RESUMEN
The present study is aimed at investigating the effect of hybridisation on Kevlar/E-Glass based epoxy composite laminate structures. Composites with 3 mm thickness and 16 layers of fibre (14 layers of E-glass centred and 2 outer layers of Kevlar) were fabricated using compression moulding technique. The fibre orientation of the Kevlar layers had 3 variations (0, 45 and 60°), whereas the E-glass fibre layers were maintained at 0° orientation. Tensile, flexural, impact (Charpy and Izod), interlaminar shear strength and ballistic impact tests were conducted. The ballistic test was performed using a gas gun with spherical hard body projectiles at the projectile velocity of 170 m/s. The pre- and post-impact velocities of the projectiles were measured using a high-speed camera. The energy absorbed by the composite laminates was further reported during the ballistic test, and a computerised tomographic scan was used to analyse the impact damage. The composites with 45° fibre orientation of Kevlar fibres showed better tensile strength, flexural strength, Charpy impact strength, and energy absorption. The energy absorbed by the composites with 45° fibre orientation was 58.68 J, which was 14% and 22% higher than the 0° and 60° oriented composites.
RESUMEN
Natural fibre-based composites are replacing traditional materials in a wide range of structural applications that are used in different environments. Natural fibres suffer from thermal shocks, which affects the use of these composites in cold environment. Considering these, a goal was set in the present research to investigate the impact of cryogenic conditions on natural fibre composites. Composites were developed using polyester as matrix and jute-fibre and waste Teak saw-dust as reinforcement and filler, respectively. The effects of six parameters, viz., density of saw-dust, weight ratio of saw-dust, grade of woven-jute, number of jute layers, duration of cryogenic treatment of composite and duration of alkaline treatment of fibres on the mechanical properties of the composite was evaluated with an objective to maximise hardness, tensile, impact and flexural strengths. Taguchi method was used to design the experiments and response-surface methodology was used to model, predict and plot interactive surface plots. Results indicated that the duration of cryogenic treatment had a significant effect on mechanical properties, which was better only up to 60 min. The models were found to be statistically significant. The study concluded that saw-dust of density 300 kg/m3 used as a filler with a weight ratio of 13 wt.% and a reinforcement of a single layer of woven-jute-fibre mat of grade 250 gsm subjected to alkaline treatment for 4 h in a composite that has undergone 45 min of cryogenic treatment presented an improvement of 64% in impact strength, ca. 21% in flexural strength, ca. 158% in tensile strength and ca. 28% in hardness.