RESUMEN
OBJECTIVE: To evaluate in vitro the effects of tooth whitening using gel with Amorphous Calcium Phosphate (ACP) on the bond strength of metal brackets. METHODS: Thirty-six bovine incisors were sectioned at the crown-root interface, and the crowns were then placed in PVC cylinders. The specimens were divided into 3 groups (n = 12) according to whitening treatment and type of gel used, as follows: G1 (control) - no whitening; G2 - whitening with gel not containing ACP (Whiteness Perfect - FGM), G3 - whitening with gel containing ACP (Nite White ACP - Discus Dental). Groups G2 and G3 were subjected to 14 cycles of whitening followed by an interval of 15 days before the bonding of metal brackets. Shear bond strength testing was performed on a Kratos universal test machine at a speed of 0.5 mm/min. After the mechanical test, the specimens were assessed to determine the adhesive remnant index (ARI). The results were subjected to ANOVA, Tukey's test and Kruskal-Wallis test (5%). RESULTS: Significant differences were noted between the groups. Control group (G1 - 11.10 MPa) showed a statistically higher shear bond strength than the groups that underwent whitening (G2 - 5.40 Mpa, G3 - 3.73 MPa), which did not differ from each other. There were no significant differences between the groups in terms of ARI. CONCLUSIONS: Tooth whitening reduces the bond strength of metal brackets, whereas the presence of ACP in the whitening gel has no bearing on the results.
Asunto(s)
Fosfatos de Calcio/uso terapéutico , Recubrimiento Dental Adhesivo , Soportes Ortodóncicos , Blanqueadores Dentales , Adhesividad , Análisis de Varianza , Animales , Bovinos , Esmalte Dental , Análisis del Estrés Dental , Geles , Resistencia al Corte , Estadísticas no ParamétricasRESUMEN
OBJECTIVE: To evaluate in vitro the effects of tooth whitening using gel with Amorphous Calcium Phosphate (ACP) on the bond strength of metal brackets. METHODS: Thirty-six bovine incisors were sectioned at the crown-root interface, and the crowns were then placed in PVC cylinders. The specimens were divided into 3 groups (n = 12) according to whitening treatment and type of gel used, as follows: G1 (control) = no whitening; G2 = whitening with gel not containing ACP (Whiteness Perfect - FGM), G3 = whitening with gel containing ACP (Nite White ACP - Discus Dental). Groups G2 and G3 were subjected to 14 cycles of whitening followed by an interval of 15 days before the bonding of metal brackets. Shear bond strength testing was performed on a Kratos universal test machine at a speed of 0.5 mm/min. After the mechanical test, the specimens were assessed to determine the adhesive remnant index (ARI). The results were subjected to ANOVA, Tukey's test and Kruskal-Wallis test (5%). RESULTS: Significant differences were noted between the groups. Control group (G1 = 11.10 MPa) showed a statistically higher shear bond strength than the groups that underwent whitening (G2 = 5.40 Mpa, G3 = 3.73 MPa), which did not differ from each other. There were no significant differences between the groups in terms of ARI. CONCLUSION: Tooth whitening reduces the bond strength of metal brackets, whereas the presence of ACP in the whitening gel has no bearing on the results.
OBJETIVO: avaliar, in vitro, a influência do clareamento dentário com gel contendo fosfato de cálcio amorfo (ACP) na resistência da união adesiva de braquetes metálicos. MÉTODOS: trinta e seis dentes incisivos bovinos foram seccionados no limite coronorradicular e tiveram suas coroas incluídas em cilindros de PVC. Os corpos de prova foram divididos em três grupos (n = 12), de acordo com a realização do tratamento clareador e tipo de gel utilizado, sendo: G1 (controle) - sem clareamento; G2 - clareamento com gel sem ACP (Whiteness Perfect, FGM); G3 - clareamento com gel contendo ACP (Nite White ACP, Discus Dental). Os grupos G2 e G3 foram submetidos a 14 ciclos de clareamento, seguidos de intervalo de espera de 15 dias para a fixação adesiva dos braquetes metálicos. O ensaio mecânico de cisalhamento foi realizado em máquina universal Kratos, com velocidade de 0,5mm/min. Após o teste mecânico, os corpos de prova foram avaliados quanto ao índice de remanescente adesivo (ARI). Os resultados foram submetidos à ANOVA, ao teste de Tukey e ao de Kruskall-Wallis (α = 5%). RESULTADOS: diferenças significativas foram observadas entre os grupos testados. O grupo controle G1 (11,1MPa) mostrou uma resistência ao cisalhamento estatisticamente superior aos grupos submetidos ao clareamento (G2 = 5,40MPa; G3 = 3,73MPa), os quais não diferiram entre si. Não se observou diferença significativa para o ARI entre os grupos estudados. CONCLUSÃO: o clareamento dentário reduz a resistência da união adesiva de braquetes metálicos, enquanto a presença de ACP no gel clareador não influencia os resultados encontrados.