RESUMEN

In this study, a magnetic metal-organic framework (MMOF) was synthesized and post-modified with poly(propyleneimine) dendrimer to fabricate a novel functional porous nanocomposite for adsorption and recovery of palladium (Pd(II)) from aqueous solution. The morphological and structural characteristics of the prepared material were identified by field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Brunauer-Emmet-Teller (BET) isotherm, and vibrating sample magnetometer (VSM). The results confirmed the successful synthesis and post-modification of MMOF. Semispherical shape particles (20-50 nm) with appropriate magnetic properties and a high specific surface area of 120 m2/g were obtained. An experimental design approach was performed to show the effect of adsorption conditions on Pd(II) uptake efficiency of the dendrimer-modified magnetic adsorbent. The study showed that the Pd(II) uptake on dendrimer-modified MMOF was well described by the Langmuir isotherm model with the highest uptake capacity of 291 mg/g under optimal condition (adsorbent content of 12.5 mg, Pd ion concentration of 80 ppm, pH = 4, and contact time of 40 min). The adsorption kinetics of Pd(II) ions was suggested to be a pseudo-first-order model. The results revealed a faster adsorption rate and higher adsorption capacity (about 43%) for dendrimer-modified MMOF. Finally, the reusability of the provided adsorbent was evaluated. This work provides a valuable strategy for designing and developing efficient magnetic adsorbents based on MOFs for the adsorption and recovery of precious metals.

Asunto(s)

Dendrímeros , Estructuras Metalorgánicas , Nanocompuestos , Contaminantes Químicos del Agua , Adsorción , Cinética , Fenómenos Magnéticos , Paladio , Polipropilenos , Proyectos de Investigación , Espectroscopía Infrarroja por Transformada de Fourier , Contaminantes Químicos del Agua/análisis

RESUMEN

Herein, a magnetic zirconium-based metal-organic framework nanocomposite was synthesized by a simple solvothermal method and used as an adsorbent for the removal of direct and acid dyes from aqueous solution. To enhance its adsorption performance, poly(propyleneimine) dendrimer was used to functionalize the as-synthesized magnetic porous nanocomposite. The dendrimer-functionalized magnetic nanocomposite was characterized by field-emission scanning electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, nitrogen adsorption/desorption isotherms, and vibration sample magnetometer. The obtained results revealed the successful synthesis and functionalization of the magnetic nanocomposite. The adsorbents exhibited good magnetic properties with high saturation magnetization and high specific surface area. The adsorption isotherms and kinetics of anionic dyes were described by the Freundlich and pseudo-second-order models, respectively. It was found that the kinetics of adsorption of both the investigated dyes by the dendrimer-functionalized magnetic composite is considerably faster than the magnetic composite under the same condition. The adsorption capacity of the dendrimer-functionalized magnetic composite for investigated direct and acid dyes was 173.7 and 122.5 mg/g, respectively, which was higher than those of the existing magnetic adsorbents. This work provides new insights into the synthesis and application of hybrid magnetic adsorbents with synergistic properties of nanoporous metal-organic frameworks and dendrimer with a large number of functional groups for the removal of organic dyes.