RESUMEN
We report a rapid additive-free synthesis of nanocrystals (NCs) of RHO-type ZIF-71 () of composition [Zn(dcim)2] (dcim = 4,5-dichloroimidazolate) in 1-propanol as solvent at room temperature. NC- has a size of 30-60 nm and exhibits permanent microporosity with a surface area (SBET = 970 m(2) g(-1)) comparable to that of microcrystalline material. When kept under the mother solution NC- undergoes transformation into a novel SOD-type polymorph (), which in turn converts into known ZIF-72 () with lcs topology. It is shown that microcrystals (MCs) of can be favourably synthesised using 1-methylimidazole as a coordination modulator. NC- with size <200 nm was prepared using NC-ZIF-8 as a template with SOD topology in a solvent assisted ligand exchange-related process. DFT-assisted Rietveld analysis of powder XRD data revealed that novel polymorph possesses an unusual SOD framework conformation. was further characterised with regard to microporosity (SBET = 597 m(2) g(-1)) and thermal as well as chemical stability. DFT calculations were performed to search for further potentially existing but not-yet synthesised polymorphs in the [Zn(dcim)2] system.
RESUMEN
Recently, nanodiamonds (NDs) have attracted great interest due to their unique physical and chemical properties that could be used in various biological applications. However, depending on the origin, NDs often contain different impurities which may affect cellular functions and viability. Therefore, before their biomedical application, the cytotoxicity of newly produced NDs should be assessed. In the present study, we have evaluated cytotoxicity of four types of ND particles with two cell models: a human osteosarcoma cell line, MG-63, and primary rat mesenchymal stem cells (rMSCs). Detonation-generated nanodiamond (DND) particles were purified with different acid oxidizers and impurities' content was determined by elemental analysis. The particles size distribution was measured revealing that the DND particles have an average size in the range of 51-233 nm. Cytotoxicity was assessed by optical microscopy and proliferation assay after 72 hours exposure of the cells to nanoparticles. We observed cell-specific and material-specific toxicity for all tested particles. Primary stem cells demonstrated higher sensitivity to DND particles than osteosarcoma cells. The most toxic were the DND particles with the smallest grain size and slight content of non-diamond carbon, while DNDs with higher grain size and free from impurities had no significant influence on cell proliferation and morphology. In addition, the smaller DND particles were found to form large aggregates mainly during incubation with rMSCs. These results demonstrate the role of the purification method on the properties of DND particles and their cytotoxicity as well as the importance of cell types used for evaluation of the nanomaterials.
RESUMEN
The kinetics and mechanism of crystallization of the dense zinc imidazolate framework with zni topology, from comparatively dilute methanol solutions containing Zn(NO(3))·6H(2)O and imidazole with variation of the zinc-to-imidazole ratio, were followed in situ by time-resolved static and dynamic light scattering. The light scattering data revealed that metastable primary particles of about 100 nm in diameter form rapidly upon mixing the component solutions. After a lag time that is dependent on the imidazole concentration, the primary particles aggregate into secondary particles by a monomer addition mechanism with the primary particles as the monomers. Complementary scanning electron microscopy revealed that further evolution of the secondary particles is a complex process involving polycrystalline intermediates, the non-spherical morphologies of which depend on the initial zinc-to-imidazole ratio. Time and location of the first appearance of crystalline order could so far not be established. The pure-phase ZIF-zni crystals obtained after 240 min are twins. The aspect ratio of the tetragonal crystals can be controlled via the zinc-to-imidazole ratio.
RESUMEN
Nanoscale copper was selectively photodeposited onto the surface of hexadecylamine (HDA) stabilized (monodispersed not agglomerated) ZnO nanoparticles (NPs) of a diameter of 2-5 nm, which leads to HDA-stabilized Cu/ZnO NPs of varied Cu loading. The particles are soluble in non-polar organic solvents. The line broadening and the red shift of the surface plasmon band of Cu/ZnO NPs relative to HDA-stabilized Cu NPs, the profound decrease of the Cu/ZnO NPs visible photoluminescence at 525 nm, the increase of the UV emission intensity at 365 nm and the enhancement of the Raman scattering (RS) intensity in comparison to the parent ZnO NPs confirmed the interfacial contact between the Cu and ZnO phase.
RESUMEN
Free-standing, ZnO surface decorated Cu nanoparticles of 1-3 nm size were obtained by sequential co-pyrolysis of [Cu(OCHMeCH2NMe2)2] and ZnEt2 in squalane in the absence of additional surfactants and proved to be highly active quasi homogeneous catalysts for methanol synthesis from CO and H2.
Asunto(s)
Cobre/química , Metanol/síntesis química , Nanopartículas/química , Compuestos Organometálicos/química , Óxido de Zinc/química , Monóxido de Carbono/química , Catálisis , Coloides , Hidrógeno/química , Metanol/química , Tamaño de la PartículaRESUMEN
A novel, non-aqueous, organometallic route to nanocomposite Cu@TiO2 materials is presented. TiO2 nanorods stabilized with oleic acid (OLA) were used as support for the photo-assisted deposition of Cu using the organometallic Cu(II) precursor [Cu(OCH(CH3)CH2N(CH3)2)2] (1). The copper precursor penetrates through the shell of OLA and is photo reduced to deposit Cu0 directly at the surface of the TiO2 rods. The obtained Cu decorated nanorods were still soluble in nonpolar organic solvents without change of the morphology of nanorods. The Cu@TiO2 colloid was characterized by means of UV-VIS, XRD, AAS, and HRTEM. FTIR CO adsorption studies provide evidence for Cu0 anchored at the titania surface by a characteristic absorption at 2084 cm-1. Comparative studies of Cu-deposition were performed using CuCl2 as simple Cu source which proved that the concept of organometallic disguise of the metal centre results in a higher reaction rate and the circumvention of non-selective reduction, parasitic side reactions and undesired agglomeration of the OLA stabilized titania nanorods.