RESUMEN

Due to their high lipid content, microalgae are one of the most significant sources of green hydrocarbons, which might help lessen the world's need for fossil fuels. Many zeolite-based catalysts are quickly deactivated by coke production and have a short lifetime. In this study, a bimetallic Lanthanum-Cerium (La-Ce)-modified HZSM-5 zeolite catalyst was synthesized through an impregnation method and was tested for the conversion of hydrolyzed oil into oxygen-free hydrocarbon fuels of high energy content. Initially, hydrolyzed oil (HO), the byproduct of the transesterification process, was obtained by the reaction of crude oil derived from Chlorella vulgaris microalgae and a methanol. Various catalysts were produced, screened, and evaluated for their ability to convert algal HO into hydrocarbons and other valuable compounds in a batch reactor. The performance of HZSM-5 was systematically tested in view of La-Ce loaded on conversion, yield, and selectivity. NH3-TPD analysis showed that the total acidity of the La-Ce-modified zeolites was lower than that of the pure HZSM-5 catalyst. TGA testing revealed that including the rare earth elements La and Ce in the HZSM-5 catalyst lowered the catalyst propensity for producing coke deposits. The acid sites necessary for algal HO conversion were improved by putting La and Ce into HZSM-5 zeolite at various loading percentages. The maximum hydrocarbon yield (42.963%), the highest HHV (34.362 MJ/Kg), and the highest DOD% (62.191%) were all achieved by the (7.5%La-2.5%Ce)/HZSM-5 catalyst, which was synthesized in this work. For comparison, the hydrocarbon yield for the parent HZSM-5 was 21.838%, the HHV was (33.230 MJ/Kg), and the DOD% was 44.235%. In conclusion, La and Ce-loading on the parent HZSM-5 may be responsible for the observed alterations in textural properties; nevertheless, there is no clear correlation between the physical features and the hydrocarbon yield (%). The principal effect of La and Ce modifying the parent HZSM-5 zeolite was to modify the acidic sites needed to enhance the conversion (%) of the algal HO during the catalytic deoxygenation process, which in turn raised the hydrocarbon yield (%) and increased the HHV and DOD%.

Asunto(s)

RESUMEN

Despite the extensive research into the catalytic uses of zeolite-based catalysts, these catalysts have a limited useful lifetime because of the deactivating effect of coke production. This study looks at the use of Cerium (Ce) loaded HZSM-5 zeolite catalysts in the hydrocarbon and oxygenated chemical conversion from Chlorella Vulgaris microalgae crude oil. Characterization of structure, morphology, and crystallinity was performed after the catalysts were manufactured using the impregnation technique. Soxhlet extraction was carried out to extract the crude oil of microalgae. Transesterification reaction was used to produce algal hydrolyzed oil (HO), and the resulting HO was put to use in a batch reactor at 300 °C, 1000 rpm, 7 bars of nitrogen pressure, a catalyst to the algal HO ratio of 15% (wt. %), and a retention time of 6 h. To determine which Ce-loaded HZSM-5 catalysts would be most effective in converting algal HO into non-oxygenated molecules (hydrocarbons), we conducted a series of tests. Liquid product characteristics were analyzed for elemental composition, higher heating value (HHV), atomic ratios of O/C and H/C, and degree of deoxygenation (DOD%). Results were categorized into three groups: product yield, chemical composition, and carbon number distribution. When Cerium was added to HZSM-5 zeolite at varying loading percentages, the zeolite's acid sites became more effective in facilitating the algal HO conversion. The results showed that 10%Ce/HZSM-5 had the greatest conversion of the algal HO, the yield of hydrocarbons, HHV, and DOD% (98.2%, 30%, 34.05 MJ/Kg, and 51.44%, respectively) among all the synthesized catalysts in this research. In conclusion, the physical changes seen in the textural characteristics may be attributed to Cerium-loading on the parent HZSM-5; nevertheless, there is no direct association between the physical features and the hydrocarbons yield (%). The primary impact of Cerium alteration of the parent HZSM-5 zeolite was to change the acidic sites required to boost the conversion (%) of the algal HO in the catalytic deoxygenation process, which in turn increased the hydrocarbons yield (%), which in turn increased the HHV and DOD%.

Asunto(s)

RESUMEN

Microalgae is one of the most important sources of green hydrocarbons because it contains a high percentage of lipids and is likely to reduce reliance on fossil fuels. Several zeolite-based catalysts have a short lifetime due to coke-formation deactivation. In this study, a lanthanum-modified HZSM-5 zeolite catalyst for the conversion of crude oil into non-oxygenated compounds (hydrocarbons) and oxygenated compounds has been investigated. The crude oil of Chlorella Vulgaris microalgae was extracted using Soxhlet and converted into hydrolyzed oil (HO) through a transesterification reaction. The experiments were conducted in a batch reactor (300 °C, 1000 rpm, 7 bar of N2, the catalyst to the algal HO ratio of 15% (wt.%) and 6 h). The results were organized into three groups: product yield, chemical composition, and carbon number distribution. The liquid products were investigated, including their elemental composition, higher heating value (HHV), atomic ratios of O/C and H/C, and degree of deoxygenation (DOD%). The loading of lanthanum into HZSM-5 zeolite with different loading percentages enhanced the acid sites needed for the algal HO conversion. Among all the synthesized catalysts, 10%La/HZSM-5 produced the highest conversion of the algal HO, the highest yield of hydrocarbons, the highest HHV, and the highest DOD%; those were 100%, 36.88%, 34.16 MJ/kg, and 56.11%, respectively. The enhanced catalytic conversion was due to the presence of lanthanum, which alters the active sites for the desired reactions of catalytic deoxygenation. The main effect of the modification of the parent HZSM-5 zeolite with lanthanum led to adjusting the acidic sites needed to increase the conversion (%) of the algal HO in the catalytic deoxygenation process and thus increase the hydrocarbon yield (%), which in turn led to an increase in the HHV and DOD%. The proposed La-based zeolite composite is promising for different energy applications due to its unique benefits compared to other expensive and less-stable catalysts.

Asunto(s)

RESUMEN

Novel corona virus (COVID-19) pandemic in the last 4 months stimulates the international scientific community to search for vaccine of antiviral agents suitable for in activating the virus inside and outside the human body. More than 4 million people globally are infected by the virus and about 300,000 dead cases until this moment. The ventilation and airborne filters are also investigated aiming to develop an efficient antiviral filtration technology. Human secretion of the infected person as nasal or saliva droplets goes as airborne and distributes the virus everywhere around the person. N95 and N98 filters are the must use filters for capturing particles of sizes around 300 nm. The average size of the novel corona virus (COVID-19) is 100 nm and there is no standard or special filter suitable for this virus. The nanoparticle-coated airborne filter is a suitable technique in this regard. While the efficiency of this type of filters still needs to be enhanced, new developed nanofiber filters are proposed. Most recently, the charged nanofiber filters of sizes below 100 nm are developed and provide an efficient viral filtration and inactivation. The efficiency of filter must be kept at accepted level without increasing the pressure drop. The present review outlines the most efficient antiviral nanoparticles including the recent functional nanoparticles. The filtration theory, filtration modeling, filter testing, and different types of filter with special concentration on the charged nanofiber filter were discussed. The charged nanofiber filter able to capture novel corona virus (COVID-19) with 94% efficiency and a pressure drop less than 20 MPa.