The investigations of real industrial wastewater, such as palm oil mill effluent (POME), as a recalcitrant pollutant remain a subject of global water pollution concern. Thus, this work introduced the preparation and modification of g-C3N4 and WO3 at optimum calcination temperature, where they were used as potent visible light-driven photocatalysts in the degradation of POME under visible light irradiation. Herein, g-C3N4-derived melamine and WO3 photocatalyst were obtained at different calcination temperatures in order to tune their light absorption ability and optoelectronics properties. Both photocatalysts were proven to have their distinct phases, crystallinity levels, and elements with increasing temperature, as demonstrated by the ultraviolet-visible spectroscopy (UV-Vis), X-ray diffraction analysis (XRD), thermogravimetric analysis (TGA), Fourier-transform infrared spectroscopy (FTIR), Brunauer-Emmett-Teller (BET), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS) results. Significantly, g-C3N4 (580 °C) and WO3 (450 °C) unitary photocatalysts exhibited the highest removal efficiency of POME without dilution due to good crystallinity, extended light absorption, high separation, and less recombination efficiency of electron-hole pairs. Furthermore, surprisingly, the superior energy storage photocatalytic performance with outstanding stability by WO3 achieved an approximately 10% increment during darkness, compared with g-C3N4 under visible light irradiation. Moreover, it has been proven that the WO3 and g-C3N4 photocatalysts are desirable photocatalysts for various pollutant degradations, with excellent visible-light utilization and favorable energy storage application.
RESUMEN
Herein, this study extracted nanocrystalline cellulose (NC) and silica (SiO2) from raw oil palm leaves (OPL), and employed as nanofillers in polyethersulfone (PES) to produce NC-SiO2-PES as support to immobilize Candida rugosa lipase (CRL) (NC-SiO2-PES/CRL). XRD, TGA-DTG and FTIR-ATR data affirmed that NC and SiO2 were isolated from OPL with corresponding crystallinity indices of 68 % and 70 %. A 0.02 cm membrane size with 5% (w/v) of NC-SiO2 without PVP K30 was optimal for membrane fabrication. CRL immobilized on the Glut-AP-NC-SiO2-PES membrane gave a higher conversion of pentyl valerate (PeVa) (91.3 %, p < 0.05) compared to Glut-NC-SiO2-PES (73.9 %) (p < 0.05). Characterization of the NC-SiO2-PES/CRL biocatalyst verified the presence of CRL. Hence, raw OPL is a proven good source of NC and SiO2, as reinforcement nanofillers in PES. The overall findings envisage the promising use of NC-SiO2-PES/CRL to catalyze an expedient and high yield of PeVa, alongside the suitability of NC-SiO2-PES for activating other enzymes.