Replacing synthetic fibers with natural ones as reinforcement in polymeric composites is an alternative to contribute to sustainability. Pineapple leaf fibers (PALF) have specific mechanical properties that allow their use as reinforcement. Further, graphene oxide (GO) has aroused interest due to its distinctive properties that allow the improvement of fiber/matrix interfacial adhesion. Thus, this work aimed to evaluate the ballistic performance and energy absorption properties of PALF-reinforced composites, presenting different conditions (i.e., GO-functionalization, and variation of fibers volume fraction and arrangement) through residual velocity and Izod impact tests. ANOVA was used to verify the variability and reliability of the results. SEM was employed to visualize the failure mechanisms. The Izod impact results revealed a significant increase in the absorbed energy with the increment of fiber volume fraction for the unidirectional configuration. The ballistic results indicated that the bidirectional arrangement was responsible for better physical integrity after the projectile impact. Furthermore, bidirectional samples containing 30 vol.% of GO non-functionalized fibers in a GO-reinforced matrix showed the best results, indicating its possible application as a second layer in multilayered armor systems.
RESUMEN
Graphene oxide (GO) functionalized curaua fiber (CF) has been shown to improve the mechanical properties and ballistic performance of epoxy matrix (EM) nanocomposites with 30 vol% fiber. However, the possibility of further improvement in the property and performance of nanocomposites with a greater percentage of GO functionalized CF is still a challenging endeavor. In the present work, a novel epoxy composite reinforced with 40 vol% CF coated with 0.1 wt% GO (40GOCF/EM), was subjected to Izod and ballistic impact tests as well as corresponding fractographic analysis in comparison with a GO-free composite (40CF/EM). One important achievement of this work was to determine the characteristics of the GO by means of FE-SEM and TEM. A zeta potential of -21.46 mV disclosed a relatively low stability of the applied GO, which was attributed to more multilayered structures rather than mono- or few-layer flakes. FE-SEM images revealed GO deposition, with thickness around 30 nm, onto the CF. Izod impact-absorbed energy of 813 J/m for the 40GOCF/EM was not only higher than that of 620 J/m for the 40CF/EM but also higher than other values reported for fiber composites in the literature. The GO-functionalized nanocomposite was more optimized for ballistic application against a 7.62 mm projectile, with a lower depth of penetration (24.80 mm) as compared with the 30 vol% GO-functionalized CF/epoxy nanocomposite previously reported (27.43 mm). Fractographic analysis identified five main events in the ballistic-tested 40GOCF/EM composed of multilayered armor: CF rupture, epoxy matrix rupture, CF/matrix delamination, CF fibril split, and capture of ceramic fragments by the CF. Microcracks were associated with the morphological aspects of the CF surface. A brief cost-effective analysis confirmed that 40GOCF/EM may be one of the most promising materials for personal multilayered ballistic armor.