RESUMEN
This study identifies the optimal combination of active and passive thermoplastic materials for producing multi-material programmable 3D structures. These structures can undergo shape changes with varying radii of curvature over time when exposed to hot water. The research focuses on examining the thermal, thermomechanical, and mechanical properties of active (PLA) and passive (PRO-PLA, ABS, and TPU) materials. It also includes the experimental determination of the radius of curvature of the programmed 3D structures. The pairing of active PLA with passive PRO-PLA was found to be the most effective for creating complex programmable 3D structures capable of two-sided transformation. This efficacy is attributed to the adequate apparent shear strength, significant differences in thermomechanical shrinkage between the two materials, identical printing parameters for both materials, and the lowest bending storage modulus of PRO-PLA among the passive materials within the activation temperature range. Multi-material 3D printing has also proven to be a suitable method for producing programmable 3D structures for practical applications such as phone stands, phone cases, door hangers, etc. It facilitates the programming of the active material and ensures the dimensional stability of the passive components of programmable 3D structures during thermal activation.
RESUMEN
The aim of the study was to analyse the colour fastness of 3D printed samples that could be used as decorative or household items. Such items are often fabricated with 3D printing. The colour of filaments affects not only the mechanical properties, but also the appearance and user satisfaction. Samples of biocomposite filaments (PLA and PLA with added wood and hemp fibres) were used. First, the morphological properties of the filaments and 3D printed samples were analysed and then, the colour fastness against different agents was tested (water, oil, detergent, light and elevated temperature). Finally, the dynamic mechanical properties of the filaments and 3D printed samples were determined. The differences in the morphology of the filaments and 3D printed samples were identified with SEM analysis. The most obvious differences were observed in the samples with wood fibres. All printed samples showed good resistance to water and detergents, but poorer resistance to oil. The sample printed with filaments with added wood fibres showed the lowest colour fastness against light and elevated temperatures. Compared to the filaments, the glass transition of the printed samples increased, while their stiffness decreased significantly. The lowest elasticity was observed in the samples with wood fibres. The filaments to which hemp fibres were added showed the reinforcement effect. Without the influence on their elasticity, the printed samples can be safely used between 60 and 65 °C.
RESUMEN
The aim of our research was to investigate and optimise the main 3D printing process parameters that directly or indirectly affect the shape transformation capability and to determine the optimal transformation conditions to achieve predicted extent, and accurate and reproducible transformations of 3D printed, shape-changing two-material structures based on PLA and TPU. The shape-changing structures were printed using the FDM technology. The influence of each printing parameter that affects the final printability of shape-changing structures is presented and studied. After optimising the 3D printing process parameters, the extent, accuracy and reproducibility of the shape transformation performance for four-layer structures were analysed. The shape transformation was performed in hot water at different activation temperatures. Through a careful selection of 3D printing process parameters and transformation conditions, the predicted extent, accuracy and good reproducibility of shape transformation for 3D printed structures were achieved. The accurate deposition of filaments in the layers was achieved by adjusting the printing speed, flow rate and cooling conditions of extruded filaments. The shape transformation capability of 3D printed structures with a defined shape and defined active segment dimensions was influenced by the relaxation of compressive and tensile residual stresses in deposited filaments in the printed layers of the active material and different activation temperatures of the transformation.