We have developed a new nanofilter using a carbon nanotube-silver composite material that is capable of efficiently removing waterborne viruses and bacteria. The nanofilter was subjected to plasma surface treatment to enhance its flow rate, which was improved by approximately 62%. Nanoscale pores were obtained by fabricating a carbon nanotube network and using nanoparticle fixation technology for the removal of viruses. The pore size of the nanofilter was approximately 38 nm and the measured flow rate ranged from 21.0 to 97.2L/(min·m(2)) under a pressure of 1-6 kgf/cm(2) when the amount of loaded carbon nanotube-silver composite was 1.0 mg/cm(2). The nanofilter was tested against Polio-, Noro-, and Coxsackie viruses using a sensitive real-time polymerase chain reaction assay to detect the presence of viral particles within the outflow. No trace of viruses was found to flow through the nanofilter with carbon nanotube-silver composite loaded above 0.8 mg/cm(2). Moreover, the surface of the filter has antibacterial properties to prevent bacterial clogging due to the presence of 20-nm silver nanoparticles, which were synthesized on the carbon nanotube surface.
Asunto(s)
Bacterias , Filtración/instrumentación , Nanotubos de Carbono , Plata , Virus , Microbiología del Agua , Purificación del Agua/métodosRESUMEN
Mononuclear nonheme iron(III) complexes of tetradentate ligands containing two deprotonated amide moieties, [Fe(Me(2)bpb)Cl(H(2)O)] (3 a) and [Fe(bpc)Cl(H(2)O)] (4 a), were prepared by substitution reactions involving the previously synthesized iron(III) complexes [Et(3)NH][Fe(Me(2)bpb)Cl(2)] (3) and [Et(3)NH][Fe(bpc)Cl(2)] (4). Complexes 3 a and 4 a were characterized by IR and elemental analysis, and complex 3 a also by X-ray crystallography. Nonheme iron(III) complexes 3, 3 a, 4, and 4 a catalyze olefin epoxidation and alcohol oxidation on treatment with m-chloroperbenzoic acid. Pairwise comparisons of the reactivity of these complexes revealed that the nature of the axial ligand (Cl(-) versus H(2)O) influences the yield of oxidation products, whereas an electronic change in the supporting chelate ligand has little effect. Hydrocarbon oxidation by these catalysts was proposed to involve an iron(V) oxo species which is formed on heterolytic O-O bond cleavage of an iron acylperoxo intermediate (FeOOC(O)R). Evidence for this iron(V) oxo species was derived from KIE (k(H)/k(D)) values, H(2) (18)O exchange experiments, and the use of peroxyphenylacetic acid (PPAA) as the peracid. Our results suggest that an Fe(V)=O moiety can form in a system wherein the supporting chelate ligand comprises a mixture of neutral and anionic nitrogen donors. This work is relevant to the chemistry of mononuclear nonheme iron enzymes that are proposed to oxidize organic substrates via reaction pathways involving high-valent iron oxo species.