RESUMEN
A new and simple method of synthesizing fluorinated carbon at the gram scale is presented by reacting a fluorinated alcohol with sodium at elevated temperatures in a sealed Teflon reactor. The resulting carbon nanoparticles are around 100 nm in diameter, and display a hollow shell morphology, with a significant amount of fluorine doped into the carbon. The nanoparticles disperse easily in ethanol, and are thermally stable up to 400 °C and 450 °C under air and nitrogen, respectively. The nanoparticle dispersion was printed onto various substrates (paper, cloth, silicon), inducing superhydrophobicity.
RESUMEN
Fuel cells offer an alternative to burning fossil fuels, but use platinum as a catalyst which is expensive and scarce. Cheap, alternative catalysts could enable fuel cells to become serious contenders in the green energy sector. One promising class of catalyst for electrochemical oxygen reduction is iron-containing, nanostructured, nitrogen-doped carbon. The catalytic activity of such N-doped carbons has improved vastly over the years bringing industrial applications ever closer. Stoichiometric carbon nitride powder has only been observed in recent years. It has nitrogen content up to 57% and as such is an extremely interesting material to work with. The electrochemical activity of carbon nitride has already been explored, confirming that iron is not a necessary ingredient for 4-electron oxygen reduction. Here, we synthesize carbon nitride on a carbon nanotube support and subject it to high temperature treatment in an effort to increase the surface area and conductivity. The results lend insight into the mechanism of oxygen reduction and show the potential for carbon nanotube-supported carbon nitride to be used as a catalyst to replace platinum in fuel cells.