RESUMEN
In this work, we report a heterojunction formed by a PbS/CdS bilayer using the chemical bath deposition (CBD) technique because it is a relatively simple, fast, and low-cost technique; is permitted to obtain high-quality thin films (TFs); and also covers large areas. Some characterizations have been carried out to confirm the identity of the involved bilayer. For the cadmium sulfide (CdS) film, optical properties such as absorption, transmission, reflection, extinction coefficient, and refractive index were measured. Moreover, the bandgap was calculated, and morphology was obtained by scanning electron microscopy (SEM). Also, X-ray diffraction (XRD) and high-resolution transmission electron microscopy (TEM) were performed for the synthesis of CdS films. On the other hand, for the synthesis of lead sulfide (PbS) films, we performed TEM, energy-dispersive spectroscopy, and XRD. A surface morphological SEM image of the PbS film synthesized was also taken. The multiheterojunction PbS/CdS bilayer was characterized by the current-voltage (I-V) curve, and the behavior of the bilayer was evaluated under the conditions of darkness and controlled fixed lighting, detecting a very slight photosensitivity of the complete diodic device through those measurements. The calculated bandgap for the CdS TF was E g = 2.55 eV, while after a chosen thermal annealing, the bandgap decreased to 2.38 eV. On the other hand, the PbS film presented a cubic structure.
RESUMEN
This work describes a controlled and low-cost synthesis method to obtain Pb/Pb3O4 nanocomposites using synthetic zeolite 4A. The nanostructures obtained have a core-shell configuration with 5-25 nm diameters. High-resolution transmission electron microscopy (HRTEM), BF, high-angle annular dark-field annular scanning transmission electron microscopy (HAADF-STEM), energy-dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), and ultraviolet-visible (UV-vis) characterization techniques were used. Crystallographic planes (111), (200), and (220) for the core and planes (110) and (211) for the shell, corresponding to FCC and tetragonal structures for Pb and Pb3O4, respectively, were determined using HRTEM. The HAADF-STEM images allowed the analysis of intensity contrast images proportional to the number of atoms. XPS spectral analysis showed a 4.8 eV difference in binding energy between Pb 4f7/2 and Pb 4f5/2 for lead and lead oxide. EDS elemental mapping, XPS, and UV-vis spectroscopy analyses revealed the simultaneous presence of lead and lead oxide in the same structure. The band gap obtained for the shell was determined to be 4.50 eV. Consequently, Pb/Pb3O4 nanocomposites show a higher response to high-energy photons, making them suitable for UV photocatalysis applications.