RESUMEN
We report the functional assessment of tungsten (VI) oxide on gamma-ray attenuation properties of 60Sb2O3-(40-x)NaPO3-xWO3 antimony glasses. The elemental mass-fractions and glass-densities of each glass sample are specified separately for the MCNPX Monte Carlo code. In addition to fundamental gamma absorption properties, Transmission Factors throughout a broad radioisotope energy range were measured. According to findings, holmium (Ho) incorporation into the glass structure resulted in a net increase of 0.3406 g/cm3, whereas cerium (Ce) addition resulted in a net increase of 0.2047 g/cm3. The 40% WO3 reinforced S7 sample was found to have the greatest LAC value, even though seven glass samples exhibited identical behavior. The S2 sample had the lowest HVL values among the glass groups evaluated in this work, computed in the energy range of 0.015-15 MeV. The lowest EBF and EABF values were reported for 40% WO3 reinforced S7 sample with the highest LAC and density values. According to the findings of this research, WO3 will likely make a significant contribution to the gamma ray absorption properties of antimony glasses, which are employed for optical and structural modification. Therefore, it can be concluded that WO3 may be treated monotonically and can be employed successfully in circumstances where gamma-ray absorption characteristics, optical properties, and structural qualities need to be enhanced.
RESUMEN
We report the critical optical properties such as Average Visible Transmittance (AVT), colour, Color Rendering Index (CRI), and Correlated Color Temperature (CCT) of a multicomponent glass system with a nominal composition of 50TeO2-30B2O3-(20-x)Li2O-xCeO2 (x = 0,0.5,1,2,3,4,5,10,15,20 mol%). Various advanced theoretical approaches as well as calculations are utilized in terms of determining the optical properties of studied glasses. The maximum transmittance and AVT values of the glass system exceeded 80% and 79.59%, respectively. The colour coordinates are found extremely near to D65 and the achromatic point without CeO2 contribution. According to our results, the current system has a promising ability to be utilized for coloured window applications in terms of both AVT and colour with 2% CeO2 doping. Our results showed that, the CeO2 additive is able to move the glass colour straight into the red spectrum by shifting the transmittance spectrum to the long-wavelength portion of the visible spectrum. With 10% CeO2 doping, opacity in the visible area and permeability in the NIR region are obtained, and the CCT value changes from 5002 K to 2560 K. It can be concluded that a filter system with modifiable NIR or red optical characteristics may be produced through the CeO2 alterations in borotellurite glass systems.
RESUMEN
Background: During mammography, a lead-acrylic protective screen is recommended to reduce radiation exposure to the unexposed breast. Objectives: This research study aimed to construct an Indium-(III)-oxide-rich tellurite-glass screen (TZI8) and compare its performance to that of lead acrylic. Materials and Methods: A three-layer heterogeneous-breast phantom was developed, using the MCNPX (version 2.7.0) Monte Carlo code. An MCNPX-simulation geometry was designed and implemented, using the lead-acrylic and TZI8 shielding screens between the right and left breast. Next, the reliability of the phantom and the variations in absorption between the lead-acrylic and TZI8 glass were investigated. Results: The findings show that the TZI8-protective-glass screen offers significantly greater radioprotection than the lead-acrylic material. The quantity of total dose absorbed in the unexposed breast was much lower for TZI8 than for lead-based acrylic. The TZI8-glass screen gives about 60% more radioprotection than the lead-acrylic screen. Conclusion: Considering the toxic lead in the structure that may be hazardous to the human tissues, the TZI8-glass screen may be used in mammography examination to provide greater radioprotection than the lead-acrylic screen, in order to greatly reduce the dose to the unexposed breast.