GII, GIII, and GIV were bleached with Pyrenees (3.5% HP), GC TiON (20% HP), and Hi-Lite (35% HP) respectively. Enamel treatment with one and two steps self-etch adhesives (Clearfil S3 Bond- S3, and Clearfil SE Bond-SE) then micro-tubes were fixed on enamel and filled with AP-X composite (n=5). Bond was tested with the universal testing machine. Data were analyzed using two-way ANOVA and Tukey's tests at 5 % level of significance. The µSBS was significantly different between adhesives (F=154.46; p<0.05) and bleaching systems (F=77.33; p<0.05) with significant interaction. Specimens bonded with S3 shows a significantly lower µSBS than those bonded with SE (p<0.05) in all groups. For both adhesives the bleached groups demonstrate lower µSBS than unbleached except specimens bleached with Pyrenees and bonded with SE (p>0.05). A significant difference was observed between groups of the bleaching systems (p<0.05). Different peroxide concentrations photo-activated bleaching systems adversely affect µSBS of one and two steps self-etch adhesives. Low concentration system (Pyrenees) does not influence the bond strength of two steps adhesive.

Asunto(s)

RESUMEN

Abstract The aim of this study was to evaluate the micro-shear bond strength (µSBS) of one and two steps self-etch adhesive systems after enamel bleaching with photo-activated bleaching systems of different hydrogen peroxide (HP) concentration. Occlusal enamel of forty intact human molars were flattened and assigned into four groups. GI Unbleached, GII, GIII, and GIV were bleached with Pyrenees (3.5% HP), GC TiON (20% HP), and Hi-Lite (35% HP) respectively. Enamel treatment with one and two steps self-etch adhesives (Clearfil S3 Bond- S3, and Clearfil SE Bond-SE) then micro-tubes were fixed on enamel and filled with AP-X composite (n=5). Bond was tested with the universal testing machine. Data were analyzed using two-way ANOVA and Tukey's tests at 5 % level of significance. The µSBS was significantly different between adhesives (F=154.46; p<0.05) and bleaching systems (F=77.33; p<0.05) with significant interaction. Specimens bonded with S3 shows a significantly lower μSBS than those bonded with SE (p<0.05) in all groups. For both adhesives the bleached groups demonstrate lower µSBS than unbleached except specimens bleached with Pyrenees and bonded with SE (p>0.05). A significant difference was observed between groups of the bleaching systems (p<0.05). Different peroxide concentrations photo-activated bleaching systems adversely affect μSBS of one and two steps self-etch adhesives. Low concentration system (Pyrenees) does not influence the bond strength of two steps adhesive.

Resumo O objetivo deste estudo foi avaliar a resistência ao cisalhamento (µSBS) de sistemas auto-adesivos de um e dois passos após clareamento do esmalte com sistemas de clareamento foto-ativados de diferentes concentrações de peróxido de hidrogênio (HP). O esmalte oclusal de quarenta molares humanos intactos foi aplainado e atribuído em quatro grupos. GI Unbleached, GII, GIII, e GIV foram branqueados com Pyrenees (3,5% HP), GC TiON (20% HP), e Hi-Lite (35% HP) respectivamente. Tratamento de esmalte com adesivos de um e dois passos auto-adesivos (Clearfil S3 Bond- S3, e Clearfil SE Bond-SE), depois os microtubos foram fixados no esmalte e preenchidos com composto AP-X (n=5). A resistência ao cisalhamento foi testada com a máquina universal de testes. Os dados foram analisados usando os testes de ANOVA e Tukey de duas vias a um nível de 5% de significância. O µSBS foi significativamente diferente entre adesivos (F=154,46; p<0,05) e sistemas de clareadores (F=77,33; p<0,05) com interação significativa. Os espécimes colados com S3 mostram um μSBS significativamente inferior aos colados com SE (p<0,05) em todos os grupos. Para ambos os adesivos, os grupos clareados demonstram µSBS inferiores aos não clareados exceto os espécimes clareados com Pyrenees e colados com SE (p>0,05). Foi observada uma diferença significativa entre os grupos dos sistemas de clareamento (p<0,05). Diferentes concentrações de peróxidos foto-ativados nos sistemas de clareamento afetam negativamente μSBS dos adesivos de uma e duas etapas de auto-colagem. O sistema de baixa concentração (Pyrenees) não influenciou a resistência ao cisalhamento do adesivo de duas etapas.

RESUMEN

This study tested if dentin adhesion is affected by Er:YAG laser. Ninety dentin disks were divided in groups (n = 10): G1, control; G2, Er:YAG laser 150 mJ, 90 degrees contact, 38.8 J/cm(2); G3, Er:YAG laser 70 mJ, 90 degrees contact, 18.1 J/cm(2); G4, Er:YAG laser 150 mJ, 90 degrees non-contact, 1.44 J/cm(2); G5, Er:YAG laser 70 mJ, 90 degrees non-contact, 0.67 J/cm(2); G6, Er:YAG laser 150 mJ, 45 degrees contact, 37.5 J/cm(2); G7, Er:YAG laser 70 mJ, 45 degrees contact, 17.5 J/cm(2); G8, Er:YAG laser 150 mJ, 45 degrees non-contact, 1.55 J/cm(2); and G9, Er:YAG laser 70 mJ, 45 degrees non-contact, 0.72 J/cm(2). Bonding procedures were carried out and the micro-shear-bond strength (MSBS) test was performed. The adhesive surfaces were analyzed under SEM. Two-way ANOVA and multiple comparison tests revealed that MSBS was significantly influenced by the laser irradiation (p < 0.05). Mean values (MPa) of the MSBS test were: G1 (44.97 +/- 6.36), G2 (23.83 +/- 2.46), G3 (30.26 +/- 2.57), G4 (35.29 +/- 3.74), G5 (41.90 +/- 4.95), G6 (27.48 +/- 2.11), G7 (34.61 +/- 2.91), G8 (37.16 +/- 1.96), and G9 (41.74 +/- 1.60). It was concluded that the Er:YAG laser can constitute an alternative tool for dentin treatment before bonding procedures.

Asunto(s)

RESUMEN

OBJECTIVES: To monitor the stiffening rate of demineralized dentin matrix at the early stages after exposure to different neat solvents. METHODS: Dentin beams approximately 0.8x0.7x8.0 mm were obtained from human third molars. After covering their ends with resin composite, the middle exposed length of 4.0mm (gauge-length) was demineralized in 0.5 M EDTA (pH 7.0) for 7 days. The specimens were gripped by a testing machine, pre-loaded to 10 g and cyclically stressed in tension to 5% strain, for 30 repeated cycles (total 20 min) at 0.6 mm/min while immersed in water (control). Then, water was replaced by either 100% acetone, methanol, ethanol, propanol, HEMA or air and the specimens subjected to the same cyclic protocol. The maximum apparent modulus of elasticity (E(Max)) was calculated for every cycle, plotted as a function of time and subjected to regression analysis. Stiffening rate was calculated as changes in E (min). Regression analysis examined the relationship between E and time for each solvent. Data were analyzed by one-way ANOVA and Student-Newman-Keuls test at alpha=0.05. RESULTS: Regression analysis showed that E increased significantly with time in all water-free solvents (R2=0.8-0.99). Stiffening rate was higher for acetone (0.9 MPa/min) and ethanol (0.8 MPa/min), intermediate for air (0.7 MPa/min), methanol (0.6 MPa/min) and propanol (0.5 MPa/min), lower for HEMA (0.2 MPa/min) and practically none for water (0.07 MPa/min) with p<0.05. CONCLUSIONS: The solvent-induced stiffening rate of demineralized dentin matrix is both time and solvent-dependent. The ability of solvents to promptly stiffen the demineralized dentin matrix may be important in maintaining the resin-infiltrated matrix expanded during the solvent evaporation stage of resin bonding.

Asunto(s)