RESUMEN
In this work, epoxy composites filled with flake graphite of various size (less than 10 µm and less than 45 µm) were produced. The aim of the research was to develop a self-lubricating material with favorable tribological properties, i.e., reduced friction coefficient compared to unfilled epoxy resin and limited abrasive wear. The research material was produced using technical epoxy resins based on bisphenol A. The detailed process of composite production was described, and typical technological problems were considered. The addition of graphite led to an increase in dynamic viscosity, which positively limits the phenomenon of sedimentation, but an increase in the filler content also led to an increase in the porosity of the material. A series of tests have shown that the addition of graphite above 5% by weight allows for a reduction in the friction coefficient from 0.6 to 0.4 and significantly reduces the material's tendency to abrasive wear.
RESUMEN
Degradation of polymer composites is a significant problem in many engineering aspects. Due to the interaction of various degradation factors during the exploitation of composites, a synergistic effect of destruction is observed. The article describes the phenomena occurring in glass fiber reinforced polyester laminates under the influence of ultraviolet radiation (UV) in an aquatic environment. The laminates were exposed to UV-A, UV-B and UV-C radiation for 1000 h in free-air and underwater conditions. During the test, the materials were immersed at stable depth of 1 mm and 10 mm, respectively. The three-point bending tests performed on the samples after being exposed to UV showed an increase in the flexural strength of the composites. Simultaneously, degradation of the outer surface layer was observed. The degradation removed the thin resin film from the surface which resulted in a direct exposure of the reinforcing fibers to the environment. The transformations taking place in the deeper layers of the composite increased the mechanical strength due to the additional cross-linking reactions excited by the energy arising from the radiation. Moreover, the formation of polymer structures from free styrene remaining after the technological process and the occurrence of free radical reactions as a result of the cage effect was also observed.
RESUMEN
This work is devoted to evaluating the effectiveness of the recovery of carbon fibers from end-of-life wind turbine blades in the pyrolysis process, and the use of those fibers in the production of flat composite panels. The recovery of carbon fibers from wind turbine blades uses a pyrolysis process at 500-600 °C in a non-oxidizing atmosphere, in such a way that makes it possible to preserve the shape and dimensions of the fibers. Using recycled carbon fibers, flat CFRP sheets with epoxy resin matrix were produced by pressing. Seven different series of samples were tested, which differed in fiber length, fiber orientation, and pressure holding time. The results obtained on the recycled fibers were compared to the original carbon fibers, cut to corresponding lengths. Additionally, one of the series was reinforced with a biaxial fabric. The most favorable pressing parameters are empirically found to be pre-pressing 2 MPa (10 min), and further pressing at a pressure of 7 MPa until the resin completely cross-linked (about 120 min). A number of tests were carried out to demonstrate the usefulness of pyrolytic fibers, including tensile strength of carbon fibers, bending strength, SEM observations, FT-IR, and Raman spectroscopy. The tests carried out on the carbon fibers show that the pyrolysis process used leaves about 2% of the matrix on the surface of the fiber, and the tensile strength of the fibers drops by about 20% compared to the new carbon fibers. The research results show that the use of the recycled carbon fibers in the production of flat composite plates is reliable, and their mechanical properties do not differ significantly from plates made of corresponding original carbon fibers. Composite panels with the pyrolytic fibers (274 MPa) show up to a 35% higher flexural strength than similarly produced panels with the original new carbon fibers (203 MPa), which means that the panels can be used in the production of elements for footbridges, bridges, pipelines, or structural elements of buildings and roofing.
RESUMEN
In this paper, the performance of epoxy/SbSI nanocomposite under tensile stress was investigated. X-ray diffraction studies show the main stress mode has shear nature in the case of elastic deformation, while a combination of shear and tensile stress during plastic deformation caused lattice deformation of SbSI and shift of sulfur atoms along the c axis of the unit cell. Apart from that, the piezoelectric signals were recorded during tensile tests. Epoxy/SbSI nanocomposite responded to the applied tensile stress by generating a piezoelectric current with a relatively high value. The measured piezoelectric peak-to-peak current is relatively high (Ip-p = 1 pA) in comparison to the current flowing through the sample (8.16 pA) under an applied voltage of 100 V. The current level is independent of the deformation speed rate in contradistinction to complex stress states. The signal comes from the whole volume of the sample between electrodes and is generated by shear stress.
Asunto(s)
Resinas Epoxi , Nanocompuestos , Electrodos , Estrés Mecánico , Difracción de Rayos XRESUMEN
In this paper, sedimentation inhibition attempts were examined using colloidal silica in a mathematical and experimental approach. Experimental results were validated by a two-step verification process. It was demonstrated that application of quantitative metallography and hardness measurements in three different regions of samples allows us to describe the sedimentation process using modified Stokes law. Moreover, proper application of Stokes law allows one to determine the optimal colloidal silica amount, considering characteristics of applied filler (alumina or graphite). The results of mathematical calculations have been confirmed experimentally-the experimental results show good agreement with the calculated data.
RESUMEN
In this paper, we investigated the thermodynamics of the resin curing process, when it was a part of composition with graphite powder and cut carbon fibers, to precisely determine the time and temperature of gelation. The material for the research is a set of commercial epoxy resins with a gelation time not exceeding 100 min. The curing process was characterized for the neat resins and for resins with 10% by weight of flake graphite and cut carbon fibers. The results recorded in the analysis of temperature derivative (ATD) method unequivocally showed that the largest first derivative registered during the test is the gel point of the resin. The innovative approach to measuring the gelation time of resins facilitates the measurements while ensuring the stability of the curing process compared to the normative tests that introduce mechanical interaction. In addition, it was found during the research that the introduction of 10% by weight of carbon particles in the form of graphite and cut carbon fibers rather shortens the gelation time and lowers the temperature peak due to the effective absorption and storage of heat from the cross-linking system. The inhibiting (or accelerating) action of fillers is probably dependent on chemical activity of the cross-linking system.
RESUMEN
The article discusses the influence of the post-process on the mechanical properties of elements produced with the use of the mask stereolithography (mSLA) method. Printed samples were subjected to the following post-process steps: Washing and post-curing, at various times. Then, static tensile and static bending tests were carried out, as well as Shore D hardness measurements for the inner and surface part of the sample, as well as profilographometric analysis of the surface. The post-curing time has been found to strongly affect the tensile and bending strength of printouts, and to improve their surface quality. Washing has an ambiguous effect on the strength of the printouts, but, in the end, it was found that extended washing slightly reduces the strength. Washing significantly affects the quality of the printout surface. A washing time that is too short results in a surface that strongly resembles the printing process, with high roughness. Increasing the washing time to 10 min lowers the roughness by one order of magnitude. Post-curing has also been shown to be beneficial for the cured sample with the application of shielding water. This approach results in an improvement in the flexural strength of the printouts. In general, the obtained research results indicate that, for printouts with cross-sectional dimensions of several mm, the optimal washing time is no more than 10 min and the post-curing time is at least 30 min.
RESUMEN
In this paper, we investigated theimpact of glassy carbon (GC) reinforcement oncrystal structure and the mechanical performance of high-density polyethylene (HDPE). We made composite samples by mixing HDPE granules with powder in ethanol followed bymelt mixing in a laboratory extruder. Along with the investigated composite, we also prepared samples with carbon nanotubes (CNT), graphene (GNP) and graphite (Gr) to compare GC impact with already used carbon fillers. To evaluate crystal structure and crystallinity, we used X-ray diffraction (XRD) and differential scanning calorimetry (DSC). We supported the XRD results with a residual stress analysis (RSA) according to the EN15305 standard. Analysis showed that reinforcing with GC leads to significant crystallite size reduction and low residual stress values. We evaluated the mechanical properties of composites with hardness and tensile testing. The addition of glassy carbon results inincreased mechanical strength incomposites with CNT and GNP.
RESUMEN
This paper shows a piezoelectric response from an innovative sensor obtained by casting epoxy-SbSI (antimony sulfoiodide) nanowires nanocomposite to a grid structure printed using a fuse deposition modeling (FDM) method. The grid is shown to be a support structure for the nanocomposite. The applied design approach prospectively enables the formation of sensors with a wide spectrum of shapes and a wide applicability. The voltage signal obtained as a result of the piezoelectric effect reached 1.5V and 0.5V under a maximum static stress of 8.5 MPa and under a maximum dynamic stress of 22.3 kPa, respectively. These values are sufficient for potential application in sensor systems. The effect of a systematic increase in the voltage signal with subsequent cycles was also observed, which similarly allows the use of these sensors in monitoring systems for structures exposed to unfavorable cyclical loads. The obtained results also show that the piezoelectric signal improves with increase in strain rate.
RESUMEN
In this study, the influence of different carbon fillers on the tribological and manufacturing properties of the thermoplastic polyamide PA6 is presented. The following materials were used as carbon additives: glassy carbon (GC), carbon obtained from the pyrolysis of polymer wastes (BC), and graphene oxide (GO). Fillers were introduced into the PA6 matrix by mechanical stirring in alcohol to settle carbon particles onto the granule surface. Samples were made by injection molding from the produced granules. The microstructure, hardness, and melt flow index (MFI) of the prepared materials were determined. Also, the degree of crystallinity of the samples was examined by Differential Scanning Calorimetry (DSC) and X-ray Diffraction (XRD). The melting point (Tm) was examined using DSC, the results from which allowed the correct heat treatment of PA6 to increase the crystallinity of the obtained material to be selected. The dry sliding tribological behavior of the composites was evaluated via pin-on-block tests against cast iron counterparts. The tests were performed at room temperature, with a sliding speed 0.1 m/s, a sliding distance of 250 m, and a normal force of 40 N. The obtained results revealed that the introduction of GO into the PA6 matrix provides favorable wear behavior, such as the formation of debris that acts as rollers that give a decrease in wear and a lower coefficient of friction. The coefficient of friction in samples with graphene oxide was nearly two times lower than with other samples. However, the ease of manufacture of this material was drastically reduced compared to GC or BC fillers. Microstructural investigations of wear tracks revealed poor adhesion between the polymer matrix and micrograins of carbon fillers (GC and BC), and therefore their influence on tribological properties was less compared to graphene oxide.
RESUMEN
Low-density polyethylene (LDPE) composites reinforced with finely powdered waste glass were identified as a potential material for 3D printed structures for use in low-duty frictional applications. A recently published 3D printing model was used to calculate the limits in the filament feed rate and printing speed. Tribological tests (pin-on-disc method) of the printed composites were performed for different print-path directions. Differential scanning calorimetry (DSC) was performed on the samples and the composites showed a higher crystallinity compared with LDPE, which partially explains the higher elastic modulus of the composites determined during static tensile tests. Using a fine glass powder as reinforcement improved the wear resistance of LDPE by 50% due to the formation of a sliding film on the sample's surface. An evident effect of friction direction vs. the printed path direction on wear was found; which was likely related to differences in the removal of friction products from the friction area for different print-path directions. The LDPE composites with fine waste glass particles are promising materials for low-duty frictional applications and should be the subject of further research.