The manufacture of natural pozzolans as cement products is economically affordable and contributes to CO2 mitigation in the cement-based materials industry. Through two experimental stages, this study evaluates the feasibility of using volcanic ash (VA) to partially substitute portland cement (PC) in mortar production. In Stage 1, the effectiveness of different activation methods, such as calcination, alkali activation, and lime addition, in enhancing VA reactivity was assessed when the mortars were produced using 35% VA. The compressive strength (fcm) and physical properties of the mortars produced were determined at 7 and 28 days and compared with those of mortars without activated VA. In Stage 2, the most effective treatments obtained from Stage 1 were applied to produce mortars with 50% and 75% of VA replacements, focusing on their physical and mechanical properties. The findings revealed promising results, particularly when mortars were produced with up to 50% calcined VA (CVA) at 700 °C and 20 wt% lime addition, reaching a higher fcm than 45 MPa. Chemical activation with 2% CaCl or 1% NSi enhanced early-age strength in 35% VA-based mortars. Additionally, NSi-activated CVA-lime-based mortar at 50% VA achieved a notable fcm of 40 MPa at 28 days. Even mortars with 75% VA replacement achieved an adequate compressive strength of 33MPa at 28 days. This study determined that VA-based mortars have the potential for construction applications.
RESUMEN
The construction industry is affected by the constant growth in the populations of urban areas. The demand for cement production has an increasing environmental impact, and there are urgent demands for alternative sustainable solutions. Volcanic ash (VA) is an abundant low-cost material that, because of its chemical composition and amorphous atomic structure, has been considered as a suitable material to replace Portland cement clinker for use as a binder in cement production. In the last decade, there has been interest in using alkali-activated VA material as an alternative material to replace ordinary Portland cement. In this way, a valuable product may be derived from a currently under-utilized material. Additionally, alkali-activated VA-based materials may be suitable for building applications because of their good densification behaviour, mechanical properties and low porosity. This article describes the most relevant findings from researchers around the world on the role of the chemical composition and mineral contents of VA on reactivity during the alkali-activation reaction; the effect of synthesis factors, which include the concentration of the alkaline activator, the solution-to-binder ratio and the curing conditions, on the properties of alkali-activated VA-based materials; and the mechanical performance and durability properties of these materials.