RESUMEN
In this study, we demonstrate the fabrication of a novel 2D transition metal dichalcogenide, VTe2, into a saturable absorber (SA) by using the liquid phase exfoliation method. Furthermore, the first-principles calculations were conducted to elucidate the electronic band structures and absorption spectrum. The nonlinear optical absorption properties of VTe2 at 1.0, 2.0, and 3.0 µm were measured using open-aperture Z-scan and P-scan methods, which showed saturation intensities and modulation depths of 95.57 GW/cm2 and 9.24%, 3.11 GW/cm2 and 7.26%, and 15.8 MW/cm2 and 17.1%, respectively. Furthermore, in the realm of practical implementation, the achievement of stable passively Q-switched (PQS) lasers employing SA composed of few-layered VTe2 nanosheets has manifested itself with broadband operating wavelengths from 1.0 to â¼3.0 µm. Specifically, PQS laser operations from near-infrared to mid-infrared with pulse durations of 195 and 563 ns for 1.0 and 2.0 µm solid-state lasers, respectively, and 749 ns for an Er3+-doped fluoride fiber laser at 3.0 µm were obtained. Our experimental results demonstrate that VTe2 is a potential broadband SA device for achieving PQS lasers. To the best of our knowledge, this is the first demonstration of using VTe2 as an SA in PQS lasers in the near- and mid-infrared regions, which highlights the potential of VTe2 for future research and applications in optoelectronic devices.
RESUMEN
In this work, we successfully fabricated a transmissive saturable absorber (SA) with Ti2CTx MXene using the spin-coating method. By inserting the Ti2CTx saturable absorber into the diode-pumped solid-state (DPSS) Nd:YAG laser, a stable passively Q-switched operation was obtained near 1.06 µm. At a pump power of 4.5 W, we obtained the shortest pulse duration of 163 ns with a repetition rate of 260 kHz. The corresponding single pulse energy and peak pulse power were 3.638 µJ and 22.3 W, respectively. The slope efficiency and the optical conversion efficiency of the laser were 21% and 25.5%, respectively. To the best of our knowledge, this is the first time that Ti2CTx was used in the passively Q-switched solid-state lasers. This work demonstrates that Ti2CTx can be a promising saturable absorber for solid-state laser pulse generation.