RESUMEN
ABSTRACT Objective: This clinical study was conducted in order to evaluate force decay over time of latex and non-latex orthodontic intraoral elastics. Methods: Patients (n = 15) were evaluated using latex and non-latex elastics in the periods of : 0, 1, 3, 12 and 24 hours. The rubber bands were transferred to the testing machine (EMIC DL-500 MF), and force values were recorded after stretching the elastic to a length of 25mm. Paired t test was applied and analysis of variance (ANOVA) was used to evaluate the variation of force generated. LSD (Fisher's least significant difference) post-hoc test was thus employed. Results: As regards the initial forces (zero time), the values of force for non-latex elastic were slightly higher than for the latex elastic. In the subsequent times, the forces generated by the latex elastic showed higher values. Regarding the material degradation, at the end of 24 hours the highest percentage was observed for non-latex elastic. Conclusions: The latex elastics had a more stable behavior during the studied period, compared with non-latex.
RESUMO Objetivo: o objetivo deste estudo clínico foi avaliar e comparar o comportamento dos elásticos de látex e não látex quanto à perda de força ao longo do tempo. Método: os pacientes (n = 15) foram avaliados usando ambos os tipos de material (látex e não látex) em cada tempo: 0, 1, 3, 12 e 24 horas. Os elásticos foram transferidos para a máquina de ensaios mecânicos (EMIC DL-500 MF) e os valores de força foram registrados após a distensão dos elásticos a uma distância de 25 mm. Foi aplicado o teste t pareado, e a análise de variância (ANOVA) foi realizada para verificar a variação das forças geradas em todos os tempos estudados. Em seguida, o teste post-hoc LSD (Fisher's least significant difference) foi aplicado. Resultados: quanto às forças iniciais (tempo zero), os valores de força dos elásticos não látex foram ligeiramente maiores do que dos elásticos de látex. Nos tempos subsequentes, as forças geradas pelos elásticos de látex apresentaram valores superiores às geradas pelos elásticos não látex. Em relação à degradação do material, ao fim do período de 24 horas, o maior percentual foi observado pelos elásticos não látex. Conclusões: os elásticos de látex apresentaram comportamento mais estável durante o período de estudo, em comparação aos não látex.
Asunto(s)
Humanos , Adulto , Adulto Joven , Aparatos Ortodóncicos , Goma/química , Materiales Dentales/química , Látex/química , Elastómeros de Silicona/química , Estrés Mecánico , Resistencia a la Tracción , Ensayo de Materiales , Análisis de Varianza , Diseño de Aparato Ortodóncico , Análisis del Estrés Dental/métodos , Elasticidad , Fenómenos MecánicosRESUMEN
OBJECTIVE: This clinical study was conducted in order to evaluate force decay over time of latex and non-latex orthodontic intraoral elastics. METHODS: Patients (n = 15) were evaluated using latex and non-latex elastics in the periods of : 0, 1, 3, 12 and 24 hours. The rubber bands were transferred to the testing machine (EMIC DL-500 MF), and force values were recorded after stretching the elastic to a length of 25mm. Paired t test was applied and analysis of variance (ANOVA) was used to evaluate the variation of force generated. LSD (Fisher's least significant difference) post-hoc test was thus employed. RESULTS: As regards the initial forces (zero time), the values of force for non-latex elastic were slightly higher than for the latex elastic. In the subsequent times, the forces generated by the latex elastic showed higher values. Regarding the material degradation, at the end of 24 hours the highest percentage was observed for non-latex elastic. CONCLUSIONS: The latex elastics had a more stable behavior during the studied period, compared with non-latex.
Asunto(s)
Materiales Dentales/química , Látex/química , Aparatos Ortodóncicos , Goma/química , Adulto , Análisis de Varianza , Análisis del Estrés Dental/métodos , Elasticidad , Humanos , Ensayo de Materiales , Fenómenos Mecánicos , Diseño de Aparato Ortodóncico , Elastómeros de Silicona/química , Estrés Mecánico , Resistencia a la Tracción , Adulto JovenRESUMEN
Aim: This study was conducted in order to evaluate and compare the behavior of latex and non-latex elastics, as the loss of strength over time in vitro. Methods: The study evaluated 15 of each elastic material for the pre-selected times: 0, 1, 3, 12 and 24 hours. The rubber bands were transferred to the testing machine (EMIC DL-500 MF). The force values were recorded after stretching the elastic to a length of 25mm. Independent t-test was applied. Analysis of variance (ANOVA) was used to check the variation of the forces generated between those determined times. To identify between which times the difference was present, Tukey post-hoc test was accomplished. Results: As regards the initial forces (zero time), the values of force for non-latex elastic were slightly higher than the latex elastic. In subsequent times, the forces generated by the latex elastic showed higher values. Regarding the material degradation, at the end of 24 hours the highest percentage was observed for non-latex elastic. Conclusion: The latex elastic had a more stable behavior during the studied period compared with non-latex. Thus, it is suggested that the non-latex elastics should be changed more frequently and that larger initial forces must be applied than the látex elastics
Asunto(s)
Elastómeros de Silicona , Resistencia a la Tracción , Elastómeros , LátexRESUMEN
São objetivos deste trabalho avaliar clínica e laboratorialmente a intensidade das forças liberadas por elastômeros em cadeia pré-estirados. A intensidade e o percentual de degradação das forças elásticas liberadas por duas marcas de elastômeros em cadeia (3M - 3MU e American Orthodontics - AO) foram avaliadas em solução de saliva artificial e no meio bucal. As forças liberadas durante a realização do experimento foram quantificadas através de uma máquina de ensaios de tração (EMIC). Todos os grupos apresentaram forças menores geradas pelos elastômeros em três semanas, quando comparadas com as respectivas forças iniciais. Houve uma grande variação das médias apresentadas em relação aos períodos de tempo intermediários avaliados para os dois meios e para as duas marcas testadas. No final de um período de 3 semanas, os valores médios das forças geradas pelos elastômeros da marca AO foram mais elevados do que os gerados por elastômeros da marca 3MU. Após o período de 3 semanas ambas as marcas de elastômeros geraram forças suficientes para produzir o movimento dentário.
The objective of this study was to evaluate clinically and in the laboratory the intensity of forces delivered by prestretched elastomeric chains. The intensity and percentage of force decay of two commercial brands of elastomeric chains, 3M Unitek (3MU) and American Orthodontics (AO), were evaluated in artificial saliva and in the oral environment. The forces generated during the experiment were quantified by means of a tensile testing machine (EMIC). All groups showed a reduction in the forces generated by the elastomers within a 3-week period compared with their respective initial (baseline) forces. There was a wide variation in the means achieved in those time periods in which the two environments and the two brands were assessed. At the end of a 3-week period, the mean values of the forces generated by AO elastomers were higher than those generated by 3MU elastomers. After the 3-week period both brands of elastomers still generated enough force to produce dental movement.
Asunto(s)
Elastómeros , Ortodoncia , Resistencia a la TracciónRESUMEN
A idade do paciente é um importante dado tanto para estudos demográficos como para o uso clínico no diagnóstico, prognóstico e plano de tratamento. Porém, nem sempre a idade cronológica coincide com outros indicadores de maturação. O objetivo deste estudo foi avaliar o grau de correlação entre as idades cronológica, esquelética e dentária em pacientes submetidos ao tratamento ortodôntico na clínica de especialização em Ortodontia da Faculdade de Odontologia da Universidade Veiga de Almeida. A amostra foi constituída por 31 meninas e 24 meninos com idades de 7 a 17 anos. A idade cronológica foi obtida a partir da leitura das fichas clínicas e calculada através da data da realização dos exames radiográficos utilizados. Através de radiografias panorâmicas, foi calculada a idade dentária utilizando o método de maturação dental de Demirjian (1973). A idade esquelética foi obtida através da inspeção de radiografias de mão e punho e comparação com o Atlas de Greulich (1959). Os resultados revelaram que para a amostra total (meninos e meninas), a maior correlação encontrada foi entre a idade cronológica e esquelética (r = 0.878), e a menor entre a idade esquelética e dentária (r = 0.737). As meninas apresentaram maior correlação entre as três idades quando comparadas aos meninos. A maior correlação tanto para os meninos quanto para as meninas foi novamente entre a idade cronológica e esquelética (meninas r = 0.895 e meninos r = 0.859), e a menor entre a idade esquelética e dentária (meninas r = 0.859 e meninos r = 0.676...
The age of the patient is an important data for demographic studies, clinical diagnosis, prognosis, and treatment plane. However, the chronological age does not always correspond to the other maturation indicators. The aim of this study was to evaluate the grade of correlation among chronological, dental, and skeletal ages in patients from the orthodontic clinic at Veiga de Almeida University. The sample consisted of 31 girls and 24 boys, age between 7 and 17 years old. Chronological age was obtained by reading clinical marks and calculated according to the date when the radiographs were done. The dental age was obtained through panoramic radiographs using the Demirjian4 (1973) method of dental maturity. The skeletal age was achieved through inspection of hand-wrist radiographs and compared to Greulichs9 (1959) atlas. Results showed that for the hole sample (boys and girls) the strongest correlation was between chronological and skeletal ages (r = 0.878) and the weakest between skeletal and dental ages (r = 0.737). When compared to the boys, the girls have demonstrated more correlation for all the three ages. Again, the biggest correlation also for boys and girls was between chronological and skeletal ages (girls r = 0.895 and boys r = 0.859) and the smallest correlation was between skeletal and dental ages (girls r = 0.859 and boys r = 0.676)...
Asunto(s)
Humanos , Masculino , Femenino , Niño , Adolescente , Adulto Joven , Determinación de la Edad por el Esqueleto , Determinación de la Edad por los Dientes , Ortodoncia , Radiografía PanorámicaRESUMEN
Introdução / Embora se saiba que algumas alterações hormonais podem afetar o tratamento ortodôntico, existe uma escassez de dados publicados sobre a relação entre essas alterações do sistema endócrino e os possíveis problemas durante o tratamento ortodôntico. Quase todos os estudos foram experimentais, realizados em ratos; os estudos em humanos foram raros, com preponderância de relatos de casos e avaliação de um único hormônio. / Objetivo / A presente revisão busca sintetizar, para o ortodontista clínico, a evidência disponível sobre os principais aspectos que devem ser observados para o tratamento de pacientes portadores de alterações endócrinas, sob o ponto de vista ortodôntico, quanto aos aspectos de crescimento craniofacial, erupção e movimentação dentária, os quais requerem cuidados especiais e que podem apresentar possíveis limitações para o tratamento ortodôntico. / Métodos / Por meio de busca nas bases de dados Medline, PubMed, Cochrane, Embase, Lilacs e BVS, foram selecionados os artigos mais relevantes que avaliaram pacientes com as características acima descritas. / Resultados / Os hormônios somatotrófico, insulina, paratormônio e esteroides sexuais podem induzir alterações indesejadas no crescimento craniofacial, metabolismo ósseo e no aumento de predisposição a problemas periodontais, o que requer adequação do plano de tratamento pelo ortodontista. Há pouca evidência sobre o uso dos hormônios tiroxina, relaxina, vitamina D e calcitonina para evitar reabsorção radicular e aumentar a velocidade de movimentação dentária. / Conclusão / Mais estudos com seres humanos, de alto nível de evidência, são necessários para aprofundar o conhecimento sobre a influência dos hormônios na Ortodontia, para reduzir o risco de efeitos indesejados e aumentar a previsibilidade dos resultados a serem obtidos.
Asunto(s)
Hormonas/efectos adversos , Ortodoncia , Cráneo/crecimiento & desarrollo , Técnicas de Movimiento Dental , Erupción DentalRESUMEN
Este artigo objetivou avaliar a prevalência do cisto ósseo traumático (COT) por meio da coincidência entre o diagnóstico do COT e o paciente que se apresenta para tratamento ortodôntico. A amostra constou de 12.805 pacientes oriundos de clínicas privadas, cursos de graduação e pós-graduação recrutados no período de 1990 e 2009. Inicialmente, cada profissional foi calibrado com radiografias panorâmicas que não fizeram parte da pesquisa, sobre as características e o diagnóstico de COT. O método consistiu na aplicação de um questionário objetivo, respondido por ortodontistas, com o objetivo de avaliar a prevalência de cisto ósseo traumático no contingente total de pacientes de cada profissional. O questionário de avaliação interrogou cada profissional sobre o número total de pacientes, bem como a quantidade de pacientes com diagnóstico de COT, após a criteriosa avaliação dos exames radiográficos panorâmicos. Evidenciou-se uma prevalência de 0,02% de cisto ósseo traumático na população estudada. A prevalência de COT foi muito baixa (1 em cada 4268 pacientes ortodônticos examinados), entretanto, por ser uma lesão assintomática, é de fundamental importância a realização de exames imaginológicos a partir dos 10 anos de idade para o seu diagnóstico.
His article aimed to assess the prevalence of traumatic bone cyst (TBC) in patients undergoing orthodontic treatment based on the evaluation of panoramic x-rays. The sample was composed of 12.805 patients from private practices, graduation and post-graduation programs recruited between 1990 and 2009. At first, each professional was calibrated with panoramic radiographs that were not part of the research on the characteristics and diagnosis of TBC. The method consisted on a objective questionnaire answered by orthodontists with the aim of evaluating the prevalence of traumatic cyst bone on the patients from each professional. The evaluation questionnaire asked each professional about the total number of patients as well as the number of patients diagnosed with TBC, after careful evaluation of panoramic radiographs. A prevalence of 0.02% of traumatic bone cyst (TBC) was found in the investigated population. The prevalence of TBC was very low (1 out of 4268 orthodontic patients examined). However, since TBC is an asymptomatic lesion it is of paramount importance to establish its diagnosis by having imaging examinations performed starting at age 10.
Asunto(s)
Humanos , Quistes Óseos , MandíbulaRESUMEN
O objetivo deste trabalho foi comparar a força adesiva na recolagem de bráquetes novos e reutilizados, quando os mesmos procedimentos da colagem inicial são realizados. Foram utilizados 20 incisivos bovinos. Na face vestibular de cada dente foi colado bráquete metálico (Morelli, Sorocaba, Brasil), seguindo o mesmo protocolo de colagem. Para a primeira descolagem foi utilizada força de cisalhamento através da máquina de ensaios mecânicos (Emic dl 500 mf célula drd 23, São José dos Pinhais, Paraná - Brasil). Para a segunda colagem (recolagem), a amostra foi dividida em grupo 1 e grupo 2 (1R e 2R). Em ambos os grupos foram realizados os mesmos procedimentos da colagem inicial, sendo que no grupo 2R foram usados bráquetes reutilizados por microjateamento. Nos dois grupos (1 e 2), a descolagem foi feita empregando-se a mesma máquina de ensaios mecânicos, pelo mesmo operador, e foram anotadas as cargas de rupturas. Foi aplicada à amostra a análise de variância (Anova) que calculou as médias, desvios-padrão e mostrou haver diferença entre os grupos, sendo realizado então, o teste de múltipla comparação de Tukey. Os resultados mostraram que a recolagem com bráquetes metálicos pode ser considerada uma boa alternativa para o tratamento ortodôntico.
The aim of this study was to compare the shear Bond strength when rebonding with new and reconditioned brackets, using the same procedures as at initial bonding. Twenty bovine incisors were used. Metallic brackets (Morelli, Sorocaba, Brasil) were bonded on the vestibular surface of the tooth, following the same bonding protocol. First debonding was done by universal test machine (EMIC DL 500 MF CÉLULA DRD 23, São José dos Pinhais, Paraná Brazil). For the second bonding (rebonding), the sample was divided in groups (1R and 2R). On both groups the same bonding procedures were performed, as at initial bonding, and brackets reconditioned with microetching were used on group 2R. Second debonding was done using the same test machine, by the same operator and results were recorded. Descriptive statistics, including the mean, standard deviation, and minimum and maximum values of the shear Bond strength were calculated using analysis of variance (ANOVA) and indicated a significant difference into groups, so Tukeys multiple pairwise comparisons were performed. The results showed that rebondedmetal brackets are a good alternative for the orthodontic treatment.
Asunto(s)
Animales , Bovinos , Recubrimiento Dental Adhesivo , Desconsolidación Dental , Soportes Ortodóncicos , OrtodonciaRESUMEN
A intervenção cirúrgica nos casos de discrepância esquelética severa do tipo classe II em pacientes sem crescimento é fundamental para obtenção de um resultado estético, funcional e psicológico satisfatórios. A cirurgia proporcionará aos pacientes não somente uma oclusão favorável e estável, como uma mudança significativa em seu perfil. Estes indivíduos são levados de uma situação de reclusão social para uma melhora na satisfação com sua aparência e com isso uma melhora no seu relacionamento com a sociedade. No caso clínico apresentado, além de um adequado resultado funcional, houve um ganho importante no que se refere à estética facial, sendo este impossível sem o auxílio da cirurgia de avanço mandibular, proporcionando harmonia entre o terço inferior da face com o restante do perfil. O plano de tratamento deve ser exposto ao paciente e deve proporcionar um correto esclarecimento sobre o tratamento orto-cirúrgico, com ênfase nos riscos e benefícios deste tipo de tratamento.
Surgical intervention of severe skeletal class II discrepancy of patients without growth is essential to obtain an aesthetic, functional and psychological satisfactory results, giving these patients, not only a favorable and stable occlusion, as a significant change in their profile. Patients are moved from a situation of social isolation to an improvement in satisfaction with their appearance with an improvement in their relationship with society. In the case presented, the patient had an important gain in regard to function as facial aesthetics, which was impossible without the aid of surgery for mandibular advancement, providing harmony between the lower third of the face with the rest of the profile. The treatment plan should be proposed to the patient providing a proper explanation about the treatment ortho-surgery, with emphasis on the risks and benefits of such treatment.
Asunto(s)
Femenino , Adolescente , Avance Mandibular , Cirugía Bucal , OrtodonciaRESUMEN
The purpose of this study was to compare, in vitro, the friction generated by elastomeric ligature with polymer coating to conventional elastomeric ligature. Three calipers of stainless steel wire were tested: 0.020, 0.019 x 0.025 and 0.019 x 0.026 . Two acrylic plates were manufactured. An upper central incisor bracket was fixed to one of them and a canal (or groove) where orthodontic wires were fixed was made on the other. The acrylic plates were adapted and adjusted to a traction test machine so that the wire would fit into the bracket slot without any angulation. Ten ligatures of each kind were tested for each wire. The wires were pulled and slid into the bracket for a distance of 5mm at a constant rate of 5mm/min. The obtained data was compared by Student´s T test with the significance value of p<0.05 and revealed the existence of great differences between the forces generated for each wire caliper. The conventional ligatures without polymer coating generated significantly higher forces than the ligatures with coating. The polymer-coated ligatures generated lower friction than the conventional ligature in all calipers evaluated. That suggests that this type of ligature should be the best choice for sliding mechanism
O objetivo deste estudo foi comparar, in vitro, o atrito gerado por ligaduras elásticas com cobertura polimérica com ligaduras convencionais. Três calibres de fio de aço inoxidável foram testados: 0.020, 0.019 x 0.025 and 0.019 x 0.026 . Foram confeccionadas duas placas de acrílico, onde em uma placa foi colado um bráquete de incisivo central superior e na outra placa foi feita uma canaleta onde os fios ortodônticos foram fixados. As placas de acrílico foram adaptadas e reguladas em uma máquina de ensaio de tração de maneira que o fio se encaixasse no bráquete sem nenhuma angulação. Para cada fio foram testadas 10 ligaduras de cada tipo. Os fios foram tracionados, deslizando pelo slot do bráquete a uma distância de 5mm com uma velocidade constante de 5mm/min. Os resultados obtidos foram comparados pelo teste t de Student com significância de p<0.05, e revelaram a existência de diferenças significativas entre as forças geradas para cada calibre de fio. As ligaduras convencionais sem cobertura polimérica geraram forças significativamente maiores que as ligaduras com cobertura polimérica. As ligaduras com cobertura polimérica geraram menor atrito que as ligaduras convencionais em todos os calibres de fio avaliados, sugerindo que estas ligaduras devem ser o material de escolha nas mecânicas de deslizamento.
Asunto(s)
Elastómeros , Fricción , OrtodonciaRESUMEN
OBJECTIVES: To describe the microscopic pulpal reactions resulting from orthodontically induced tooth movement associated with low-level laser therapy (LLLT) in rats. MATERIALS AND METHODS: Forty-five young male Wistar rats were randomly assigned to three groups. In group I (n = 20), the maxillary right first molars were submitted to orthodontic movement with placement of a coil spring. In group II (n = 20), the teeth were submitted to orthodontic movement plus LLLT at 4 seconds per point (buccal, palatal, and mesial) with a GaAlAs diode laser source (830 nm, 100 mW, 18 J/cm(2)). Group III (n = 5) served as a control (no orthodontic movement or LLLT). Groups I and II were divided into four subgroups according to the time elapsed between the start of tooth movement and sacrifice (12 hours, 24 hours, 3 days, and 7 days). RESULTS: Up until the 3-day period, the specimens in group I presented a thicker odontoblastic layer, no cell-free zone of Weil, pulp core with differentiated mesenchymal and defense cells, and a high concentration of blood vessels. In group II, at the 12- and 24-hour time points, the odontoblastic layer was disorganized and the cell-free zone of Weil was absent, presenting undifferentiated cells, intensive vascularization with congested capillaries, and scarce defense cells in the cell-rich zone. In groups I and II, pulpal responses to the stimuli were more intense in the area underneath the region of application of the force or force/laser. CONCLUSIONS: The orthodontic-induced tooth movement and LLLT association showed reversible hyperemia as a tissue response to the stimulus. LLLT leads to a faster repair of the pulpal tissue due to orthodontic movement.
Asunto(s)
Pulpa Dental/patología , Terapia por Luz de Baja Intensidad , Técnicas de Movimiento Dental , Animales , Capilares/patología , Núcleo Celular/patología , Cromatina/patología , Citoplasma/patología , Pulpa Dental/irrigación sanguínea , Pulpa Dental/efectos de la radiación , Eritrocitos/patología , Fibroblastos/patología , Hiperemia/patología , Láseres de Semiconductores , Masculino , Mesodermo/patología , Diente Molar/patología , Diente Molar/efectos de la radiación , Odontoblastos/patología , Alambres para Ortodoncia , Distribución Aleatoria , Ratas , Ratas Wistar , Factores de Tiempo , Técnicas de Movimiento Dental/instrumentaciónRESUMEN
A impacção dentária representa um desafio ao cirurgião-dentista, especialmente quando essa envolve dentes anteriores, devido à grande preocupação estética por parte dos pacientes. Os dentes podem se encontrar impactados por uma série de fatores etiológicos, incluindo a falta de espaço na arcada dentária; a presença de elementos supranumerários, cistos ou tumores; o posicionamento ectópico do germe dentário, entre outros; o que pode levar a uma má-oclusão dentária. Este artigo descreve o tracionamento ortodôntico-cirúrgico de um incisivo central superior impactado em um indivíduo do sexo masculino de 11 anos de idade. A sequência do tratamento, desde a abertura de espaço na arcada dentária superior à exposição cirúrgica da coroa e ao tracionamento do elemento impactado mostrou a importância do correto diagnóstico e planejamento e sobretudo de uma abordagem multidisciplinar, o que levou a um resultado bastante satisfatório, com excelente resposta à mecânica utilizada.
Dental impaction represents a challenge to the general dentist, especially when it involves anterior teeth, due to the great esthetic concern of the patients. Teeth may be impacted due to númerous etiological factors, including lack of space in the dental arch, the presence of supranumerary teeth and ectopic positioning of the dental germ, which can lead to malocclusion. This article describes the surgical-orthodontic traction of an impacted maxillary central incisor in a male patient aged 11 years. The sequence of treatment, since the opening of space in the upper dental arch to the surgical exposure of the crown and the traction of the impacted teeth showed the importance of correct diagnosis and planning and of a multidisciplinary approach, which led to a very satisfactory result with excellent response to the mechanics.
Asunto(s)
Humanos , Masculino , Adolescente , Diente/anatomía & histología , Ortodoncia , Diente Impactado , Estética DentalRESUMEN
INTRODUCTION: Children with congenital heart disease commonly experience delayed growth. Studies comparing growth and development of these children generally found that they have decreased height and weight, but with no information on craniofacial growth. The aim of this study was to evaluate the craniofacial characteristics of patients with heart disease. METHODS: We used lateral head cephalograms of 131 patients, aged 8 to 12, attending the Department of Pediatrics of the Hospital of the State University of Rio de Janeiro in Brazil on a routine basis. The study group comprised 50 boys and 38 girls with congenital heart disease. The control group included 20 boys and 23 girls with no heart disease. The skeletal, dental, growth, esthetic, and vertical patterns were analyzed with several cephalometric measurements. The chi-square test was applied to verify a possible association between sex and heart disease, and the Student t test was used to verify differences between the groups of patients with and without heart disease. RESULTS: Heart disease is not sex-related (chi-square = 0.267). But some measurements had sex differences in the groups with and without heart diseases. The Student t test showed significant differences between the groups in the SNA angle measurement in male patients (P = 0.032), and in ANB angle (P = 0.002) and the relationship of the lower lip to the Steiner line (P = 0.034) in the girls. CONCLUSIONS: Skeletal patterns were characterized by maxillary protrusion in the boys with heart disease and by increased ANB angles in the girls without heart disease. The esthetic pattern showed a more pronounced lower lip in the girls without heart disease. However, from a clinical point of view, these were slight and irrelevant alterations. The results suggest that patients suffering from heart disease have similar craniofacial characteristics to those without this condition.
Asunto(s)
Huesos Faciales/crecimiento & desarrollo , Cardiopatías Congénitas/fisiopatología , Desarrollo Maxilofacial/fisiología , Cráneo/crecimiento & desarrollo , Cefalometría , Niño , Estética Dental , Cara , Huesos Faciales/patología , Femenino , Humanos , Incisivo/patología , Labio/patología , Masculino , Mandíbula/patología , Maxilar/patología , Hueso Nasal/patología , Odontogénesis/fisiología , Silla Turca/patología , Factores Sexuales , Cráneo/patología , Diente/patología , Dimensión VerticalRESUMEN
PURPOSE: To compare the shear bond strength of stainless steel brackets bonded with two orthodontic adhesive systems, Transbond XT (3M Unitek) and Orthobond (Morelli Dental Products). MATERIALS AND METHODS: Forty bovine teeth were randomly divided in two groups of 20 each: group 1 (control): Transbond XT primer + Transbond XT Adhesive paste (3M Unitek); group 2: Orthoprimer (Morelli Dental Products) + Orthobond. In each group all teeth were etched with 37% phosphoric acid, and all products were used according to manufacturers instructions. After 30 min, a universal testing machine was used to apply an occlusal shear force directly to the enamel/bracket interface at a speed of 0.5 mm/min. The groups were compared using Student's t-test. RESULTS: Mean results and standard deviations for the groups were: group 1= 11.22 Mpa (1.68), group 2= 4.88 Mpa (1.18). A significant difference was observed in the bond strengths of the two groups evaluated (p < 0.0001). CONCLUSION: Under the conditions of this study, Orthobond system presented lower shear bond strength when compared to Transbond XT.
Asunto(s)
Recubrimiento Dental Adhesivo , Soportes Ortodóncicos , Cementos de Resina/química , Grabado Ácido Dental , Animales , Bovinos , Resinas Compuestas/química , Luces de Curación Dental , Esmalte Dental/ultraestructura , Análisis del Estrés Dental/instrumentación , Ensayo de Materiales , Ácidos Fosfóricos/química , Distribución Aleatoria , Resistencia al Corte , Acero Inoxidable/química , Estrés Mecánico , Factores de TiempoRESUMEN
O presente trabalho tem como objetivo apresentar o relato de um caso clínico de paciente portador de mordida cruzada anterior com transpasse vertical excessivo e três incisivos superiores envolvidos. Para correção foi utilizado o arco palatino com mola. O resultado clínico mostrou que este dispositivo é eficaz no tratamento da mordida cruzada anterior dentária e indicado em casos onde mais de um incisivo superior está envolvido.
Asunto(s)
Humanos , Masculino , Niño , Incisivo/anomalías , Maloclusión/terapia , Aparatos OrtodóncicosRESUMEN
O objetivo deste estudo foi avaliar a influência de duas concentrações diferentes de pH salivar (4,9 e 7,2) na força gerada por ligaduras elásticas modulares, da cor cinza, de duas marcas comerciais diferentes (TP Orthodontics e Morelli). Essas foram estiradas em estiletes de aço inoxidável com diâmetro aproximado ao de braquete de incisivo central superior, imersas em solução de saliva artificial de pH 4,9 e 7,2 e mantidas à temperatura ambiente. Tiveram suas forças medidas nos períodos de zero hora, 24 horas, 7, 14, 21 e 28 dias em uma máquina de ensaios de tração. Os resultados foram gerados por um computador conectado à máquina de tração e foram submetidos a testes estatísticos (t-Student) com p<0,05. O valor encontrado para a marca TP Orthodontics na comparação entre as concentrações de pH (4,9 x 7,2) foi p=0,589. Já na comparação entre as marcas (TP Orthodontics x Morelli), tanto no pH 4,9 quanto no 7,2, os valores encontrados foram de p <0,001. Concluiu-se que o pH salivar não influencia de forma significativa a força gerada por ligaduras elásticas, enquanto a marca comercial mostrou diferença significativa, com menor degradação de força para a marca TP Orthodontics.
Asunto(s)
Concentración de Iones de Hidrógeno , Elastómeros , SalivaRESUMEN
INTRODUCTION: The aim of this study was to evaluate the resistance to deformation or fracture of esthetic brackets produced by archwire torsion. METHODS: Six types of maxillary right central incisor brackets were analyzed: traditional ceramic brackets (cer); ceramic brackets reinforced with a stainless steel slot (cer/ss); ceramic brackets reinforced with a gold slot (cer/gold); traditional polycarbonate brackets (poly); polycarbonate brackets reinforced with a stainless steel slot (poly/ss); and polycarbonate brackets reinforced with ceramic fillers and a stainless steel slot (poly/cer/ss). Stainless steel wire segments were used, and the testing instrument (Emic DL 10000, São José do Rio Preto, PR, Brazil) was moved at a rate of 1 inch per minute to generate the wire torsion. RESULTS: The brackets showed deformation or fracture resistance values (gf x mm) in decreasing order as follows: cer/ss (3528.1 +/- 516.6), cer/gold (2858.7 +/- 611.6), cer (2424.0 +/- 352.1), poly/cer/ss (2279.5 +/- 174.5), poly/ss (2142.0 +/- 275.7), and poly (1463.6 +/- 193.3). The cer/ss ceramic brackets showed the greatest statistically significant (P <0.01) values of resistance to fracture, and the poly brackets had the lowest statistically significant (P <0.01) values of resistance to deformation. The cer brackets showed no significant differences (P >0.01) from the cer/gold, the poly/cer/ss, and the poly/ss brackets. CONCLUSIONS: This suggested that the stainless steel slot might enhance resistance to deformation or fracture, although gold slots and ceramic fillers are ineffective for reinforcing esthetic brackets.
Asunto(s)
Estética Dental , Soportes Ortodóncicos , Alambres para Ortodoncia , Cerámica/química , Aleaciones Dentales/química , Materiales Dentales/química , Falla de Equipo , Aleaciones de Oro/química , Humanos , Ensayo de Materiales , Diseño de Aparato Ortodóncico , Cemento de Policarboxilato/química , Acero Inoxidable/química , Estrés Mecánico , Propiedades de Superficie , Torsión MecánicaRESUMEN
Nos casos ortodônticos em que há a presença de dentes inclusos, os primeiros exames complementares solicitados geralmente são as radiografias panorâmicas e periapicais para avaliação da condição do dente incluso e da relação deste elemento com os dentes e estruturas adjacentes. Porém, estes exames são bidimensionais e muitas vezes fornecem informações limitadas a respeito da real posição do dente incluso e da condição em que este se encontra. Muitas vezes, estes podem apresentar dilacerações e reabsorções imperceptíveis nos exames tradicionais. A tomografia volumétrica computadorizada permite a visualização das estruturas anatômicas em três dimensões, fornecendo muito mais detalhes e informações que serão muito úteis para o ortodontista no diagnóstico e plano de tratamento, e também para o cirurgião, que poderá determinar a melhor abordagem cirúrgica, removendo menor quantidade de osso. Esse trabalho teve como objetivo,ilustrar com caso clínico, a importância da tomografia volumétrica computadorizada no diagnóstico e planejamento do tratamento ortodôntico de dentes inclusos, ressaltando como as condutas clínicas podem ser diferentes quando se avalia o mesmo paciente com exames bi ou tridimensionais.
In orthodontic cases in which there is the presence of impacted teeth, the first complementary exams required are usually panoramic and periapical radiographs to assess the condition of the impacted tooth and the relationship of this element with the adjacent teeth and structures. However, these exams are bidimensional and they normally supply limited information about the real position of the impacted tooth and its physical condition. These could frequently present dilacerations and resorptions that are imperceptible in traditional exams. The volumetric computed tomography allows the anatomic structures to be visualized in three dimensions, providing more details and information, which are very useful to the orthodontist in diagnosing and planning treatment, as well as to the surgeon, who may determine the best surgical approach, removing a smaller quantity of bone. The aim of this study was to use a clinical case to illustrate the importance of the volumetric computed tomography in diagnosing and planning orthodontic treatment of impacted teeth, emphasizing how the clinical procedures could differ when the same patient is assessed by means of bi or tridimensional exams.
Asunto(s)
Humanos , Masculino , Niño , Tomografía Computarizada de Haz Cónico , Diente no Erupcionado/diagnóstico , Ortodoncia , Planificación de Atención al PacienteRESUMEN
OBJETIVO: avaliar ligaduras elásticas da marca Morelli, dos tipos modular e bengala, nas cores cinza e cristal para determinação do percentual de degradação das forças geradas pelas mesmas. METODOLOGIA: as ligaduras elásticas foram estiradas em estiletes de aço inoxidável com diâmetro de 4mm, imersas em solução de saliva artificial a 37ºC, sendo a intensidade das forças liberadas medidas nos tempos de zero hora, 24 horas, 1 semana, 2 semanas, 3 semanas e 4 semanas, em máquina de ensaios de tração. RESULTADOS E CONCLUSÕES: as ligaduras do tipo bengala liberaram, em média e no período de 4 semanas, maior intensidade de força que as do tipo modular. O percentual de degradação das forças liberadas por todas as ligaduras aumentou de forma acentuada entre zero e 24 horas e de forma gradativa após este período, com exceção do 28º dia quando, provavelmente, houve perda das propriedades elásticas das ligaduras. Não foi observado um comportamento constante das ligaduras bengala e modular em relação às cores cinza e cristal.
PURPOSE: to evaluate gray and clear module and cane-loaded elastomeric ligatures of the brand Morelli to determine the percentage of decay of the forces they deliver. METHODS: the elastomeric ligatures were stretched over 4mm diameter stainless steel dowels and placed in synthetic saliva bath at 37ºC. The intensity of the forces delivered were taken at start, after 24 hours, one week, two weeks, three weeks and four weeks at a tensile test machine. RESULTS AND CONCLUSIONS: the cane-loaded ligatures delivered, in a period of 4 weeks, in average, greater force intensity than the modules. The percentage of force decay of all ligatures increased rapidly between zero and 24 hours and gradually after that period, except for the 28th day, when probably there was a loss of elastic properties of the ligatures. The researchers did not note any constant behavior in the cane-loaded and module ligatures in relation to the colors: gray and clear.
Asunto(s)
Ligadura/efectos adversos , Ligadura , Ciencia de los Materiales , Ensayo de MaterialesRESUMEN
Foi avaliada a intensidade das forças liberadas por ligaduras elásticas de cinco cores quando imersas em solução de saliva artificial. As amostras foram testadas por meio de uma máquina de ensaios de tração, nos períodos de tempo inicial, 1 dia, 7, 14, 21 e 28 dias de imersão em saliva artificial. Encontrou-se uma diminuição acentuada e estatisticamente significante nas forças liberadas para as primeiras 24 horas (P<0,0001), sendo que entre os demais períodos (7, 14, 21, 28 dias) ocorreu uma queda gradativa não significante destes valores. Entretanto, não houve diferença significante para as magnitudes de forças liberadas pelas ligaduras elásticas modulares em relação às diferentes cores analisadas