RESUMEN
In this work the applicability of neopentasilane (Si(SiH(3))(4)) as a precursor for the formation of silicon nanowires by using gold nanoparticles as a catalyst has been explored. The growth proceeds via the formation of liquid gold/silicon alloy droplets, which excrete the silicon nanowires upon continued decomposition of the precursor. This mechanism determines the diameter of the Si nanowires. Different sources for the gold nanoparticles have been tested: the spontaneous dewetting of gold films, thermally annealed gold films, deposition of preformed gold nanoparticles, and the use of "liquid bright gold", a material historically used for the gilding of porcelain and glass. The latter does not only form gold nanoparticles when deposited as a thin film and thermally annealed, but can also be patterned by using UV irradiation, providing access to laterally structured layers of silicon nanowires.
RESUMEN
Binary systems of Pt-Si are prepared by electron-beam-induced deposition using the two precursors, trimethyl(methylcyclopentadienyl)platinum(IV) (MeCpPt(Me)(3)) and neopentasilane (Si(SiH(3))(4)), simultaneously. By varying the relative flux of the two precursors during deposition, we are able to study composites containing platinum and silicon in different ratios by means of energy-dispersive X-ray spectroscopy, atomic force microscopy, electrical transport measurements, and transmission electron microscopy. The results show strong evidence for the formation of a binary, metastable Pt(2)Si(3) phase, leading to a maximum in the conductivity for a Si/Pt ratio of 3:2.