We report on femtosecond laser writing of channel waveguides in Nd(3+) ion doped YAG ceramics by multiple inscriptions of damage filaments. Waveguiding between filaments was found to resist annealing temperatures as high as 1500 degrees C. Microluminescence imaging experiments have been carried out to elucidate the potential application of the obtained waveguides as integrated laser sources as well as to elucidate the waveguiding mechanisms.
RESUMEN
A study of Ba(2)NaNb(5)O(15) and LiNbO(3) crystals with periodic ferroelectric domain structures using the scanning near field optical microscopy technique is reported. Optical contrast is observed in the regions of ferroelectric domain boundaries and it is analysed using beam propagation method modelling. This reveals that the optical contrast, a consequence of changes in the refractive index, is not due to variation of the waveguide-coupling efficiency, and supports the hypothesis that it is associated with the domain array, which is related to the size of the domain.
RESUMEN
The LiNbO(3) congruent crystals doped with small Nd concentrations, <1 mol% Nd, and co-doped with Mg ions, 0-9 mol% Mg, were systematically investigated by means of micro-Raman spectroscopy in the Y and Z crystal directions. Results obtained from an undoped congruent crystal, an Nd-doped crystal, a Mg-doped crystal and Nd, Mg-co-doped crystals are compared. From the analyses of the results obtained in the Y direction, the Nd and Mg content dependence of the two lowest-Raman A(1)(TO(1)) and A(1)(TO(2)) modes, the half-width composition and the area ratio of the A(1)(TO(4)) and E(TO(8)) bands, we reached several conclusions about the incorporation mechanism of the Nd and Mg ions into the LiNbO(3) lattice. Likewise the Raman shift and half-width of the E(TO(1)) and E(TO(7)) modes were investigated in the Z direction. Results indicate that Mg and Nd ions are located in the Li site for low doping concentrations and for larger concentrations there is a replacement in both Li and Nb ion sites.
RESUMEN
We report on the in-depth micro-modifications induced by femtosecond laser ablation in Nd:YAG crystals. Near Field Optical experiments have revealed that, below the ablated volume, a permanent change in the Nd:YAG reflectivity, extending parallel to the irradiation direction, has been induced. Micro-luminescence experiments have provided experimental evidence that these permanent changes in the surface reflectivity are accompanied by strong changes in the luminescence properties of Nd(3+) ions revealing relevant micro structural modifications in the Nd:YAG system.