RESUMEN

Hybrid nanocomposites combining biopolymer fibers incorporated with nanoparticles (NPs) have received increasing attention due to their remarkable characteristics. Inorganic NPs are typically chosen for their properties, such as magnetism and thermal or electrical conductivity, for example. Meanwhile, the biopolymer fiber component is a backbone, and could act as a support structure for the NPs. This shift towards biopolymers over traditional synthetic polymers is motivated by their sustainability, compatibility with biological systems, non-toxic nature, and natural decomposition. This study employed the solution blow spinning (SBS) method to obtain a nanocomposite comprising poly(vinyl pyrrolidone), PVA, and gelatin biodegradable polymer fibers incorporated with magnetic iron oxide nanoparticles coated with poly(acrylic acid), PAA2k, coded as γ-Fe2O3-NPs-PAA2k. The fiber production process entailed a preliminary investigation to determine suitable solvents, polymer concentrations, and spinning parameters. γ-Fe2O3-NPs were synthesized via chemical co-precipitation as maghemite and coated with PAA2k through the precipitation-redispersion protocol in order to prepare γ-Fe2O3-NPs-PAA2k. Biopolymeric fibers containing coated NPs with sub-micrometer diameters were obtained, with NP concentrations ranging from 1.0 to 1.7% wt. The synthesized NPs underwent characterization via dynamic light scattering, zeta potential analysis, and infrared spectroscopy, while the biopolymer fibers were characterized through scanning electron microscopy, infrared spectroscopy, and thermogravimetric analysis. Overall, this study demonstrates the successful implementation of SBS for producing biopolymeric fibers incorporating iron oxide NPs, where the amalgamation of materials demonstrated superior thermal behavior to the plain polymers. The thorough characterization of the NPs and fibers provided valuable insights into their properties, paving the way for their potential applications in various fields such as biomedical engineering, environmental remediation, and functional materials.

RESUMEN

Tensile perpendicular to grain is an important mechanical property in the design of joints in timber structures. However, according to the standards, this strength can be determined using at least two different methods: uniaxial tensile and three-point static bending. In this context, the present paper aims to investigate the influence of these test methods on the determination of tensile strength perpendicular to grain of wood used in civil construction timber. Three wood species from Brazilian planted forests (Pinus spp., Eucalyptus saligna, and Corymbia citriodora) were used in this investigation. Twelve specimens of each species were used for each test method investigated. Moreover, a statistical analysis was performed to propose an adjustment to the equation of the Code of International Organization for Standardization 13910:2014 for the three-point bending test. Tensile strength values perpendicular to grain obtained from the uniaxial tensile test were significantly higher than those determined by the three-point bending test. It is proposed that the tensile strength perpendicular to grain can be determined more precisely with adoption of coefficient 5.233 in the term [(3.75·Fult)/b·Lh] of the equation specified by the Code of International Organization for Standardization 13910:2014 for the three-point bending test.

RESUMEN

This investigation explores the fabrication of polymer matrix nanocomposites via additive manufacturing (AM), using a UV photopolymerization resin and copper nanoparticles (Cu-NPs) with vat photopolymerization 3D printing technology. The aim in this study is to investigate the mentioned materials in different formulations in terms of inexpensive processing, the property related variability, and targeting multifunctional applications. After the AM process, samples were post-cured with UV light in order to obtain better mechanical properties. The particles and resin were mixed using an ultrasonicator, and the particle contents used were 0.0, 0.5, and 1.0 wt %. The process used in this investigation was simple and inexpensive, as the technologies used are quite accessible, from the 3D printer to the UV curing device. These formulations were characterized with scanning electron microscopy (SEM) to observe the materials' microstructure and tensile tests to quantify stress-strain derived properties. Results showed that, besides the simplicity of the process, the mixing was effective, which was observed in the scanning electron microscope. Additionally, the tensile strength was increased with the UV irradiation exposure, while the strain properties did not change significantly.

RESUMEN

The use of mineral reinforcements in polymer matrix composites has emerged as an alternative for sustainable production, reducing waste and enhancing the physical and mechanical properties of these materials. This study investigated the impact of the melt flow index (MFI) of HDPE and the particle size of two mineral reinforcements, Bahia Beige (BB) and Rio Grande do Norte Limestone (CRN), on the composites. All composites were processed via extrusion, followed by injection, with the addition of 30 wt.% reinforcement. Chemical analyses revealed similar compositions with high CaO content for both minerals, while X-ray diffraction (XRD) identified predominantly calcite, dolomite, and quartz phases. Variations in the MFI, reinforcement type, and particle size showed a minimal influence on composite properties, supported by robust statistical analyses that found no significant differences between groups. Morphological analysis indicated that composites with lower MFI exhibited less porous structures, whereas larger particles of BB and CRN formed clusters, affecting impact resistance, which was attributed to poor interfacial adhesion.

RESUMEN

In the present work, the influence of a corrosive environment and temperature on the corrosion resistance properties of duplex stainless steel S31803 was evaluated. The corrosive process was carried out using solutions of 1.5% HCl (m/m) and 6% FeCl3 (m/m), at temperatures of 25 and 50 °C. The microstructure of UNS S31803 duplex stainless steel is composed of two phases, ferrite and austenite, oriented in the rolling direction, containing a ferrite percentage of 46.2% in the rolling direction and 56.1% in the normal direction. Samples, when subjected to corrosive media and temperature, tend to decrease their mechanical property values. It was observed, in both corrosive media, that with increasing test temperature, there is an increase in the corrosion rate, both uniform and pitting. The sample in HCl solution obtained a uniform corrosion rate of 0.85% at 25 °C and 0.92% at 50 °C and pitting rates of 0.77% and 1.47% at the same temperatures, respectively. When tested in FeCl3 solution, it obtained uniform corrosion of 0.0006% and 0.93% and pitting of 0.53% and 18.5%, at the same temperatures. A reduction in dissolution potentials is also noted, thus characterizing greater corrosion in the samples with increasing temperature.

RESUMEN

The mechanical and ballistic performance of epoxy matrix composites reinforced with 10, 20, and 30 vol.% of babassu fibers was investigated for the first time. The tests included tension, impact, and ballistic testing with 0.22 caliber ammunition. The results showed an improvement in tensile strength, elastic modulus, and elongation with the addition of babassu fiber, and the 30 vol.% composite stood out. Scanning electron microscopy analysis revealed the fracture modes of the composites, highlighting brittle fractures in the epoxy matrix, as well as other mechanisms such as fiber breakage and delamination in the fiber composites. Izod impact tests also showed improvement with increasing babassu fiber content. In ballistic tests, there was an increase in absorbed energy. All composites surpassed plain epoxy by over 3.5 times in ballistic energy absorption, underscoring the potential of babassu fiber in engineering and defense applications.

RESUMEN

With its extensive production and consumption, the coffee industry generates significant amounts of lignocellulosic waste. This waste, primarily comprising coffee biomasses, is a potential source of cellulose. This cellulose can be extracted and utilized as a reinforcing agent in various biocomposites with polymer matrices, thereby creating high-value products. One such biodegradable polymer, Poly(butylene adipate-co-terephthalate) (PBAT), is notable for its properties that are comparable with low-density polyethylene, making it an excellent candidate for packaging applications. However, the wider adoption of PBAT is hindered by its relatively high cost and lower thermomechanical properties compared with conventional, non-biodegradable polymers. By reinforcing PBAT-based biocomposites with cellulose, it is possible to enhance their thermomechanical strength, as well as improve their water vapor and oxygen barrier capabilities, surpassing those of pure PBAT. Consequently, this study aims to provide a comprehensive review of the latest processing techniques for deriving cellulose from the coffee industry's lignocellulosic by-products and other coffee-related agro-industrial wastes. It also focuses on the preparation and characterization of cellulose-reinforced PBAT biocomposites.

RESUMEN

Additive manufacturing has garnered significant attention as a versatile method for fabricating green and complex composite materials. This study delves into the fabrication of polymer composites by employing polylactic acid (PLA) in conjunction with rice husk as a reinforcing filler. The filaments were made by an extruded filament maker and then were used to make tensile and impact samples by another extrusion technology, fused deposition modeling (FDM). The structural and morphological characteristics of the composite materials were analyzed using scanning electron microscopy SEM. Results show that both the filament and samples are very reliable in producing polymer parts with this rice husk solid waste. This research contributes to increasing materials' circularity and potentially creating a local social economy around rice production, where this waste is not much used.

RESUMEN

Bone tissue is one of the most important in the human body. In this study, scaffolds of poly (lactic acid) PLA reinforced with hydroxyapatite (HA) and carbon nanotubes (CNT) were manufactured, evaluating their mechanical and biological properties. HA was synthesized by wet method and characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The scaffolds were produced using additive manufacturing and characterized by optical microscopy, SEM, thermogravimetric analysis (TGA), Raman spectroscopy and biological tests. The SEM results showed that the PLA surface was affected by the incorporation of CNT. TG showed that the incorporation of HA into the polymer matrix compromised the thermal stability of PLA. On the other hand, the incorporation of CNT to the polymer and the impregnation with HA on the surface by thermal effect increased the stability of PLA/CNT scaffolds. Raman spectra indicated that HA impregnation on the surface did not modify the polymer or the ceramic. In the compression tests, PLA and PLA/CNT scaffolds displayed the best compressive strength. In the biological tests, more than 85% of the cells remained viable after 48 h of incubation with all tested scaffolds and groups with CNT in the composition disclosing the best results.

Asunto(s)

Durapatita , Nanotubos de Carbono , Humanos , Durapatita/química , Poliésteres/química , Polímeros/química , Proliferación Celular , Ácido Láctico/química , Fibroblastos , Andamios del Tejido/química , Espectroscopía Infrarroja por Transformada de Fourier

RESUMEN

To complement previous results, an analysis of the chemical and morphological properties of babassu fibers (Attalea speciosa Mart. ex Spreng.) was conducted in order to evaluate their potential as reinforcements in the production of composites with epoxy matrix. The diameter distribution was analyzed in a sample of one hundred fibers, allowing the verification of its variation. The determination of the chemical properties involved experimental analyses of the constituent index and X-ray diffraction. The diffractogram was used to calculate the crystallinity index and the microfibril angle, which are crucial parameters that indicate the consistency of the mechanical properties of babassu fibers and the feasibility of their use in composites. The results revealed that babassu fiber has a chemical composition, with contents of 28.53% lignin, 32.34% hemicellulose, and 37.97% cellulose. In addition, it showed a high crystallinity index of 81.06% and a microfibril angle of 7.67°. These characteristics, together with previous results, indicate that babassu fibers have favorable chemical and morphological properties to be used as reinforcements in composites, highlighting its potential as an important material for applications in technology areas.

RESUMEN

The demand for materials with improved properties and less negative impact on the environment is growing. Artificial stones are examples of these materials produced with up to 90% of particulate material joined by a binder. This article evaluates the physical and mechanical properties of two artificial stones produced with processing steel residue (blast furnace dust waste) and quartz powder. Two binders were used: pure epoxy resin, denoted as ASPB100, or a mixture of 70 wt% epoxy resin with 30 wt% cashew nut shell oil, denoted as ASPB7030. The process took place under vibration, compression (3 MPa/20 min and 90 °C) and vacuum (80 Pa). ASPB100 showed water absorption of 0.07%, while for ASPB7030, it was 0.54%. They were classified as having high mechanical strength associated with bending stress values equal to 32 and 25 MPa, respectively. Stain resistance indicated that both artificial stones had their stains removed with the tested cleaning agents. In this way, the novel artificial stones produced are sustainable alternatives for the application of blast furnace waste and cashew nut shell oil, reducing their negative impacts on the environment.

RESUMEN

Seeking to improve personal armor equipment by providing mobility and resistance to penetration, this research aimed to explore the potential of sustainable materials in order to assess their ability in ballistic applications. Titica vine fibers (TVFs) extracted from aerial roots of Heteropsis flexuosa from the Amazon region were incorporated at 10, 20, 30, and 40 vol% into an epoxy matrix for applications in ballistic multilayered armor systems (MASs) and stand-alone tests for personal protection against high-velocity 7.62 mm ammunition. The back-face signature (BFS) depth measured for composites with 20 and 40 vol% TVFs used as an intermediate layer in MASs was 25.6 and 32.5 mm, respectively, and below the maximum limit of 44 mm set by the international standard. Fracture mechanisms found by scanning electron microscopy (SEM) attested the relevance of increasing the fiber content for applications in MASs. The results of stand-alone tests showed that the control (0 vol%) and samples with 20 vol% TVFs absorbed the highest impact energy (Eabs) (212-176 J), and consequently displayed limit velocity (VL) values (213-194 m/s), when compared with 40 vol% fiber composites. However, the macroscopic evaluation found that, referring to the control samples, the plain epoxy shattered completely. In addition, for 10 and 20 vol% TVFs, the composites were fragmented or exhibited delamination fractures, which compromised their physical integrity. On the other hand, composites with 30 and 40 vol% TVFs, whose Eabs and VL varied between 166-130 J and 189-167 m/s, respectively, showed the best physical stability. The SEM images indicated that for composites with 10 and 20 vol% TVFs, the fracture mode was predominantly brittle due to the greater participation of the epoxy resin and the discrete action of the fibers, while for composites with 30 and 40 vol% TVFs, there was activation of more complex mechanisms such as pullout, shearing, and fiber rupture. These results indicate that the TVF composite has great potential for use in bulletproof vests.

RESUMEN

The development of wind turbines for regions with low wind speeds imposes a challenge to the expansion of the corresponding energy generation capacity. The present work consists of an evaluation of the potential carded jute fiber and jute yarn to be used in the construction of a wind blade for regions of low wind intensity. The fibers used were supplied by Company Textile of Castanhal (Castanhal-Para-Brazil) and used in the study without chemical treatment in the form of single-filament fibers and yarns with a surface twist of 18.5°. The composites were produced through the resin infusion technique and underwent tensile and shear tests using 120-Ohm strain gauges and a blade extensometer to obtain the Young's modulus. In the analysis of the results, the ANOVA test was applied with a 0.05 significance level, followed by Tukey's test. The results showed that long, aligned jute fibers can be a good option for laminated structures applied in composites for small wind turbine blades.

RESUMEN

The main modifications of thermal and colorimetric parameters after thermal aging of DGEBA/TETA system (plain epoxy) and fique-fiber woven fabric-reinforced epoxy composites are described. As a preliminary study, thermal analysis was carried out on epoxy matrix composites reinforced with 15, 30, 40 and 50% fique-fiber woven fabric. After this previous analysis, the 40% composite was chosen to be thermally aged, at 170 °C. Three exposure times were considered, namely, 0, 72, 120 and 240 h. Samples were studied by thermogravimetric analysis (TGA), differential thermal analysis (DTA), differential scanning calorimetry (DSC), thermomechanical analysis (TMA) and colorimetry analysis. Significant color changes were observed after thermal aging combined with oxidation. It was also found that the thermal behavior of the plain epoxy showed greater resistance after thermal exposure. By contrast, the composites were more sensitive to temperature variations as a result of thermal stresses induced between fique fibers and the epoxy matrix.

RESUMEN

Hybrid composites are expanding applications in cutting-edge technology industries, which need materials capable of meeting combined properties in order to guarantee high performance and cost-effectiveness. This original article aimed for the first time to investigate the hybrid laminated composite thermal behavior, made of two types of fibers: synthetic Twaron® fabric and natural curaua non-woven mat, reinforcing epoxy matrix. The composite processing was based on the ballistic helmets methodology from the North American Personal Armor System for Ground Troops, currently used by the Brazilian Army, aiming at reduced costs, total weight, and environmental impact associated with the material without compromising ballistic performance. Thermal properties of plain epoxy, aramid fabric, and curaua mat were evaluated, as well as the other five configurations of hybrid laminated composites. These properties were compared using thermogravimetric analysis (TGA) with its derivative (DTG), differential thermal analysis (DTA), and thermomechanical analysis (TMA). The results showed that the plain epoxy begins thermal degradation at 208 °C while the curaua mat at 231 °C and the aramid fabric at 477 °C. The hybrid laminated composites curves showed two or three inflections in terms of mass loss. The only sample that underwent thermal expansion was the five-aramid and three-curaua layers composite. In the third analyzed temperature interval, related to the glass transition temperature of the composites, there was, in general, an increasing thermal stability behavior.

RESUMEN

The search for unexplored natural materials as an alternative to synthetic components has driven the development of novel polymeric composites reinforced with environmentally-friendly materials. Natural lignocellulosic fibers (NLFs) have been highlighted as potential reinforcement in composite materials for engineering applications. In this work, a less known Amazonian fiber, the ubim fiber (Geonoma baculifera), is investigated as a possible reinforcement in epoxy composites and was, for the first time, thermally characterized by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Additionally, its chemical structure was elucidated by Fourier transform infrared spectroscopy (FTIR). Ballistic tests were also performed against the threat of a 7.62 mm high-speed lead projectile. The results were statistically analyzed by the Weibull statistical analysis method. FTIR analysis showed the functional groups normally found for NLFs highly rich in cellulose, hemicellulose, and lignin. The TGA/DTG results showed the onset of thermal degradation for the composites (325~335 °C), which represents better thermal stability than isolated ubim fiber (259 °C), but slightly lower than that of pure epoxy (352 °C). The DSC results of the composites indicate endothermic peaks between 54 and 56 °C, and for the ubim fibers, at 71 °C. Ballistic tests revealed higher energy absorption in composites with lower fiber content due to the more intense action of the brittle fracture mechanisms of the epoxy resin, which tended to dissipate more energy. These failure mechanisms revealed the presence of river marks, cracks, and broken fibers with a detachment interface. These results may contribute to the production of ubim fiber-reinforced composites in engineering applications, such as ballistic armors.

RESUMEN

This article presents a comprehensive study on the physical, mechanical, thermal, and chemical properties of polypropylene (PP) composites reinforced with hemp fibers (HF) and compatibilized with maleic anhydride (MAPP). The composites were processed using a twin-screw extruder, followed by hot compression at 190 °C. Subsequently, the composites were analyzed using Izod impact and Shore D hardness tests to evaluate their mechanical properties. Thermal properties were investigated through differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), while X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR) were employed to study their chemical properties. Additionally, a statistical analysis was conducted to compare the average results of the impact and hardness tests. XRD analysis revealed that the addition of HF and MAPP led to the disappearance of peaks corresponding to the beta phase in pure PP. Hemp fibers exhibited an impressive crystallinity of 82.10%, surpassing other natural fibers, and had a significant molecular orientation angle (MFA) of 6.06°, making them highly desirable for engineering applications. The crystallite size was observed to be relatively large, at 32.49 nm. FTIR analysis demonstrated strong interactions between the fiber, compatibilizing agent, and polymer matrix. TGA tests showed that the addition of 5 and 10 wt.% MAPP resulted in complete degradation of the composites, similar to pure PP. DSC analyses indicated a reduction in crystallinity (Xc) due to the incorporation of HF and MAPP. Shore D hardness tests revealed an increase in hardness with the addition of 5 wt.% MAPP, while a steep decline in this property was observed with 10 wt.% MAPP. In terms of impact resistance, fractions of 3 and 5 wt.% MAPP in the composites exhibited improved performance compared to the pure polymer. Analysis of variance (ANOVA) was employed to ensure the statistical reliability of the mechanical test results. This comprehensive study sheds light on the diverse properties of PP composites reinforced with hemp fibers and compatibilized with MAPP, emphasizing their potential as sustainable materials for engineering applications. The results contribute to the understanding of the structural and functional aspects of these composites, guiding future research and developments in the field.

RESUMEN

The search for alternative materials to replace ordinary Portland cement has been the object of work that enhances the investigation of the use of pozzolanic materials and the reduction of the carbon footprint with supplementary cementitious materials. However, not all materials are available to meet the large-scale demand for cement replacement. A relevant exception is the calcined clay, a material found worldwide that, when subjected to appropriate heat treatment, presents pozzolanic reactivity and can be used as a supplementary material to cement. This review presents, through a systematic search, methods for measuring the pozzolanic reactivity of calcined clays, namely, direct, indirect, qualitative, quantitative, chemical and physical methods such as electrical conductivity (Lùxan), the force activity index, the modified Chapelle, R3, Frattini test, thermal analysis, X-ray diffraction and X-ray fluorescence spectrometry. The most usual methods to assess the pozzolanic reactivity of calcined clays were exposed and analyzed. It should be pointed out that there is greater use of the Frattini and modified Chapelle methods as well as the analysis of the mechanical strength behavior of the material in cementitious matrices. X-ray diffraction and thermal analysis were exposed as the most used correlation methods but it was also concluded that different tests are needed to generate accurate results.

RESUMEN

Natural lignocellulosic fibers (NLFs) have been used as a reinforcement for polymer matrix composites in the past couple of decades. Their biodegradability, renewability, and abundance make them appealing for sustainable materials. However, synthetic fibers surpass NLFs in mechanical and thermal properties. Combining these fibers as a hybrid reinforcement in polymeric materials shows promise for multifunctional materials and structures. Functionalizing these composites with graphene-based materials could lead to superior properties. This research optimized the tensile and impact resistance of a jute/aramid/HDPE hybrid nanocomposite by the addition of graphene nanoplatelets (GNP). The hybrid structure with 10 jute/10 aramid layers and 0.10 wt.% GNP exhibited a 2433% increase in mechanical toughness, a 591% increase in tensile strength, and a 462% reduction in ductility compared to neat jute/HDPE composites. A SEM analysis revealed the influence of GNP nano-functionalization on the failure mechanisms of these hybrid nanocomposites.

RESUMEN

Natural lignocellulosic fibers (NLFs) have in recent decades appeared as sustainable reinforcement alternatives to replace synthetic fibers in polymer composite material applications. In this work, for the first time, the periquiteira (Cochlospermum orinocense), a lesser known NLF from the Amazon region, was analyzed for its density and, by X-ray diffraction (XRD), to calculate the crystallinity index as well as the microfibrillar angle (MFA), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), scanning electron analysis (SEM) and tensile strength. The apparent density found for the periquiteira fiber was 0.43 g/cm3, one of the NLF's lowest. XRD analysis indicated a crystallinity index of 70.49% and MFA of 7.32°. The TGA disclosed thermal stability up to 250 °C. The FTIR analysis indicated the presence of functional groups characteristic of NLFs. The SEM morphological analysis revealed that the periquiteira fiber presents fine bundles of fibrils and a rough surface throughout its entire length. The average strength value of the periquiteira fiber was found as 178 MPa. These preliminary results indicate that the periquiteira fiber has the potential to be used as a reinforcing agent in polymeric matrices and can generate a lightweight composite with excellent mechanical properties that can be used in various industrial sectors.