RESUMEN
Nanoporous materials have attracted great technological interest during the past two decades, essentially due to their wide range of applications: they are used as catalysts, molecular sieves, separators and gas sensors as well as for electronic and electrochemical devices. Most syntheses of nanoporous materials reported so far have focused on template-assisted bottom-up processes, including soft templating (chelating agents, surfactants, block copolymers and so on) and hard templating (porous alumina, carbon nanotubes and nanoporous materials) methods. Here, we exploit a mechanism implicitly occurring in lithium batteries at deep discharge to develop it into a room-temperature template-free method of wide applicability in the synthesis of not only transition metals but also metal oxides with large surface area and pronounced nanoporosity associated with unprecedented properties. The power of this top-down method is demonstrated by the synthesis of nanoporous Pt and RuO2, both exhibiting superior performance: the Pt prepared shows outstanding properties when used as an electrocatalyst for methanol oxidation, and the RuO2, when used as a supercapacitor electrode material, exhibits a distinctly better performance than that previously reported for non-hydrated RuO2 (refs 19,20).
RESUMEN
Spherical voids as light scattering centers in nanocrystalline TiO2 films were realized with polystyrene particles of diameter 400 nm, thus enhancing the photovoltaic performance by 25% on large areas, as well as providing an indication that these films can be used with electrolytes of higher viscosity.
RESUMEN
The role of the conducting glass substrate (fluorine-doped tin oxide, FTO) in the back reaction of electrons with tri-iodide ions in dye-sensitized nanocrystalline solar cells (DSCs) has been investigated using thin-layer electrochemical cells that are analogues of the DSCs. The rate of back reaction is dependent on the type of FTO and the thermal treatment. The results show that this back-reaction route cannot be neglected in DSCs, particularly at lower light intensities, where it is the dominant route for the back transfer of electrons to tri-iodide. This conclusion is confirmed by measurements of the intensity dependence of the photovoltages of DSCs with and without blocking layers. It follows that blocking layers should be used to prevent the back reaction in mechanistic studies in which the light intensity is varied over a wide range. Conclusions based on studies of the intensity dependence of the parameters of DSCs such as photovoltage and electron lifetime in cells without blocking layers, must be critically re-examined.
RESUMEN
Novel ternary assemblies consisting of fully encapsulated host-guest complexes (hemicarceplexes) and wide band gap semiconductor nanoparticles were investigated. The water-soluble amphiphilic host (octacarboxyhemicarcerand) traps the hydrophobic chromophore within its cavity and binds to the surface of metal oxide nanoparticles. Fluorescence quenching and fast charge injection, kforward >/= 7 x 109 s-1, from the S2 state of encapsulated azulene were observed. Charge recombination proceeds at a much lower rate of 2 x 107 s-1. Interestingly, the recombination kinetics is homogeneous, suggesting that electron tunneling through the wall of the "molecular container" is the rate-limiting step of the process.