Reverse cationic flotation is currently the main processing technique for upgrading fine hematite from silicates. Flotation is known as an efficient method of mineral enrichment that deals with possibly hazardous chemicals. Thus, using eco-friendly flotation reagents for such a process is an emerging need for sustainable development and green transition. As an innovative approach, this investigation explored the potential of locust bean gum (LBG) as a biodegradable depressant for the selective separation of fine hematite from quartz through reverse cationic flotation. Various flotation conditions (micro and batch flotation) were conducted, and the mechanisms of LBG adsorption have been examined by different analyses (contact angle measurement, surface adsorption, zeta potential measurements, and FT-IR analysis). The micro flotation outcome indicated that the LBG could selectively depress hematite particles with negligible effect on quartz floatability. Flotation of mixed minerals (hematite and quartz mixture in various ratios) indicated that LGB could enhance separation efficiency (hematite recovery > 88%). Outcomes of the surface wettability indicated that even in the presence of the collector (dodecylamine), LBG decreased the hematite work of adhesion and had a slight effect on quartz. The LBG adsorbed selectively by hydrogen bonding on the surface of hematite based on various surface analyses.
RESUMEN
Nowadays, due to the strategic status of nickel in the global market, utilizing its disregarded resources like low-grade nickel containing pyrrhotite is of significant importance. A comprehensive set of experiments and analyses were performed to determine the bioleaching capability and mechanism for nickel extraction from hexagonal and monoclinic pyrrhotite. Over 95% Ni extraction was achieved from the hexagonal pyrrhotite sample. Ni extraction from the monoclinic sample reached its maximum value of 67% and 90% at 3% pulp density, with mixed mesophilic and moderately thermophilic cultures, respectively. Characterization analyses indicated that jarosite and elemental sulfur formation in mixed mesophilic bioleaching reduced the samples' bio-oxidation rate and metal dissolution. The kinetics study revealed that the controlling step in thermophilic bioleaching is the chemical reaction; however, the mixed control model was best fitted on mesophilic data. Electrochemistry studies confirmed bioleaching results and indicated that monoclinic pyrrhotite's oxidation rate under the operating conditions is faster than hexagonal pyrrhotite, and the temperature positively correlates with the oxidation rate. Toxicity assessment analysis showed that the final residues of both bioleached samples could be considered environmentally safe.