RESUMEN
Aromatic polyamides are well-known as high-performance materials due to their outstanding properties making them useful in a wide range of applications. However, their limited solubility in common organic solvents restricts their processability and becomes a hurdle in their applicability. This study is focused on the synthesis of processable ferrocene-based terpolyamides and their polydimethylsiloxane (PDMS)-containing block copolymers, using low-temperature solution polycondensation methodology. All the synthesized materials were structurally characterized using FTIR and 1H NMR spectroscopic techniques. The ferrocene-based terpolymers and block copolymers were soluble in common organic solvents, while the organic analogs were found only soluble in sulfuric acid. WXRD analysis showed the amorphous nature of the materials, while the SEM analysis exposed the modified surface of the ferrocene-based block copolymers. The structure-property relationship of the materials was further elucidated by their water absorption and thermal behavior. These materials showed low to no water absorption along with their high limiting oxygen index (LOI) values depicting their good flame-retardant behavior. DFT studies also supported the role of various monomers in the polycondensation reaction where the electron pair donation from HOMO of diamine monomer to the LUMO of acyl chloride was predicted, along with the calculation of various other parameters of the representative terpolymers and block copolymers.
RESUMEN
In this study methylene blue (MB) has been investigated for its adsorption and subsequent catalytic thermo-oxidative decomposition on surface of maghemite (γ-Fe2O3) nanoparticles. The experimental adsorption isotherm fit well to the Freundlich model, indicating multi-sites adsorption. Computational modeling of the interaction between the MB molecule and γ-Fe2O3 nanoparticle surface was carried out to get more insights into its adsorption behavior. Adsorption energies of MB molecules on the surface indicated that there are different adsorption sites on the surface of γ-Fe2O3 confirming the findings regarding the adsorption isotherm. The catalytic activity of the γ-Fe2O3 nanoparticles toward MB thermo-oxidative decomposition has been confirmed by subjecting the adsorbed MB to a thermo oxidation process up to 600 °C in a thermogravimetric analyzer. The experimental results showed a catalytic activity for post adsorption oxidation. The oxidation kinetics were studied using the Ozawa-Flyn-Wall (OFW) corrected method. The most probable mechanism functions were fifth and third orders for virgin MB and MB adsorbed onto γ-Fe2O3 nanoparticles, respectively. Moreover, the results of thermodynamic transition state parameters, namely changes in Gibbs free energy of activation (ΔG()), enthalpy of activation (ΔH()), and entropy of activation (ΔS()), emphasized the catalytic activity of γ-Fe2O3 nanoparticles toward MB oxidation.
RESUMEN
This study reports the effect of transition metal (TM) substitution on the electrical and optical properties of BaCe0.9Sm0.1O3-δ (BCS). Concentrations of 5-10 mol % of each of Fe and Co have been doped for the B-site of BCS by citric acid autocombustion method. Powder X-ray diffraction has revealed the formation of an orthorhombic perovskite-type structure. FTIR confirmed a distortion in the lattice upon TM-doping in BCS. Scanning electron microscopy (SEM) images of 1400 °C sintered samples have manifested a higher densification in BaCe0.8Sm0.1Co0.1O3-δ (BCSC10) with a grain size â¼11 µm compared to the parent compound BCS (â¼2 µm). Thermogravimetric (TG) analysis showed a water uptake in case of BaCe0.85Sm0.1Co0.05O3-δ (BCSC5), while BaCe0.85Sm0.1Fe0.05O3-δ (BCSF5) did not show a noteworthy uptake of water. TG has also proved that the incorporation of Fe and Co in BCS did not improve the chemical stability in CO2 at elevated temperature. The band gap estimated using Kubelka-Munk model based on the diffuse reflectance data was found to be the lowest for BCSC5 (2.47 eV). However, it increases upon lowering oxygen partial pressure (pO2), which was interpreted by a band structure modifications. Among the samples investigated, BCSC10 sintered at 1400 °C showed the highest electrical conductivity of 0.02 S cm(-1) in air at 600 °C, while its proton mobility appears to be negligible under the investigated humidity atmosphere.
RESUMEN
This study investigates the effect of surface acidity and basicity of aluminas on asphaltene adsorption followed by air oxidation. Equilibrium batch adsorption experiments were conducted at 25°C with solutions of asphaltenes in toluene at concentrations ranging from 100 to 3000 g/L using three conventional alumina adsorbents with different surface acidity. Data were found to better fit to the Freundlich isotherm model showing a multilayer adsorption. Results showed that asphaltene adsorption is strongly affected by the surface acidity, and the adsorption capacities of asphaltenes onto the three aluminas followed the order acidic>basic and neutral. Asphaltenes adsorbed over aluminas were subjected to oxidation in air up to 600°C in a thermogravimetric analyzer to study the catalytic effect of aluminas with different surface acidity. A correlation was found between Freundlich affinity constant (1/n) and the catalytic activity. Basic alumina that has the lowest 1/n value, depicting strongest interactions, has the highest catalytic activity, followed by neutral and acidic aluminas, respectively.