J Nanosci Nanotechnol
; 14(12): 9548-53, 2014 Dec.
Artículo
en Inglés
| MEDLINE
| ID: mdl-25971097
RESUMEN
Ingots of Ni-Ti-Hf shape memory alloys were prepared by vacuum arc re-melting. Isothermal hot compression tests were conducted at temperatures ranging from 700 to 1000 degrees C and at strain rates from 10(-2) s(-1) to 1.0 s(-1). A decrease in the Ni content below 50.2 at.% significantly deteriorated the hot workability due to the formation of a brittle second phase. Also, the low Ni content alloy showed poor workability when the temperature exceeded 900 degrees C. Additional compression tests were conducted under various conditions to clarify the effects of the chemical composition, solidification anisotropy, and the strain rate.