RESUMEN
A simple method of synthesis of TiO2 nanotubes (TiNT) loaded with hydroxyapatite (HAP) is described. Such nanotubes find wide applications in various fields, including biomedicine, solar cells, and drug delivery, due to their bioactivity and potential for osseointegration. The Cp-Ti substrate was anodized at a constant voltage of 40 V, with the subsequent heat treatment at 450 °C. The resulting TiNT had a diameter of 100.3 ± 2.8 nm and a length of 3.5 ± 0.04 µm. The best result of the growth rate of HAP in Hanks' balanced salt solution (Hanks' BSS) was obtained in calcium glycerophosphate (CG = 0.1 g/L) when precipitates formed on the bottom and walls of the nanotubes. Structural properties, surface wettability, corrosion resistance, and growth rate of HAP as an indicator of the bioactivity of the coating have been studied. X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), potentiodynamic polarization test (PPC), electrochemical impedance spectroscopy (EIS), and contact angle (CA) measurements were used to characterize HAP-loaded nanotubes (HAP-TiNT). The CA, also serving as an indirect indicator of bioactivity, was 30.4 ± 1.1° for the TiNT not containing HAP. The contact angle value for HAP-TiNT produced in 0.1 g/L CG was 18.2 ± 1.2°, and for HAP-TiNT exposed to Hanks' BSS for 7 days, the CA was 7.2 ± 0.5°. The corrosion studies and measurement of HAP growth rates after a 7-day exposure to Hanks' BSS confirmed the result that TiNT processed in 0.1 g/L of CG exhibited the most significant capacity for HAP formation compared to the other tested samples.
RESUMEN
Titanium-zirconium dioxide nanostructures loaded by hydroxyapatite were produced on the surface of Ti65Zr alloy. The alloy was treated by anodization with the subsequent immersion in calcium glycerophosphate (CG) solutions. The resulting surfaces present TiO2-ZrO2 nanotubular (TiZr-NT) structures enriched with hydroxyapatite (HAP). The nanotube texture is expected to enhance the surface's corrosion resistance and promote integration with bone tissue in dental implants. The TiZr-NT structure had a diameter of 73 ± 2.2 nm and a length of 10.1 ± 0.5 µm. The most favorable result for the growth of HAP in Hanks' balanced salt solution (Hanks' BSS) was obtained at a CG concentration of 0.5 g/L. Samples soaked in CG at a concentration of 0.5 g/L demonstrated in a decrease of the contact angles to 25.2°; after 3 days of exposure to Hanks' BSS, the contact angles further reduced to 18.5°. The corrosion studies also showed that the TiZr-NT structure soaked in the CG = 0.5 g/L solution exhibited the best corrosion stability.
RESUMEN
Hydroxyapatite (HA) is a bioactive material that is widely used for improving the osseointegration of titanium dental implants. Titanium can be coated with HA by various methods, such as chemical vapor deposition (CVD), thermal spray, or plasma spray. HA coatings can also be grown on titanium surfaces by hydrothermal, chemical, and electrochemical methods. Plasma electrolytic oxidation (PEO), or microarc oxidation (MAO), is an electrochemical method that enables the production of a thick porous oxide layer on the surface of a titanium implant. If the electrolyte in which PEO is performed contains calcium and phosphate ions, the oxide layer produced may contain hydroxyapatite. The HA content can then be increased by subsequent hydrothermal treatment. The HA thus produced on titanium surfaces has attractive properties, such as a high porosity, a controllable thickness, and a considerable density, which favor its use in dental and bone surgery. This review summarizes the state of the art and possible further development of PEO for the production of HA on Ti implants.