RESUMEN
Hierarchical structures in nature provide unique functions for living organisms that can inspire technology. Nanoscale hierarchical structured surfaces are essential to realize the dual functions of non-wetting and transparency for applications such as cover glasses and windows; however, these structures are challenging to fabricate. In this study, nano-hierarchical structured glass surfaces were fabricated using multi-step colloidal lithography and etching to obtain tunable morphology. Nanostructured surfaces of mono-pillar structures of diameter 120 and 350 nm and hierarchical-pillar structures of their combinations exhibited superhydrophobicity after perfluoropolyether coating. In particular, the hierarchical nanosurfaces showed excellent non-wetting properties with the apparent, advancing, and receding water contact angles exceeding 177° and contact angle hysteresis below 1°. Water bouncing behaviors - contact time, spreading diameter, and shape of the bouncing motion were also evaluated according to the Weber number to examine the robustness of superhydrophobicity. Hierarchical nanosurfaces showed larger spreading diameters than mono-nanosurfaces with 14 bounces, indicating minimal energy loss from friction, as can be explained by the effective slip length. Furthermore, the nano-hierarchical structures exhibited better transmittance for wide angles of incidence up to 70° than mono-nanostructures owing to their reduced scattering area and multi-periodicity.
RESUMEN
Metal-oxide sensors, detect gas through the reaction of surface oxygen molecules with target gases, are promising for the detection of toxic pollutant gases, combustible gases, and organic vapors; however, their sensitivity, selectivity, and long-term stability limit practical applications. Porous structure for increasing surface area, adding catalyst, and altering the operation temperature are proposed for enhancing the sensitivity and selectivity. Although humidity can significantly affect the property and stability of the sensors, studies focusing on the long-term stability of gas sensors are scarce. To reduce the effects of humidity, 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (PFOTS) was coated on a porous SnO2 film. The interconnected SnO2 nanowires improved the high surface area, and the PFOTS coating provided superhydrophobicity at water contact angle of 159°and perfect water vapor repellency inside E-SEM. The superhydrophobic porous morphology was maintained under relative humidity of 99% and operating temperature of 300 °C. The CO gas sensing of 5, 20, and 50 ppm were obtained with linearity at various humidity. Flame detection was also achieved with practical high humidity conditions. These results suggest the simple way for reliable sensing of nanostructured metal-oxide gas sensors with high sensitivity and long-term stability even in highly humid environments.